Sol-gel synthesis and characterization of ZnAl2O4 powders for transparent ceramics

Add time:08/13/2019    Source:sciencedirect.com

The sol-gel synthesis of ZnAl2O4 ceramic powders from alkoxide and acetate sources of metals, as well as the microstucture and the hardness of the hot-pressed ZnAl2O4 specimens were considered. ZnAl2O4 powders were prepared by the hydrolysis of an alcohol solution of aluminium isopropoxide using an aqueous solution of zinc acetate followed by heat treatment. The thermal evolution of the ZnAl2O4 precursor was investigated. The effect of calcination temperature on the morphology and the specific surface area of ZnAl2O4 powders were also studied. The sintering of the resultant powders to the high transparent ceramic using a hot pressing with 1 wt% ZnF2, as a sintering additive was successfully demonstrated. The in-line transmittance of ZnAl2O4 ceramics (1 mm thickness) achieved 80% in the visible region and 85% at 5 µm; Vickers hardness was 11.6 GPa.

We also recommend Trading Suppliers and Manufacturers of basic aluminum carbonate gel (cas 12538-82-8). Pls Click Website Link as below: cas 12538-82-8 suppliers

Prev:One-pot synthesis of Al2O3-La2O2CO3 systems obtained from the metallic precursor by the sol-gel method
Next:Terpyridine-Pr-Fe3O4@boehmite nanoparticles; a novel and highly effective magnetic nanocatalyst for preparation of cyclic carbonates from carbon dioxide and epoxides under solventless conditions)