Effects of the mechanical activation of Zinc carbonate hydroxide (cas 12539-71-8) on the formation and properties of zinc oxides

Add time:08/15/2019    Source:sciencedirect.com

The nanocrystalline ZnO powders were obtained by mechanochemical treatment of Zinc carbonate hydroxide (cas 12539-71-8). The mechanical activation was carried out in a planetary ball mill (Fritsch–Premium line–Pulversette No 7) by varying of the milling speed. The phase and structural transformation was investigated by X-ray diffraction (XRD) and infrared spectroscopy (IR). The morphology of the obtained ZnO powders was characterized by scanning electron microscopy (SEM). The crystallite size of the samples calculated from XRD and the SEM observation were in the range from 8 to 50 nm. The optical properties were investigated by UV–vis spectroscopy. The photocatalytic activity was studied with respect to the photodegradation of Malachite green (MG) under UV-light irradiation. The milling speed of 500 rpm led to full amorphization of the initial zinc carbonate hydroxide. After heat-treatment at 400 °C of X-ray amorphous sample single ZnO powder (20 nm) was obtained. The direct synthesis of ZnO nanoparticles (8 nm) was achieved at milling speed of 1000 rpm for short time (90 min). The mechanochemically synthesized ZnO powders possess good optical and photocatalytic properties. The additional heat-treatment improved the photocatalytic activity and the transparency of ZnO powders in the visible spectral range.

We also recommend Trading Suppliers and Manufacturers of Zinc carbonate hydroxide (cas 12539-71-8). Pls Click Website Link as below: cas 12539-71-8 suppliers

Prev:Thermal decomposition of Zinc carbonate hydroxide (cas 12539-71-8)
Next:Enhanced photocatalytic dye degradation activity of carbonate intercalated layered Zn, ZnNi and ZnCu hydroxides)