Proton conductivity of mesoporous zirconium phosphate pyrophosphate

Add time:08/16/2019    Source:sciencedirect.com

The conductivity of a mesoporous zirconium phosphate pyrophosphate of composition Zr(P2O7)0.81(O3POH)0.38 and surface area of 215 m2/g has been determined as a function of temperature at controlled relative humidity. Ac and dc conductivity measurements carried out on pellets with platinum electrodes, in nitrogen or hydrogen flow, showed that the charge carriers are protons. At 20°C and relative humidity decreasing in the range 90–20%, the conductivity changes from 1.3×10−3 S cm−1 to 4×10−7 S cm−1. The activation energy for conduction in the range 20/−20°C increases from 4.6 to 8.7 kcal/mol with decreasing relative humidity. At 100°C and 90% relative humidity the pyrophosphate groups undergo a slow rehydration and the conductivity rises up to 2.6×10−3 S cm−1 as a consequence of the increase of the number of -POH groups.

We also recommend Trading Suppliers and Manufacturers of ZIRCONIUM PYROPHOSPHATE (cas 13565-97-4). Pls Click Website Link as below: cas 13565-97-4 suppliers

Prev:Heterovalent Zr4+-Cu2+ substitution in ZIRCONIUM PYROPHOSPHATE (cas 13565-97-4): From theoretical models to synthesis and utilization
Next:From layered zirconium phosphates and phosphonates to nanofillers for ionomeric membranes)