The mechanochemical and solution combustion syntheses of cerium-doped lutetium oxyorthosilicate powder

Add time:07/21/2019    Source:sciencedirect.com

Lu2SiO5:Ce powders have been synthesized by mechanochemical processing of the constituent oxides and by urea/hexamine-nitrate-based solution-combustion methods with microwave and furnace sintering of each material. Powder x-ray diffraction (PXRD), photoluminescence excitation (PLE) and emission (PL) spectroscopy, time-correlated single photon counting (TCSPC), particle size analysis (PSA), and scanning electron microscopy (SEM) have been used to characterize the resulting powders. Mechanochemical synthesis results in the formation of agglomerated powders with the C 1 2/c 1 symmetry while solution combustion leads to the formation of porous powders with a mixture of the C 1 2/c 1 and P 1 21/c 1 symmetries. This mixture transitions to the C 1 2/c 1 phase with sintering. Both syntheses result in particle sizes of less than 50 μm before sintering. Each material shows the typical luminescence from the 5d-4f transition in addition to decay times that match standard Ce3+ values.

We also recommend Trading Suppliers and Manufacturers of lutetium hydrate (2:1) (cas 12339-78-5). Pls Click Website Link as below: cas 12339-78-5 suppliers

Prev:Discovery of gallium, germanium, lutetium, and hafnium isotopes
Next:Apparent molar volumes and compressibilities of lanthanum, gadolinium and lutetium trifluoromethanesulfonates in dimethylsulfoxide)