The use of poly(3-hydroxybutyrate), C-PHYCOCYANIN (cas 11016-15-2), and phenolic compounds extracted from Spirulina sp. LEB 18 in latex paint formulations
-
Add time:08/21/2019 Source:sciencedirect.com
Commercial paints are produced using components that can be harmful to the environment. In light of this, our study aimed to reduce these drawbacks by investigating water-based paints in which the latex resin (polyvinyl acetate [PVA]) was replaced with poly(3-hydroxybutyrate) (PHB) extracted from Spirulina sp. LEB 18. In addition, C-phycocyanin and phenolic compounds, both also extracted from this microalga, were added to the paints for coloration and antimicrobial properties, respectively. Characterization analyses indicate that paint with 9.2% PHB and 6.1% limonene performs better in the following aspects: density (1.47 g cm−3), solids (41.5%) and pigment contents (38.4%), hiding power (94.2%), abrasion resistance (123 cycles), adhesion (5–15% area removed), drying time (90 min), reflectance (90%), and emissivity (0.80). Moreover, the biocolorant C-phycocyanin, besides conferring color, also provides better coverage by the paints. At a concentration of 0.8%, the phenolic compounds are the most effective among the biocides tested. Overall, we found that it is possible to develop a product similar to commercial ones using natural substances extracted from microalgae, which have not yet been used in formulations of paint. Thus, this study contributes to a sustainable alternative for paint formulation.
We also recommend Trading Suppliers and Manufacturers of C-PHYCOCYANIN (cas 11016-15-2). Pls Click Website Link as below: cas 11016-15-2 suppliers
Prev:C-PHYCOCYANIN (cas 11016-15-2) extraction assisted by pulsed electric field from Artrosphira platensis
Next:Different characteristics of C-PHYCOCYANIN (cas 11016-15-2) (C-PC) in two strains of the extremophilic Galdieria phlegrea) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Preparation and characterization of C-PHYCOCYANIN (cas 11016-15-2) peptide grafted N-succinyl chitosan by enzyme method08/23/2019
- Different characteristics of C-PHYCOCYANIN (cas 11016-15-2) (C-PC) in two strains of the extremophilic Galdieria phlegrea08/22/2019
- C-PHYCOCYANIN (cas 11016-15-2) extraction assisted by pulsed electric field from Artrosphira platensis08/20/2019
- Evaluation of the co-production of total carotenoids, C-PHYCOCYANIN (cas 11016-15-2) and polyhydroxyalkanoates by Arthrospira platensis08/19/2019
- Thermosynechococcaceae as a source of thermostable C-PHYCOCYANIN (cas 11016-15-2)s: properties and molecular insights08/18/2019
- Enhancement of C-PHYCOCYANIN (cas 11016-15-2) purity using negative chromatography with chitosan-modified nanofiber membrane08/17/2019
- Continuous aqueous two-phase extraction of microalgal C-PHYCOCYANIN (cas 11016-15-2) using a coiled flow inverter08/16/2019
- Original articlePhysical extraction and extrusion entrapment of C-PHYCOCYANIN (cas 11016-15-2) from Arthrospira platensis☆08/15/2019
- Liquid biphasic flotation for the purification of C-PHYCOCYANIN (cas 11016-15-2) from Spirulina platensis microalga08/14/2019