The peculiarities in oxidation behavior of the ZrB2-SiC ceramics with chromium additive
-
Add time:08/15/2019 Source:sciencedirect.com
ZrB2-SiC-Cr powder sintering at 1600 °C and its oxidation behavior at 1000–1500 °C in air were studied as a function of chromium content. It was shown that the relative density of the ZrB2-SiC ceramics increases with an increase in chromium content in the powdered mixture. This is related to the formation of the liquid Cr-Si-C-B phase during the high-temperature interaction of SiC with chromium and ZrB2.It was stated that the mechanism of ZrB2-SiC-Cr ceramics oxidation is changed from bulk to passive. The oxidation resistance is improved for the ceramics with 13% of chromium or less, which can be explained by a decrease in its porosity. The ceramics with higher chromium content demonstrates the opposite effect, namely, large-size Cr2O3 crystals are formed during oxidation, this promotes microcracking in the oxidizing layer and causes damage of surface integrity. As a result, the oxidation resistance of the ZrB2-SiC-Cr ceramics with high chromium content is decreased.
We also recommend Trading Suppliers and Manufacturers of Chromium oxide (cas 1308-38-9). Pls Click Website Link as below: cas 1308-38-9 suppliers
Prev:Research articleAn efficient utilization of chromium–containing vanadium tailings: Extraction of chromium by soda roasting–water leaching and preparation of Chromium oxide (cas 1308-38-9)
Next:Full Length ArticleEffective redox reactions by Chromium oxide (cas 1308-38-9) anions: Sulfur dioxide oxidation in the gas phase) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Full Length ArticleEffective redox reactions by Chromium oxide (cas 1308-38-9) anions: Sulfur dioxide oxidation in the gas phase08/16/2019
- Research articleAn efficient utilization of chromium–containing vanadium tailings: Extraction of chromium by soda roasting–water leaching and preparation of Chromium oxide (cas 1308-38-9)08/14/2019
-
Health and Chemical more >