Strength and hydration products of cemented paste backfill from sulphide-rich tailings using reactive MgO-activated slag as a binder

Add time:08/16/2019    Source:sciencedirect.com

This paper investigated the potential of using reactive MgO-activated ground granulated blastfurnace slag (MgO-GGBS) as a binder in cemented paste backfill (CPB) from sulphide-rich tailings. The effects of reactive MgO content of MgO-GGBS on the unconfined compressive strength (UCS) of CPB were investigated. The test results showed that the CPB achieved target strength (≧1.0 MPa) at 28 d and the UCS at 360 d showed an increasing trend when MgO-GGBS dosage was 14 wt% and reactive MgO content of MgO-GGBS was 2.5–7.5 wt%. Thermodynamic calculations and analyses of potential reactions including acid and sulphate attack have been performed. The hydration products were identified by X-ray diffraction (XRD) and thermogravimetry analysis (TG/DTG). Finally, the hydration mechanism of CPB was discussed based on the thermodynamic and experimental results. The conclusion is that MgO-GGBS will be a promising binder for tailings with sulphide.

We also recommend Trading Suppliers and Manufacturers of SODIUM SULPHIDE HYDRATE (cas 1313-84-4). Pls Click Website Link as below: cas 1313-84-4 suppliers

Prev:Investigation of chemical associations and leaching behavior of heavy metals in sodium sulfide hydrate stabilized stainless steel pickling sludge
Next:Multiphase flash calculations for gas hydrates systems)