Structural, optical and electrical impacts of marcasite (cas 1317-66-4) in pyrite thin films
-
Add time:08/15/2019 Source:sciencedirect.com
The structural and electro-optical influence of marcasite (cas 1317-66-4) on the properties of solution-processed iron pyrite thin films was investigated. Marcasite has a strong tendency to form simultaneously with pyrite upon sulfurization of amorphous iron-oxide precursor films, leading to a mixed-phase structure in which pyrite grains are surrounded by nanocrystalline marcasite boundaries. The optical analysis in combination with spectroscopic ellipsometry revealed that marcasite should have a bandgap of approximately 0.85–0.88 eV with a higher absorption coefficient than pyrite, differing strongly from the prior belief that marcasite has a bandgap of less than 0.4 eV. In addition, the pyrite/marcasite film has been found to have a larger diffusion coefficient for photogenerated minority carriers than the phase-pure pyrite film from electrochemical impedance analyses, resulting in a higher photocurrent density, as determined through photoelectrochemical measurement. The facile transport of a minority carrier along the marcasite boundaries is the putative origin of the observed improvement in the photoactivity of the pyrite/marcasite mixture films.
We also recommend Trading Suppliers and Manufacturers of marcasite (cas 1317-66-4). Pls Click Website Link as below: cas 1317-66-4 suppliers
Prev:Effects of mechanical activation on lithium extraction from a lepidolite (cas 1317-64-2) ore concentrate
Next:DFT+U study on the electronic structures and optical properties of pyrite and marcasite (cas 1317-66-4)) - 【Back】【Close 】【Print】【Add to favorite 】