A novel process for synthesis of TOBERMORITE (cas 1319-31-9) fiber from high-alumina fly ash

Add time:08/24/2019    Source:sciencedirect.com

A new two-step process was developed for the synthesis of TOBERMORITE (cas 1319-31-9) fiber from high alumina fly ash. The results reveal that high alumina extraction efficiency from the fly ash can be achieved in the first step and tobermorite fiber with excellent properties can be produced from the dealumination slag in the second step. FETEM images show that typical single crystal fibers with a length of 5–10 μm and a length-to-diameter ratio of 50–100 have been synthesized successfully. The strength tests after compression molding demonstrate that the compressive and flexural strengths of the products are greater than 0.34 MPa and 0.85 MPa, respectively, with a low bulk density of 218 kg/m3 and a thermal conductivity of 0.059 W/(m·k). It fully complies with China's national standards for calcium silicate insulation materials. Therefore, the fibers production is very promising to be used in the building external wall thermal insulation application.

We also recommend Trading Suppliers and Manufacturers of TOBERMORITE (cas 1319-31-9). Pls Click Website Link as below: cas 1319-31-9 suppliers

Prev:Humic acid-induced formation of TOBERMORITE (cas 1319-31-9) upon hydrothermal treatment with municipal solid waste incineration bottom ash and its application for efficient removal of Cu(II) ions
Next:Direct impregnation and characterization of Colemanite/Ulexite (cas 1319-33-1)-Mg(OH)2 paraffin based form-stable phase change composites)