Combined impact of SILICATE (cas 12627-13-3)-amorphicity and MgO-reactivity on the performance of Mg-SILICATE (cas 12627-13-3) cement

Add time:08/19/2019    Source:sciencedirect.com

This work investigated the synergistic impact of silicate- and MgO-reactivity on the performance of Mg-silicate-based cement. Ceramic waste (CW) and glass waste (GW) as two silicate sources were used. Different decarbonation temperatures (800 and 1200 °C) were applied on magnesium carbonate to yield MgOs with different reactivities (MgO800 and MgO1200). Highest strength and shortest setting times associated with an enhancement in silicate dissolution rate and the formation of large magnesium silicate hydrate (MSH) were recorded in case of GW-MgO800-H2O system. The use of MgO1200 resulted in the retardation of MSH-formation rate in both of GW-MgO-H2O and CW-MgO-H2O systems. Comparing with GW-MgOs set, the CW-MgOs one showed the lowest performance at all curing ages. Due to high alumina content in CW, secondary hydrotalcite-like phases were detected in CW-MgOs alongside MSH-phase.

We also recommend Trading Suppliers and Manufacturers of SILICATE (cas 12627-13-3). Pls Click Website Link as below: cas 12627-13-3 suppliers

Prev:Synthesis of mesoporous CuFe/SILICATE (cas 12627-13-3)s catalyst for methanol steam reforming
Next:Delaying the hydration of Portland cement by sodium SILICATE (cas 12627-13-3): Setting time and retarding mechanism)