Strength development and microstructural characteristics of Barium hydroxide (cas 17194-00-2)-activated ground granulated blast furnace slag
-
Add time:08/18/2019 Source:sciencedirect.com
In this study, barium hydroxide was proposed as a main activator for ground granulated blast-furnace slag (GGBFS) to produce a strong binder, and it was compared to calcium hydroxide in terms of strength development, reaction products, and microstructure. The Ba(OH)2-activated GGBFS (BHAS) achieved a significantly higher compressive strength than Ca(OH)2-activated GGBFS (CHAS), except at 3 days, mainly due to (1) the more formation of hydration products, leading to a notable reduction in pore sizes and volume, and (2) the higher solubility of Ba(OH)2, resulting in a higher dissolution of GGBFS than that of Ca(OH)2. Although calcium silicate hydrate (C-S-H) was a major reaction product in both mixtures, the Ca/Si ratios were much different. In the BHAS, the presence of barium ions prohibited the synthesis of ettringite and monocarboaluminate, which formed in the CHAS mixtures, but it induced Ba-bearing products, strätlingite, and the hydrotalcite-like phase. The removal of ettringite was the cause of the lower strength of the BHAS at 3 days compared to that of the CHAS.
We also recommend Trading Suppliers and Manufacturers of Barium hydroxide (cas 17194-00-2). Pls Click Website Link as below: cas 17194-00-2 suppliers
Prev:Original articleConsolidation of lime mortars with ethyl silicate, nanolime and Barium hydroxide (cas 17194-00-2). Effectiveness assessment with microdrilling data
Next:Original articleConsolidation of weak lime mortars by means of saturated solution of calcium hydroxide or Barium hydroxide (cas 17194-00-2)) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Regular ArticleSolution-processed Barium hydroxide (cas 17194-00-2) modified boron-doped ZnO bilayer electron transporting materials: Toward stable perovskite solar cells with high efficiency of over 20.5%08/22/2019
- Research paperRadium removal from mine waters with the application of barium chloride and zeolite: comparison of efficiency08/21/2019
- Enhancement of reactivity of calcium hydroxide-activated slag mortars by the addition of Barium hydroxide (cas 17194-00-2)08/20/2019
- Original articleConsolidation of weak lime mortars by means of saturated solution of calcium hydroxide or Barium hydroxide (cas 17194-00-2)08/19/2019
- Original articleConsolidation of lime mortars with ethyl silicate, nanolime and Barium hydroxide (cas 17194-00-2). Effectiveness assessment with microdrilling data08/17/2019
- Original articleLaboratory and onsite study of Barium hydroxide (cas 17194-00-2) as a consolidant for high porosity limestones08/16/2019
-
Health and Chemical more >