Effect of curing temperature and relative humidity on the hydrates and porosity of calcium sulfoaluminate cement

Add time:08/17/2019    Source:sciencedirect.com

The main objective of this study was to investigate the effect of curing temperature and relatively humidity (RH) on the hydrates and porosity of calcium sulfoaluminate (CSA) cement pastes. A series of experiments including X-ray diffraction (XRD), thermogravimetric (TG) and mercury intrusion porosimetry (MIP) were performed. The results indicate that the formation of hydration products and pore characteristics of CSA cement are dependent on the curing conditions. The formation of ettringite is favor of curing with low temperature and high RH. The rate of formation of aluminum hydroxide (AH3) and monosulfoaluminate (Ms) is well promoted when curing temperature and RH are rising. The total porosity of CSA cement paste is gradually decreased by curing with low temperature and high RH.

We also recommend Trading Suppliers and Manufacturers of CALCIUM HYDROXIDE HYDRATE) (cas 1332-69-0). Pls Click Website Link as below: cas 1332-69-0 suppliers

Prev:Research PaperExtraction of alumina from KAOLIN (cas 1332-58-7) by a combination of pyro- and hydro-metallurgical processes
Next:Influence of calcium to silica ratio on H2 gas production in calcium silicate hydrate)