Thermosets derived from diallyl-containing main-chain type benzoxazine polymers

Add time:08/17/2019    Source:sciencedirect.com

To achieve high-performance thermosets, three diallyl-containing main-chain type benzoxazine polymers, (MCBP) were prepared from Mannich condensation of 2,2′-diallyl bisphenol A, paraformaldehyde, and three diamines: 4,4′-diaminodiphenylmethane (DDM), 4,4′-oxydianiline (ODA), and 2,2′-bis(4-(4-aminophenoxy)phenyl)propane (BAPP), respectively. These MCBPs can be cured and general a phenolic hydroxyl type benzoxazine thermosets even though no free ortho and free para positions to the oxygen of oxazine in their structures. After thermally curing, the resulting thermosets display much higher Tg than the thermosets of 2,2′-diallyl bisphenol A/aniline-based, 2-allyl phenol/DDM-based, and 2-allylphenol/ODA-based benzoxazine, demonstrating the advantage of MCBP on thermal properties over monomer type benzoxazines. The refractive index of the thermosets is higher than 1.689 at 589 nm, which is relatively high compared with other polymers. These results demonstrate the advantage of diallyl-containing MCBPs on thermal properties and refractive index over allyl-containing monomer type benzoxazines.

We also recommend Trading Suppliers and Manufacturers of diallyl G (cas 127808-81-5). Pls Click Website Link as below: cas 127808-81-5 suppliers

Prev:Complexes of Co(II), Ni(II) and Cu(II) with lapachol
Next:[λ‑Carrageenan‑calcium phosphate] and [sodium alginate‑calcium phosphate] modified with dimethyl diallyl ammonium chloride and diallylamin co-polymer as efficient adsorbents of anionic dyes)