Mixed monolayers of poly(VINYL STEARATE (cas 111-63-7)) with its monomer

Add time:08/22/2019    Source:sciencedirect.com

A marked gradient in surface pressure develops in monolayers of poly(vinyl sterate) (PVS) during compression. The gradient varies with position along the trough: it is large in the region close to the compression barrier and also near the other end of the trough, but relatively small at intermediate positions. In mixed monolayers of PVS with vinyl stearate (VS) the gradient is large and almost independent of the composition until the VS content exceeds about one third. Further increases in the proportion of VS cause decreases in gradient, and at VS mole fractions greater than about 0.65 the gradient is negligible. With pure PVS monolayers the gradient, once formed, remains constant for at least 90 min, but in films containing VS the gradient slowly decreases. The mixed films exhibit negative deviations in the area per repeat unit when compared to the averaged areas, with the maximum deviation occurring at a composition of 50 mol% (calculated on the basis of the PVS repeat unit). The fracture pressure is a function of the composition of the monolayer, with the maximum at about 90 mol% of PVS.

We also recommend Trading Suppliers and Manufacturers of VINYL STEARATE (cas 111-63-7). Pls Click Website Link as below: cas 111-63-7 suppliers

Prev:Polymorphic behavior of VINYL STEARATE (cas 111-63-7)
Next:Influence of soy protein isolate on the thermal stability of poly(vinyl chloride) in the presence or absence of calcium and zinc stearates)