Original articlePoly(acrylonitrile-co-3-aminocarbonyl-3-butenoic acid methyl ester): A better precursor material for carbon fiber than acrylonitrile terpolymer

Add time:08/25/2019    Source:sciencedirect.com

In order to improve the stabilization and spinnability of polyacrylonitrile, a bifunctional comonomer containing both ester and amide groups was synthesized to prepare poly(acrylonitrile-co-3-aminocarbonyl-3-butenoic acid methyl ester) [P(AN-co-ABM)] copolymers used as the carbon fiber precursor instead of poly(acrylonitrile-acrylamide-methyl acrylate) [P(AN-AM-MA)] terpolymer. The differential scanning calorimetry and thermogravimetry results show that the stabilization of P(AN-co-ABM) have been remarkably improved by ABM compared with P(AN-AM-MA) terpolymer, such as lower initiation temperature, broadened exothermic peak and smaller activation energy. Moreover, the spinnability of P(AN-co-ABM) is also improved by ABM due to the lubrication of ester groups in ABM. This study clearly shows that P(AN-co-ABM) copolymer is a better material for use as a carbon fiber precursor than P(AN-AM-MA) terpolymer.

We also recommend Trading Suppliers and Manufacturers of 3-(AMINOCARBONYL)-1,4-DIMETHYLPYRIDINIUM CHLORIDE (cas 110999-36-5). Pls Click Website Link as below: cas 110999-36-5 suppliers

Prev:Inhibition of IKK-2 by 2-[(aminocarbonyl)amino]-5-acetylenyl-3-thiophenecarboxamides
Next:Original articleDesign, synthesis and biological evaluation of 6-substituted aminocarbonyl benzimidazole derivatives as nonpeptidic angiotensin II AT1 receptor antagonists)