Research articlesFeatures of thermal and magnetic properties of nonstoichiometric DyB50 boride: The influence of the magnetic phase transition and crystal electric field
-
Add time:08/23/2019 Source:sciencedirect.com
The specific heat, thermal expansion and magnetic properties of polycrystalline sample of nonstoichiometric dysprosium boride DyB50, that was synthesized by boron-thermal reduction of the metal from its oxide in vacuum, were studied at 2–300 K. The measurements revealed a heat capacity and magnetic susceptibility anomalies at about TN ≈ 6.3 K, caused by the transition to an antiferromagnetic state. The anomalies of studied properties of DyB50 at higher temperatures have been ascribed to the influence of crystal electric field (CEF). The scheme of CEF-splitting of Dy3+ ion ground level in boride has been proposed.
We also recommend Trading Suppliers and Manufacturers of LUTETIUM BORIDE (cas 12688-52-7). Pls Click Website Link as below: cas 12688-52-7 suppliers
Prev:Effect of formation of calcium carbonate on foam stability in Neodol 25-3S (cas 12688-28-7) anionic surfactant systems
Next:Specific features of the heat capacity and thermal expansion of icosahedral holmium boride HoB50 at temperatures of 2–300 K) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- MetallurgyStandard enthalpies of formation of some lutetium alloys by high-temperature direct synthesis calorimetry08/28/2019
- Standard entropy for borides of non-transition metals, rare-earth metals and actinides☆08/27/2019
- Chapter 1 - Introduction to Lanthanide Series (From Lanthanum to Lutetium)08/26/2019
- Enthalpies of formation of rare-earth borides from first principles. Comparison with experimental values08/25/2019
- Specific features of the heat capacity and thermal expansion of icosahedral holmium boride HoB50 at temperatures of 2–300 K08/24/2019
-
Health and Chemical more >