Original ArticleThe effect of calcium zirconate modifications on the microstructure and functional properties of Sodium niobate (cas 12738-14-6) thin films prepared by chemical solution deposition

Add time:08/28/2019    Source:sciencedirect.com

Sodium niobate (cas 12738-14-6) thin films doped with manganese (NN), and NN films modified with 5 or 10 mol % calcium zirconate (CZ) on platinized silicon substrates were prepared by chemical solution deposition. The 250-nm-thick films crystallize in a perovskite phase with fine, equiaxed grains. The NN films exhibit well-shaped ferroelectric loops with a remanent polarization and coercive field of ∼10 μC/cm2 and ∼100 kV/cm, respectively. The modification with CZ strongly influences the ferroelectric response of the films: the remanent polarization progressively decreases to around 2.5 μC/cm2. The absence of an anti-ferroelectric response, which has previously been confirmed in bulk NN-CZ ceramics, is attributed to the nanoscale microstructure and residual thermal stresses. All the studied films exhibit a piezoelectric response with the highest piezoelectric d33 coefficient of 35 pm/V at 300 kV/cm bias field for the NN modified films with 5 mol % CZ, making them candidates for lead-free piezoelectric thin-film applications.

We also recommend Trading Suppliers and Manufacturers of Sodium niobate (cas 12738-14-6). Pls Click Website Link as below: cas 12738-14-6 suppliers

Prev:Original ArticleA new family of Sodium niobate (cas 12738-14-6)-based dielectrics for electrical energy storage applications
Next:Novel polyacrylonitrile/potassium Sodium niobate (cas 12738-14-6) composites with superior dielectric and thermal properties)