Precipitation and characterization of ZINC BORATE (cas 12767-90-7)s from hydrometallurgical processing of zinc ash

Add time:08/24/2019    Source:sciencedirect.com

Zinc ash has been used as a zinc source for precipitation of zinc borates through leaching–purification–precipitation route. Zinc ash containing about 71% Zn, 0.6% Fe, 28% Cl−, 0.2% Pb, and traces other elements such as Cu, Cd, As etc. in ppm level were leached in sulfuric acid. The leach solutions generated were purified by pH adjustment, followed by precipitation of borates using borax (Na2B4O7·10H2O). It has been observed that, the phase compositions of precipitated zinc borates as well as their morphologies are quite sensitive to B/Zn molar ratio, solution pH, precipitation temperature and ageing period. Precipitation of particular zinc borate phase of interest (3ZnO·3B2O3·3.5H2O) was found to be facilitated at higher precipitation temperature (≥95 °C) and in the pH range 5.5–6.0 with B/Zn molar ratio >4.0.

We also recommend Trading Suppliers and Manufacturers of ZINC BORATE (cas 12767-90-7). Pls Click Website Link as below: cas 12767-90-7 suppliers

Prev:Synthesis, characterization and standard molar enthalpies of formation of two ZINC BORATE (cas 12767-90-7)s: 2ZnO·2B2O3·3H2O and ZnB4O7
Next:Polymer paperInteraction of sodium carboxymethylamylose with aqueous surfactants in both the presence and the absence of added salt: mixed micelles and inclusion complexes)