Electronic materialCrystal growth and optical characterisation of Cr3+-doped YAl3(BO3)4

Add time:08/27/2019    Source:sciencedirect.com

This paper reports the high temperature top-seeded solution growth (TSSG) of large single crystals of Cr3+-doped YAl3(BO3)4 from a K2Mo3O10B2O3 flux cooled at a rate of 2–4 K per day in the temperature range 950–1060°C, using a crystal rotation rate of 4–6 rpm. Optical absorption measurements at T = 300 K reveal broad bands associated with transitions from the 4A2 ground state of Cr3+ to the 4T2 and 4T1 excited states. The doublet R lines and their one-phonon sideband are clearly resolved at room temperature in both absorption and luminescence spectra: the splitting of the R lines demonstrates the effect of the even-parity trigonal distortions of their environment on the 4A2 and 2E levels of the Cr3+ ions.

We also recommend Trading Suppliers and Manufacturers of Huntite (CaMg3(CO3)4) (cas 19569-21-2). Pls Click Website Link as below: cas 19569-21-2 suppliers

Prev:Preparation and some properties of rare earth iron borates, RFe3 (BO3)4
Next:The synthesis of a 4-PHENYLISOQUINOLINE (cas 19571-30-3) from a 3-phenylisoquinoline by utilization of a nitrogen analog of the pinacol rearrangement)