Short communicationElectrochemical analysis of diffusion behavior and nucleation mechanism for neodymium complex in potassium bis(trifluoromethylsulfonyl)amide melts

Add time:08/27/2019    Source:sciencedirect.com

The electrochemical behavior of Nd(III) in potassium bis(trifluoromethyl-sulfonyl) amide (KTFSA) melts was investigated in this study. It is speculated that the first reduction peak around + 2.3 V likely corresponds to the formation of Nd(II). The electrochemical analysis revealed that the reduction peak of Nd(III) around + 1.0 V would be based on the following reaction; [Nd(III) + 3e− → Nd(0)]. The diffusion coefficient of Nd(III) in KTFSA melts was estimated to be 4.39 × 10− 10 m2 s− 1 at 483 K by semi-differential analysis in voltammogram. Moreover, the nucleation and the growth process of Nd(0) were evaluated from chronoamperometry at 473 K. The result indicated that the nucleation mechanism of Nd nuclei altered from instantaneous to progressive nucleation when the induced overpotential became more negative than the peak potential of Nd(0) electrodeposition estimated from the voltammogram.

We also recommend Trading Suppliers and Manufacturers of potassium amide (cas 17242-52-3). Pls Click Website Link as below: cas 17242-52-3 suppliers

Prev:This article is part of the Special Issue on Solid-State NMR of Biomolecular AssembliesInactivation in the potassium channel KcsA☆
Next:Potent and selective inhibitors of the TASK-1 potassium channel through chemical optimization of a bis-amide scaffold)