Preparation, characterizations and properties of sodium alginate grafted Acrylonitrile (cas 107-13-1)/polyethylene glycol electrospun nanofibers

Add time:07/13/2019    Source:sciencedirect.com

In this work, to improve the spinnability of sodium alginate, potassium persulfate (KPS) was used as initiator, SA was modified with acrylonitrile (AN) to prepare sodium alginate-polyacrylonitrile copolymer (SA-g-AN), and SA-g-AN/PEG composite solutions were prepared by blending SA-g-AN and polyethylene glycol (PEG) as spinning solution to prepare corresponding electrospun nanofibers. The chemical structure and thermal stability of SA-g-AN were characterized by infrared spectroscopy (FTIR) and differential scanning calorimetry (DSC). The physical properties of SA-g-AN and SA-g-AN/PEG spinning solution were determined by viscometer, surface tension meter and electrical conductivity meter, the morphology of SA-g-AN and SA-g-AN/PEG electrospun fibers were observed by scanning electron microscopy (SEM). And the oil-water separation performance and water resistance of SA-g-AN electrospun fibers were also investigated. The results revealed that: the graft modification of acrylonitrile significantly improved the electrospinnability of sodium alginate. The water-resistance of modified graft copolymer was improved as well as the thermal stability, and the electrospun nanofibers had a uniform morphology and stable oil-water separation performance.

We also recommend Trading Suppliers and Manufacturers of Acrylonitrile (cas 107-13-1). Pls Click Website Link as below: cas 107-13-1 suppliers

Prev:Synthesis of 16α-bromoacetoxy androgens and 17 β-bromoacetylamino-4-androsten-3-one: Potential affinity labels of human placental aromatase
Next:Influence of operating parameters on the single-pass photocatalytic removal efficiency of Acrylonitrile (cas 107-13-1))