Synthesis and thermionic properties of tungsten–barium titanate composites

Add time:08/27/2019    Source:sciencedirect.com

The potential of novel tungsten–barium titanate composites as thermionic emitters is explored. Composites ranging from 20% to 80% tungsten by mass were prepared by sintering in an Ar–H2 atmosphere. XRD and SEM studies indicate four major micro-constituents; W, BaTiO3, Ba4(Ti,Fe)12O27 and BaWO4. Richardson work functions (φR) and Richardson constants (AR) were determined using a Schottky diode arrangement at temperatures ranging from 1223 to 1473 K. Work functions ranged from 2.67 eV to 3.32 eV with a shallow minimum at 40% by mass W and were relatively constant (∼2.7–2.8 eV) in the range 30–70% by mass W. The decrease in work function was accompanied by a strong decrease in AR from 39.3 A cm−2 K−2 to 0.02 A cm−2 K−2 over the range 20–70% by mass W. The reduction in both φR and AR was associated with the major conversion of the surface to BaWO4 and Ba4Ti12O27 during the activation treatment before emission testing.

We also recommend Trading Suppliers and Manufacturers of BARIUM CALCIUM TUNGSTEN OXIDE 99.9% (cas 15552-14-4). Pls Click Website Link as below: cas 15552-14-4 suppliers

Prev:Palladium(II) complexes bearing 2-(1H-imidazol/oxazol-2-yl)-pyridines: Synthesis, structures and ligand effects in Suzuki–Miyaura cross-coupling
Next:Preparation and characterization of high purity calcium, strontium and barium)