Origin of light scattering in ytterbium doped calcium fluoride transparent ceramic for high power lasers

Add time:09/02/2019    Source:sciencedirect.com

The origin of light scattering defects was studied in transparent 6 at% Yb:CaF2 ceramics. Samples were synthesized by a soft chemistry route followed by sintering and hot pressing which leads to highly transparent ceramics with low scattering losses (0.016 cm−1 at 1200 nm). Light scattering defects were studied using scanning transmission electron microscopy (STEM) and high angle annular dark field-STEM (HAADF-STEM) techniques. Energy dispersive X-ray spectroscopy showed a 50% increase in Yb3+ concentration at grain boundaries. A 3–5 nm thick oxygen rich phase was detected at some grain boundaries by both HAADF-STEM and EDS. The origin of the oxygenized grain boundaries was traced to a 2–15 nm thick oxygenized shell present on the starting powders. Analysis of high resolution HAADF-STEM images revealed that Yb3+ substitutes into the fluorite lattice as clusters rather than individual ions, but the types of clusters could not be identified by this imaging technique.

We also recommend Trading Suppliers and Manufacturers of YTTERBIUM FLUORIDE OXIDE (cas 15587-02-7). Pls Click Website Link as below: cas 15587-02-7 suppliers

Prev:Luminescence enhancement of nanosized ytterbium and europium fluorides by surface complex formation with aromatic carboxylates
Next:High-pressure synthesis, crystal structure, and structural relationship of the first ytterbium fluoride borate Yb5(BO3)2F9)