Corrosion resistance of a novel SnO2-doped dicalcium phosphate coating on AZ31 magnesium alloy
-
Add time:08/31/2019 Source:sciencedirect.com
A SnO2-doped dicalcium phosphate coating was prepared on AZ31 alloy by means of hydrothermal deposition. The results showed that the coating possessed a globular morphology with a long lamellar crystalline structure and a thickness of approximately 40 μm. The surface of the coating became smooth with an increase additive amount of the SnO2 nanoparticles. The corrosion current density and hydrogen evolution rate of the coating prepared in presence of SnO2 were reduced compared to the coating without SnO2 and the bare AZ31 substrate, indicating an improvement in the corrosion resistance of the SnO2-doped coating.
We also recommend Trading Suppliers and Manufacturers of ETHYLENEDIAMINETETRAACETIC ACID DICALCIUM SALT (cas 19709-85-4). Pls Click Website Link as below: cas 19709-85-4 suppliers
Prev:Wettability of calcite and mica modified by different long-chain fatty acids (C18 acids)
Next:Original articleProliferation and gene expression of osteoblasts cultured in DMEM containing the ionic products of dicalcium silicate coating☆) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Biomimetic scaffolds based on hydroxyapatite nanorod/poly(d,l) lactic acid with their corresponding apatite-forming capability and biocompatibility for bone-tissue engineering09/04/2019
- Original ResearchDiet-induced obesity and weight loss alter bile acid concentrations and bile acid–sensitive gene expression in insulin target tissues of C57BL/6J mice09/03/2019
- ReviewPharmaceutical salts: A summary on doses of salt formers from the Orange Book09/02/2019
- Original articleProliferation and gene expression of osteoblasts cultured in DMEM containing the ionic products of dicalcium silicate coating☆09/01/2019
-
Health and Chemical more >