Direct synthesis of a solid calcium-silicate-hydrate (C-S-H)

Add time:09/02/2019    Source:sciencedirect.com

We present new results on solid (monolithic) synthetic C-S-H made at room temperature from easily obtainable calcium sources (calcium oxide, calcium hydroxide) and nanosilica (w/s = 2) with a 2 minute mixing time. Using synchrotron X-ray diffraction combined with TGA/DSC, 29Si NMR and synchrotron pair distribution function (PDF) data we show that the solid C-S-H is crystallographically similar to the more conventionally made synthetic C-S-H slurry. We show that C-S-H is present after 1 day curing (C/S = 0.81) and no X-ray visible portlandite is present at day 3. PDF data shows that the ordered domain size is 2.5 – 4.5 nm, depending on the fit chosen.

We also recommend Trading Suppliers and Manufacturers of CALCIUM SILICATE HYDRATE (cas 1344-96-3). Pls Click Website Link as below: cas 1344-96-3 suppliers

Prev:Modification of poly(ethylene glycol) on the microstructure and mechanical properties of CALCIUM SILICATE HYDRATE (cas 1344-96-3)s
Next:Magnesium and CALCIUM SILICATE HYDRATE (cas 1344-96-3)s, Part I: Investigation of the possible magnesium incorporation in CALCIUM SILICATE HYDRATE (cas 1344-96-3) (C-S-H) and of the calcium in magnesium silicate hydrate (M-S-H))