Copolymerization of Pyrrole and Thienyl end Capped Cyclohexanone Formaldehyde Resin with Ce(IV) Oxidic Dibenzoate

Add time:07/19/2019    Source:sciencedirect.com

Block copolymers of polypyrrole (PPy) and thienyl end capped cyclohexanone formaldehyde resin (ThCFR) were synthesized via chemical oxidative polymerization of (Py) and ThCFR in the presence of cerium (IV) oxidic dibenzoate (CODB). The treatment of Py with CODB was maintained in non-aqueous media at room temperature. Several solvents including toluene, dichloromethane (DCM), were used. Besides the role of reaction media, the effect of ceric (IV) oxidic compound on polymerization was investigated. Reactions with constant amount of Py, and CODB to Py mol ratios of 0.33:1.0, 0.5:1.0 and 1.0:1.0 were observed. The results showed that in one-hour limited time, block copolymers could be obtained in toluene and dichloromethane with CODB: Py: ThCFR mol ratio of 1.0: 1.0: 0.01. Conductivities of polypyrroles were determined by 4-point probe technique. Block copolymers were prepared in dichloromethane and toluene, respectively.

We also recommend Trading Suppliers and Manufacturers of (R)-1,1'-BI-2-NAPHTHOL DIBENZOATE (cas 291772-40-2). Pls Click Website Link as below: cas 291772-40-2 suppliers

Prev:Novel MgCl2-supported catalyst containing diol dibenzoate donor for propylene polymerization
Next:Lipase-catalyzed alcoholysis of diol dibenzoates: selective enzymatic access to the 2-benzoyl ester of 1,2-propanediol and preparation of the enantiomerically pure (R)-1-O-benzoyl-2-methylpropane-1,3-diol)