Polypyrrole doped with DODECYLBENZENE (cas 123-01-3) sulfonate as a protective coating for copper
-
Add time:09/06/2019 Source:sciencedirect.com
Polypyrrole doped with DODECYLBENZENE (cas 123-01-3) sulfonate (DBS) was formed at copper, PPy–DBS, and at a thin coating of polypyrrole doped with tartrate to form a bilayer of PPy–Tar/PPy–DBS at copper. The two polymer coatings showed good protective properties. Breakdown potentials of 0.85 V and 0.93 V vs SCE were recorded in 0.1 M NaCl for the PPy–DBS and PPy–Tar/PPy–DBS bilayer, respectively. The more protective properties of the bilayer were explained in terms of an adherent thin polymer that was formed in the tartrate solution without significant dissolution of copper before the polymer was nucleated. The protective properties were also evident from open-circuit potential measurements where the potential adopted by the polymer coated copper remained constant and higher than the potential of the uncoated copper for several days. Furthermore, a decrease in the corrosion current density was observed from 1.95 μA cm−2 for copper to 0.12 μA cm−2 for the bilayer. The concentration of DBS had an influence on the properties of the polymer films with more protective films formed in 0.05 M DBS. The critical micelle concentration of DBS in 0.3 M pyrrole was measured as 9.8 mM, indicating a relatively high level of micelles in 0.05 M DBS. The protective properties of the coating were attributed to the large and immobile DBS anion, which gives the polymer cation exchange properties, minimising the uptake of chloride anions. In addition, the incorporation of anionic micelles may occur to repel further the chloride anions.
We also recommend Trading Suppliers and Manufacturers of DODECYLBENZENE (cas 123-01-3). Pls Click Website Link as below: cas 123-01-3 suppliers
Prev:Corrosion inhibition efficiency of triethanolammonium DODECYLBENZENE (cas 123-01-3) sulfonate on Q235 carbon steel in simulated concrete pore solution
Next:DODECYLBENZENE (cas 123-01-3) transformations: Dealkylation and disproportionation over immobilized ionic liquid catalysts) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Coaxial electrospinning with sodium DODECYLBENZENE (cas 123-01-3) sulfonate solution for high quality polyacrylonitrile nanofibers09/27/2019
- Highly crystalline and soluble DODECYLBENZENE (cas 123-01-3) sulfonic acid doped poly(o-toluidine)09/26/2019
- Dispersion of Fe3O4 suspensions using sodium DODECYLBENZENE (cas 123-01-3) sulphonate as dispersant09/25/2019
- The study of optical, dielectric and optoelectronic properties of DODECYLBENZENE (cas 123-01-3) sulfonic acid doped polyaniline09/24/2019
- Research paperDFT study of the intercalation of layered double hydroxides and layered hydroxide salts with dodecylsulfate and DODECYLBENZENE (cas 123-01-3) sulfonate: Exfoliation and hydration properties09/10/2019
- A case study of aggregation behaviors of titanium dioxide nanoparticles in the presence of DODECYLBENZENE (cas 123-01-3) sulfonate in natural water09/09/2019
- Electrosynthesis and properties of the polypyrrole/DODECYLBENZENE (cas 123-01-3) sulfonate polymer. Influence of structural micellar changes of sodium DODECYLBENZENE (cas 123-01-3) sulfonate at high concentrations09/08/2019
- DODECYLBENZENE (cas 123-01-3) transformations: Dealkylation and disproportionation over immobilized ionic liquid catalysts09/07/2019
- Corrosion inhibition efficiency of triethanolammonium DODECYLBENZENE (cas 123-01-3) sulfonate on Q235 carbon steel in simulated concrete pore solution09/05/2019