Synthesis and characterization of poly(diphenylacetylenes) containing both hydroxy and halogen/alkyl groups as gas separation membranes

Add time:09/10/2019    Source:sciencedirect.com

Diphenylacetylene containing siloxy and halogen/alkyl groups (P-t-BuMe2SiO-C6H4CCC6H4-p-X, X = Cl, Br, I, Me, Et, 1b–f, respectively) were polymerized with TaCl5-n-Bu4Sn catalyst to provide high molecular weight polymers (2b–f) in good yields. These polymers afforded tough free-standing membranes by casting from toluene solution. Desilylation of these siloxy-containing polymer membranes was carried out with trifluoroacetic acid to give membranes of poly(diphenylacetylenes) having hydroxy and halogen/alkyl groups (3b–f). Polymers 2b–f were soluble in nonpolar solvents such as cyclohexane, toluene, and THF, while polymers 3b–f were insoluble in these solvents. The oxygen permeability coefficients (PO2) of membranes 2b–f and 3b–f were in the range of 140–280 and 12–190 barrers, respectively. The gas permeabilities of most membranes (2b–e and 3b–f) were higher than those of the corresponding polymer membranes without halogen/alkyl substituents (2a and 3a), suggesting that introduction of small spherical groups (halogen and methyl) into the polymers 2a and 3a enhances gas permeability. The incorporation of halogen atoms into the present membranes was more effective to improve gas permeability than methyl and ethyl groups. The points of 3b–e in the PCO2 versus PCO2/PN2andPCO2/PCH4 plots were located obviously above Robeson's upper bound.

We also recommend Trading Suppliers and Manufacturers of 4-Bromo diphenylacetylene (cas 13667-12-4). Pls Click Website Link as below: cas 13667-12-4 suppliers

Prev:Thermodynamically stable, highly emissive poly(diphenylacetylene) derivative containing long alkyl side chain without silylene linkage
Next:Insertion reaction between planar chiral cyclopalladated derivatives of ferrocene and diphenylacetylene)