Fabrication of waveguides by fs-laser micromachining in Dy3+/Eu3+ doped barium borate glass with broad emission in the visible spectrum

Add time:09/10/2019    Source:sciencedirect.com

Boron-based glasses are relevant materials for optical applications on account its ability to hold large amount of oxide modifiers and rare-earth ions. The barium borates ones are particularly interesting due to its designed second and third-order optical nonlinearities. Despite the interest on barium borate glasses for linear and nonlinear optics, the fabrication of active elements for optical microcircuits are still scare. In this paper, we demonstrate the fabrication of three dimensional waveguides in barium borate glass with broad emission in the visible spectrum. Such performance was achieved through the co-doping with Dy 3+ and Eu 3+ ions, which together provide broad emissions at blue, yellow and red, along with the glass processing with femtosecond laser pulses. Almost circular waveguides, with diameter of approximately 5 μm and 7.8 mm long, were inscribed into the bulk of the glass by direct laser writing, whose support single mode guiding at 632.8 nm with propagation loss of (3 ± 1) dB/cm. When coupling UV light, such waveguides display the typical emission of Dy3+ and Eu3+ ions with its additional guiding throughout the waveguide length. The broad band emission and its guiding in the visible spectrum revel that the waveguides fabricated by femtosecond laser micromachining in co-doped barium borate glass are promising active elements for the development of optical micro-devices.

We also recommend Trading Suppliers and Manufacturers of Barium boron oxide (cas 13701-59-2). Pls Click Website Link as below: cas 13701-59-2 suppliers

Prev:Boronizing effect on the radiation shielding properties of Hardox 450 and Hardox HiTuf steels
Next:Regular ArticleSolubility products of sparingly soluble barium perborates in aqueous solution that contains B(OH)3 and H2O2 at 25 °C)