Effect of Ni–V loading on the performance of hollow anatase TiO2 in the catalytic combustion of dichloromethane

Add time:10/01/2019    Source:sciencedirect.com

A catalyst based on mixed V-Ni oxides supported on TiO2 (Ni–V/TiO2) was obtained using the sol–gel method. Its catalytic performance relative to dichloromethane (DCM) degradation was investigated. Characterization and analysis were conducted using transmission electron microscopy, H2 temperature-programmed reduction, pyridine–Fourier transform infrared spectroscopy (FTIR) characterization, and X-ray diffraction. Results showed that the original hollow anatase structure of pure TiO2 was well-maintained after Ni–V loading. The loading of NiO–VOx not only significantly improved the stability of pure TiO2 but also inhibited the formation of the by-product monochloromethane (MCM). Among the series of Ni–V/TiO2 catalysts, 4%Ni–V/TiO2 possessed the highest catalytic activity, with 90% DCM conversion at only 203°C. No by-products and no significant changes in the catalytic activity were observed during combustion of DCM after 100 hr of a continuous stability test. Furthermore, thermogravimetric analysis (O2-TG) and energy dispersive spectrometer (EDS) characterization of the used 4%Ni–V/TiO2 catalyst revealed that no coke deposition or chlorine species could be detected on the catalyst surface.

We also recommend Trading Suppliers and Manufacturers of DICHLOROMETHANE D (cas 1665-01-6). Pls Click Website Link as below: cas 1665-01-6 suppliers

Prev:Exposure to ambient dichloromethane in pregnancy and infancy from industrial sources and childhood cancers in California
Next:Individual stages of bacterial DICHLOROMETHANE D (cas 1665-01-6)egradation mapped by carbon and chlorine stable isotope analysis)