Removing molybdate from water using a hybridized zero-valent iron/magnetite/Fe(II) treatment system

Add time:09/24/2019    Source:sciencedirect.com

Batch tests were conducted to investigate molybdate removal in a hybridized zero-valent iron/Fe3O4/Fe(II) system (hZVI) in comparison with a conventional ZVI system. The hybrid system was created by employing a nitrate-Fe2+ pretreatment method to coat the ZVI grains with a magnetite (Fe3O4) surface and produce some discrete magnetite particles through a rapid ZVI-nitrate reaction. The co-presence of ZVI, Fe3O4, and Fe(II) species created a highly reactive system. Molybdate, a corrosion inhibitor, could not be effectively removed in a ZVI-only system. With the addition of Feaq2+, molybdate removal was moderately accelerated in a ZVI/Fe(II) system, possibly through the formation of Fe(II)–molybdate–iron oxide complex. In an hZVI system with magnetite and Feaq2+, molybdate was rapidly and sustainably removed via rapid reduction of Mo(VI) to lower valences, during which 1.1 mol Feaq2+ was consumed per 1 mol molybdate removal. While ZVI is the primary electron source for the redox reaction, magnetite may serve as an e−-conducting medium and host molybdate reduction reaction. Externally-supplied Fe2+ is essential to maintaining magnetite as the iron corrosion product and thus the high reactivity of ZVI surface. This study suggests that the hZVI system could overcome ZVI surface passivation problem and thus provide an effective chemical platform to harness the reactivity of ZVI for molybdate and potentially other water contaminants removal.

We also recommend Trading Suppliers and Manufacturers of Iron(II) molybdate(VI) (cas 13718-70-2). Pls Click Website Link as below: cas 13718-70-2 suppliers

Prev:Transport and retention of Molybdenum(VI) on iron oxide-coated sand: A modified multi reaction model
Next:Three-dimensional transfer of Cr(VI) co-precipitated with ferrihydrite containing silicate and its redistribution and retention during aging)