ε-Martensite formation for low strains in a lean duplex stainless steel

Add time:10/01/2019    Source:sciencedirect.com

Martensitic transformation induced by strain in duplex stainless steels is a good option to increase their strength and elongation. The influence of low deformation levels on the phase transformation was studied in a 2304 lean duplex stainless steel. It was demonstrated that this steel exhibited the phase transformation of austenite (γ) into epsilon (ε) and alpha (α′) martensite after cold rolling. The ε and α′ were observed in shear bands and close to the grain boundaries. The Shoji–Nishiyama relation 110γ//2110ε was observed. Hitherto, the ε formation has not been reported in the literature for this steel by cold deformation.

We also recommend Trading Suppliers and Manufacturers of N(ALPHA)-BPOC-N(EPSILON)-BOC-L-LYSINE (cas 18635-01-3). Pls Click Website Link as below: cas 18635-01-3 suppliers

Prev:Synthesis of dicyano-substituted ε-caprolactone and its (co)polymers
Next:Six-loop ε expansion study of three-dimensional n-vector model with cubic anisotropy)