Effect of rubber particles and steel fibers on frost resistance of roller compacted concrete in Potassium Acetate (cas 127-08-2) solution
-
Add time:09/27/2019 Source:sciencedirect.com
In this paper, the frost resistance of roller compacted concrete (RCC) mixed with rubber particles and steel fibers was investigated, 25% (by weight) Potassium Acetate (cas 127-08-2) (KAc) solution was the medium in freeze-thaw cycles. The mass loss, relative dynamic elastic modulus, microstructures, and pore structures were measured. The results show the accumulated mass loss is the greatest and up to 155.17 g/m2 after 300 freeze-thaw cycles in KAc solution when the rubber particles and the steel fibers are added at the same time. If the later hydration of cement is not considered, the improvement effect of the steel fibers and the rubber particles on the reduction of the relative dynamic elastic modulus is also not obvious. The addition of the rubber particles and the steel fibers does not effectively reduce the cracking caused by 300 freeze-thaw cycles in KAc solution because microcracks are observed in all specimens. The incorporation of the steel fibers and the rubber particles also cannot effectively reduce the increase of porosity caused by 300 freeze-thaw cycles in KAc solution.
We also recommend Trading Suppliers and Manufacturers of Potassium Acetate (cas 127-08-2). Pls Click Website Link as below: cas 127-08-2 suppliers
Prev:Acidification of Potassium Acetate (cas 127-08-2) and potassium citrate with/without KCl by electro-activation and impact of the solution on spores of Clostridium sporogenes PA 3679 at ambient temperature
Next:Research paperThe molecular structure of kaolinite–Potassium Acetate (cas 127-08-2) intercalation complexes: A combined experimental and molecular dynamic simulation study) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Full Length ArticleTransesterification of non-edible oils over Potassium Acetate (cas 127-08-2) impregnated CaO solid base catalyst09/29/2019
- Potassium Acetate (cas 127-08-2) supported on activated carbon for transesterification of new non-edible oil, bitter almond oil09/28/2019
- Research paperThe molecular structure of kaolinite–Potassium Acetate (cas 127-08-2) intercalation complexes: A combined experimental and molecular dynamic simulation study10/01/2019
- Acidification of Potassium Acetate (cas 127-08-2) and potassium citrate with/without KCl by electro-activation and impact of the solution on spores of Clostridium sporogenes PA 3679 at ambient temperature09/26/2019
- Application of electro-activated Potassium Acetate (cas 127-08-2) and potassium citrate solutions combined with moderate heat treatment on the inactivation of Clostridium sporogenes PA 3679 spores09/25/2019
- A novel synthesis of hierarchical porous carbons from resol by Potassium Acetate (cas 127-08-2) activation for high performance supercapacitor electrodes09/24/2019
- Preparation of Potassium Acetate (cas 127-08-2) intercalated metakaolinite09/10/2019
- Influencing factors of intercalation of Potassium Acetate (cas 127-08-2) into dickite using immersion method09/09/2019
-
Health and Chemical more >
-
Related Products
- Acetate de trimethylplomb
- Acetate kinase
- Potassium (2S,3S)-3-(ethoxycarbonyl)oxirane-2-carboxylate
- Potassium (4-formylphenyl)trifluoroborate
- Potassium (bromomethyl)trifluoroborate
- Potassium (R)-((3-ethoxy-1-methyl-3-oxoprop-1-enyl)amino)(4-hydroxyphenyl)acetate
- Potassium (R)-(4-hydroxyphenyl)((3-methoxy-1-methyl-3-oxoprop-1-enyl)amino)acetate
- Potassium (R)-[(3-ethoxy-1-methyl-3-oxoprop-1-enyl)amino]phenylacetate
- Potassium [(cyanomethyl)thio]acetate
- Potassium 1,2,3,6-tetrahydro-5-nitro-2,6-dioxopyrimidine-4-carboxylate