Electrocatalytic activity of nanostructured Ni and Pd–Ni on Vulcan XC-72R carbon black for methanol oxidation in alkaline medium

Add time:09/25/2019    Source:sciencedirect.com

Ni and Pd–Ni nanoparticles were chemically deposited on Vulcan XC-72R carbon black by impregnation method using NaBH4 as a reducing agent. The prepared electrocatalysts were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and energy-dispersive X-ray spectroscopy (EDX). The electrocatalytic activity of Ni/C and Pd–Ni/C electrocatalysts towards methanol oxidation in 0.5 M KOH solution was examined using cyclic voltammetry and chronoamperometry. Two methanol oxidation peaks were observed on the Pd–Ni/C at 0 and +860 mV. Their current density values are higher than those at Pd/C and Ni/C electrocatalysts by 1.92 and 1.68 times, respectively. The catalytic rate constant of methanol oxidation reaction at Ni/C and Pd–Ni/C electrocatalysts in (0.2 M MeOH + 0.5 M KOH) solution was estimated using double-step chronoamperometry as 5.64 × 103 and 6.25 × 103 cm3 mol−1 s−1, respectively. Pd–Ni/C is more stable than Pd/C and Ni/C electrocatalysts. Therefore, Pd–Ni/C is a suitable as a less expensive electrocatalyst for methanol oxidation in alkaline medium.

We also recommend Trading Suppliers and Manufacturers of Mercurous oxide，black (cas 15829-53-5). Pls Click Website Link as below: cas 15829-53-5 suppliers

Prev:Purification and growth of mercurous chloride single crystals
Next:Physical vapor transport growth of mercurous chloride crystals)