Synthesis and characterization of highly soluble and thermally stable new polyimides based on 3,5-diamino benzoyl amino phenyl-14H-dibenzo[a,j]xanthene

Add time:09/29/2019    Source:infona.pl

A new xanthene-containing diamine monomer was successfully synthesized in four steps by the condensation of β-naphthol and 4-nitrobenzaldehyde in the presence of p-toluenesulfonic acid catalyst, reduction of the nitro intermediate, the nucleophilic substitution reaction of amine compound and 3,5-dinitrobenzoyl chloride, and subsequent reduction of the dinitro compound. The diamine monomer could be obtained in quantitative yield. A series of novel organosoluble aromatic polyimides were prepared by direct polycondensation of synthesized diamine with four tetracarboxylic dianhydrides via a conventional two-step polymerization process. The polymers were obtained in quantitative yields with inherent viscosities of 0.20–0.74 dL/g. Most of the polymers dissolved in N-methyl-2-pyrrolidone, N,N-dimethylacetamide, N,N-dimethylformamide and dimethyl sulfoxide. The resulting polyimides exhibited good thermal stability; no weight loss was detected before a temperature of 450 °C in nitrogen. Wide-angle X-ray diffraction measurements showed that these polyimides were predominantly amorphous.

We also recommend Trading Suppliers and Manufacturers of Benzoyl J acid (cas 132-87-6). Pls Click Website Link as below: cas 132-87-6 suppliers

Prev:N-ortho-Ferrocenyl benzoyl dipeptide esters: Synthesis, structural characterization and in vitro anti-cancer activity of N-{ortho-(ferrocenyl)benzoyl}-glycine-l-alanine ethyl ester and N-{ortho-(ferrocenyl)benzoyl}-l-alanine-glycine ethyl ester
Next:Synergistic effects of N, N′‐bis (benzoyl) sebacic acid dihydrazide and talc on the physical and mechanical behaviors of poly(l‐latic acid))