Activated carbon adsorption of gold from cyanide-starved glycine solutions containing copper. Part 2: Kinetics

Add time:07/19/2019    Source:sciencedirect.com

The downstream processing of leachates arising from the dissolution of copper bearing gold ores in cyanide-starved alkaline glycine solutions is imperative for the successful implementation of the new leach system at industry level. This study investigates the behaviour of gold adsorption onto activated carbon in the presence of copper from cyanide-starved glycine solutions. The adsorption behaviour was kinetically investigated using the Fleming k,n model. The model had a high consistency with experimental data (up to 6 h) for both gold and copper as evidenced by the regression coefficient (R2) values which were close to 1. The effects of important parameters including glycine concentration, solution pH, cyanide concentration, initial gold concentration, adsorbent concentration and ionic strength of the solution were studied. The results showed that, except for initial gold and carbon concentrations, a variation of these major factors had a pronounced effect on copper adsorption and slightly affected the gold adsorption, both in terms of adsorption rate and overall recovery. It was also seen that the active carbon had a high adsorption tendency towards gold over copper. The gold and copper extraction from a cyanide-glycine solution containing 2 mg/L gold, 300 mg/L copper, pH 11, 5 g/L glycine, Cu:CN of 1:1 (123 mg/L CN) and 8 g/L carbon using lime as a pH modifier reached 99.0% and 52.8% respectively. Most copper and gold was recovered in the first 6 h. The corresponding initial adsorption rates are 1263.8 h−1 for gold and 19.0 h−1 for copper.

We also recommend Trading Suppliers and Manufacturers of Sodium copper cyanide (cas 14264-31-4). Pls Click Website Link as below: cas 14264-31-4 suppliers

Prev:Validation of cyanide copper electrodeposited layer on test coupons for anti-seizing and outgassing in Tokamak vacuum vessel
Next:The interaction between copper species and pyrite surfaces in copper cyanide solutions)