Evaluation of the CO2 tolerant cathode for solid oxide fuel cells: Praseodymium oxysulfates/Ba0.5Sr0.5Co0.8Fe0.2O3-δ

Add time:07/21/2019    Source:sciencedirect.com

An effective praseodymium oxysulfate/Ba0.5Sr0.5Co0.8Fe0.2O3-δ composite cathode with high stability in 10% CO2/air was investigated. The addition of 50 vol.% of the praseodymium oxysulfate shows much better tolerance to CO2, and reduced the polarization resistance of the cathode to 1/3 comparing with that of Ba0.5Sr0.5Co0.8Fe0.2O3-δ (BSCF). The CO2–temperature programmed desorption (TPD) and the electrochemical impedance spectroscopy (EIS) proved the effectiveness of the praseodymium oxysulfate phase to reduce the electrode resistance and to improve the CO2 resistance. The coefficient thermal expansion (CTE) rate along with the different volume percentage of praseodymium oxysulfate was also measured and it was found that the praseodymium oxysulfate helps to regulate the total CTE of the composite to match with doped-ceria electrolyte. It is proposed the higher acidity of Pr3+/4+ cations inhibited the reaction of alkaline earth metal oxide to form carbonates on the surface of the BSCF particles. The above results proved praseodymium oxysulfate/Ba0.5Sr0.5Co0.8Fe0.2O3-δ to be a highly active and stable cathode for solid oxide fuel cells.

We also recommend Trading Suppliers and Manufacturers of PRASEODYMIUM CARBONATE (cas 14948-62-0). Pls Click Website Link as below: cas 14948-62-0 suppliers

Prev:A study of the decomposition of praseodymium hydroxy carbonate and PRASEODYMIUM CARBONATE (cas 14948-62-0) hydrate
Next:Fluorescence intensity ratio and lifetime thermometry of praseodymium phosphates for temperature sensing)