Effect of temperature variation on the corrosion behaviour and semiconducting properties of the passive film formed on Chromium oxide (cas 11118-57-3) coatings exposed to saline solution

Add time:07/21/2019    Source:sciencedirect.com

The corrosion behaviour of Chromium oxide (cas 11118-57-3) coatings and semiconducting properties of the passive film formed on the surface of the coated samples when exposed to saline solution at a temperature range 25 °C–65 °C was investigated. The cyclic polarisation results revealed that the coatings tested at a electrolyte temperature range 25 °C–35 °C possess superior resistance to pitting corrosion when compared to coatings tested at higher temperatures. Our Mott-Schottky analysis suggests that this variation in corrosion resistance can be linked to the increase in the amount of the defect density present in the films and enhanced diffusion at higher temperatures.

We also recommend Trading Suppliers and Manufacturers of Chromium oxide (cas 11118-57-3). Pls Click Website Link as below: cas 11118-57-3 suppliers

Prev:Chromium oxide (cas 11118-57-3) formation on nanosecond and femtosecond laser irradiated thin chromium films
Next:Deposition of Chromium oxide (cas 11118-57-3)-chromium carbide coatings via high velocity suspension flame spraying (HVSFS))