The role of aluminium in C-A-S-H during sulfate attack on concrete

Add time:07/27/2019    Source:sciencedirect.com

Storage tests with C-A-S-H phases in Na2SO4 solutions (3 and 30 g/L SO4) were carried out to study changes in the C-A-S-H nanostructure during sulfate attack on concrete. Particular attention was paid to the availability of aluminium in C-A-S-H for ettringite formation. Ettringite only formed above the saturation pH of portlandite. The removal of aluminium from C-A-S-H decreased the Al/Si ratio and mean chain length (MCL) of the C-A-S-H phases. No ettringite formed in solutions below the saturation pH of portlandite. Here, decalcification of the C-A-S-H phases resulted in an increase in MCL. The formation of ettringite from aluminium in C-A-S-H exposed to Na2SO4 solutions is controlled by the availability of calcium. Sodium is adsorbed on deprotonated silanol groups in C-A-S-H. At 3 g/L SO4, the SO42− ions are adsorbed with calcium on deprotonated silanol groups, but at 30 g/L SO4, they are also bonded to other sites in C-A-S-H.

We also recommend Trading Suppliers and Manufacturers of Aluminum potassium sulfate (cas 15007-61-1). Pls Click Website Link as below: cas 15007-61-1 suppliers

Prev:Extraction and characterization of lignin from oil palm biomass via ionic liquid dissolution and non-toxic aluminium potassium sulfate dodecahydrate precipitation processes
Next:Isolation and identification of two novel butenolides as products of dimethylbenzoate metabolism by Rhodococcus rhodochrous N75)