Combustion synthesis of the titanium-aluminum-boron system

Article abstract of DOI:10.1111/j.1151-2916.1989.tb06268.x

TiB₂ and Al base composite powders, which will offer a weight-saving improvement in stiffness, were produced by combustion synthesis of Ti, Al, and B ternary powder mixtures. Finely dispersed TiB₂ was synthesized by reacting a mixture of Ti, Al, and B in the molar ratio of 1:1:4. The grain size of the TiB₂ formed was <0.5 μm, which was much smaller than that obtained from the reaction of a mixture of Ti, Al, and B in the molar ratio 1:1:2. These results are discussed in light of the reaction propagating velocity and heat removal during the combustion synthesis process.