Preparation and thermal properties of poly[acrylonitrile-co-(β- methylhydrogen itaconate)] used as carbon fiber precursor

Article abstract of DOI:10.1007/s10973-013-3534-0

In order to replace terpolymer with bipolymer, a bifunctional comonomer β-methylhydrogen itaconate (MHI) containing carboxyl group and ester group was synthesized to prepare poly[acrylonitrile-co-(β-methylhydrogen itaconate)] [P(AN-co-MHI)] bipolymers used as carbon fiber precursor for improving the stabilization and spinnability at the same time. The P(AN-co-MHI) bipolymers with different monomer feed ratios were characterized by elemental analysis, Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and differential scanning calorimetry (DSC). The results show that both the polymerization conversion and molecular mass of P(AN-co-MHI) reduce with the increasing MHI amounts in the feed due to the larger molecular volume of MHI than acrylonitrile (AN). The monomer reactivity ratios were calculated by Fineman-Ross and Kelen-Tuedos methods, the results show good agreement and MHI possesses higher reactivity than AN. Two parameters E_s = A1, 629 cm_-1 / A_{2, 244 cm 1} and SI = (I₀ - I _S) / I₀ were defined to evaluate the extent of stabilization, and the activation energy (E _a) of the cyclization was calculated by Kissinger method and Ozawa method. The FTIR, XRD, and DSC results show that P(AN-co-MHI) bipolymers exhibit significantly improved stabilization characteristics than PAN homopolymer, such as larger extent of stabilization, lower initiation temperature, and smaller E _a of cyclization, which is attributed to the ionic initiation by MHI comonomer and it is beneficial to preparing high-performance carbon fiber.