Y.-W. Chung et al. / Electrochimica Acta 53 (2007) 1703–1707
1707
will occur at a short period and only appear as one layer. When
the electrostatics-induced adsorption effect occurs at the surface
of colloidal crystal, the Ni egg-shell-roofed macroporous film
can be constructed.
It is anticipated that this special nanostructure can also be
prepared for other metals based on a template-mediated elec-
trodepositing process as the two important conditions are met,
i.e., an accurate control of electrodepositing behavior and the
presence of electrostatic-induced effect adsorption on the tem-
plate top. Because this nanostructure possesses a large surface
area and 3D well-ordered arrangement, it will have the further
potential for many applications, including magnetic device [25]
and surface-enhanced Raman spectroscopy [26].
[2] B. Cao, W. Cai, F. Sun, Y. Li, Y. Lei, L. Zhang, Chem. Commun. (2004)
604.
3] M. Winzer, M. Kleiber, N. Dix, R. Wiesendanger, Appl. Phys. A 63 (1996)
17.
4] S.I. Matsushita, T. Miwa, D.A. Tryk, A. Fujishima, Langmuir 14 (1998)
441.
1
[
[
6
6
[5] C. Hagleitner, A. Hierlemann, D. Lange, A. Kummer, N. Kerness, O. Brand,
H. Baltes, Nature 414 (2001) 293.
[6] B.P. Zhang, G. Isoya, T. Yasuda, Y. Ohfuti, C.Y. Liu, Y. Segawa, Nanotech-
nology 15 (2004) 698.
[
7] R. Torrecillas, A. Blanco, M.E. Brito, C. Lopex, M. Miguez, F. Mieseguer,
J.S. Moya, Acta Mater. 48 (2000) 4653.
[8] M. Tanaka, T. Motomura, M. Kawada, T. Anzai, T. Shiroya, K. Shimura,
M. Onishi, Biomaterials 21 (2000) 1471.
[
9] S. Han, X. Shi, F. Zhou, Nano Lett. 2 (2002) 97.
10] G.T. Duan, W.P. Cai, Y. Li, Z.G. Li, B.Q. Cao, Y.Y. Luo, J. Phys. Chem. B
10 (2006) 7184.
11] Y. Li, W.P. Cai, G.T. Duan, B.Q. Cao, F.Q. Sun, J. Mater. Res. 20 (2005)
38.
[
[
[
[
[
[
[
[
[
1
4
. Conclusion
3
12] Z. Chen, P. Zhan, Z.L. Wang, J.H. Zhang, W.Y. Zhang, N.B. Ming, C.T.
Chan, P. Sheng, Adv. Mater. 16 (2004) 417.
13] P.N. Bartlett, M.A. Ghanem, I.S.E. Hallag, P. de Groot, A. Zhukov, J. Mater.
Chem. 13 (2003) 2596.
14] J.A. Barnard, H. Fujiwara, V.R. Inturi, J.D. Jarratt, T.W. Scharr, J.L. Weston,
Appl. Phys. Lett. 9 (1996) 2758.
15] S. Zhang, J.De. Baets, M. Vereeken, A.Van. Calster, J. Electrochem. Soc.
Depending on the electrostatics-induced effect, it is antici-
pated that nickel or other metallic ions in the electrodeposition
solution will be adsorbed onto the colloid surface of template
top. Subsequently, these ions will be reduced preferentially at
these sites, and coat the colloidal particles gradually, until com-
plete coverage of the colloid particles by accurately controlling
the electrodeposition time. After removing the colloidal tem-
plate, the nanostructure of hollow sphere array will only appear
at the top of macroporous structure. Therefore, a special nanos-
tructure, i.e., the egg-shell-roofed macroporous films, consisting
of macroporous structure covered with a hollow sphere array on
the surface can be fabricated via the template-mediated elec-
trodeposition process.
146 (1999) 2870.
16] L. Xu, L.D. Tung, L. Spinu, A.A. Zakhidov, R.H. Baughman, J.B. Wiley,
Adv. Mater. 15 (2003) 1562.
17] Y. Hongwei, C.F. Blanford, J.C. Lytle, C.B. Carter, W.H. Smyrl, A. Stein,
Chem. Mater. 13 (2001) 4314.
18] P.N. Bartlett, J.J. Baumberg, S. Coyle, M.E. Abdelsalam, Faraday Discuss.
125 (2004) 117.
[
[
19] H. Wang, C.Y. Pan, Colloid Polym. Sci. 279 (2001) 98.
20] Y.W. Chung, I.C. Leu, J.H. Lee, M.H. Hon, Appl. Phys. A 79 (2004)
2
089.
[21] J.H. Yen, I.C. Leu, M.T. Wu, C.C. Lin, M.H. Hon, Diam. Relat. Mater. 14
2005) 841.
22] T. Sumida, Y. Wada, T. Kitamura, S. Yanagida, Chem. Commun. 17 (2000)
613.
Acknowledgements
(
[
The financial support through contracts NSC93-2216-E-006-
1
0
39 and NSC 94-2216-E-239-009 by the National Science
[
[
23] T. Sumida, Y. Wada, T. Kitamura, S. Yanagida, Langmuir 18 (2002) 3886.
24] F. Sun, W.P. Cai, Y. Li, B.Q. Cao, F. Lu, G.T. Duan, L.D. Zhang, Adv.
Mater. 16 (2004) 1116.
Council, Taiwan, ROC is greatly appreciated.
[
25] M.L. Povinelli, S.G. Johnson, J.D. Joannopoulos, Appl. Phys. Lett. 82
References
(
2003) 1069.
[
26] P.M. Tessier, O.D. Velev, A.T. Kalambur, J.F. Rabolt, A.M. Lenhoff, E.W.
Kalerm, J. Am. Chem. Soc. 122 (2000) 9554.
[
1] X. Wang, E. Graugnard, J.S. King, C. Wang, J. Summers, Nano Lett. 16
2004) 417.
(