Interface immobilization chemistry of cRGD-based peptides regulates integrin mediated cell adhesion

Article abstract of DOI:10.1002/adfm.201302411

The interaction of specific surface receptors of the integrin family with different extracellular matrix-based ligands is of utmost importance for the cellular adhesion process. A ligand consists of an integrin-binding group, here cyclic RGDfX, a spacer molecule that lifts the integrin-binding group from the surface and a surface anchoring group. c(-RGDfX-) peptides are bound to gold nanoparticle structured surfaces via polyproline, polyethylene glycol or aminohexanoic acid containing spacers of different lengths. Although keeping the integrin-binding c(-RGDfX-) peptides constant for all compounds, changes of the ligand's spacer chemistry and length reveal significant differences in cell adhesion activation and focal adhesion formation. Polyproline-based peptides demonstrate improved cell adhesion kinetics and focal adhesion formation compared with common aminohexanoic acid or polyethylene glycol spacers. Binding activity can additionally be improved by applying ligands with two head groups, inducing a multimeric effect. This study gives insights into spacer-based differences in integrin-driven cell adhesion processes and remarkably highlights the polyproline-based spacers as suitable ligand-presenting templates for surface functionalization. Self-organized spatial positioning of cRGD patches on glass via a gold nanopattern as a biomimetic approach to engineer cellular environments. Regulation of integrin-mediated cellular responses is achieved by tuning the length and chemical nature of the cRGD-presenting molecule. Fibroblasts exhibit higher affinity towards surfaces coated with cRGD containing a polyproline spacer compared with alkane- and polyethylene glycol-based spacers.

Full text of DOI:10.1002/adfm.201302411

www.afm-journal.de
www.MaterialsViews.com
Interface Immobilization Chemistry of cRGD-based
Peptides Regulates Integrin Mediated Cell Adhesion
Diego Pallarola, Alexander Bochen, Heike Boehm, Florian Rechenmacher,
Tariq R. Sobahi, Joachim P. Spatz,* and Horst Kessler*
subfamily use the amino acid sequence
Arg-Gly-Asp (RGD) as a minimal essen-
The interaction of specific surface receptors of the integrin family with dif-
ferent extracellular matrix-based ligands is of utmost importance for the
cellular adhesion process. A ligand consists of an integrin-binding group,
here cyclic RGDfX, a spacer molecule that lifts the integrin-binding group
from the surface and a surface anchoring group. c(-RGDfX-) peptides are
bound to gold nanoparticle structured surfaces via polyproline, polyeth-
ylene glycol or aminohexanoic acid containing spacers of different lengths.
Although keeping the integrin-binding c(-RGDfX-) peptides constant for all
compounds, changes of the ligand´s spacer chemistry and length reveal
significant differences in cell adhesion activation and focal adhesion forma-
tion. Polyproline-based peptides demonstrate improved cell adhesion kinetics
and focal adhesion formation compared with common aminohexanoic acid
or polyethylene glycol spacers. Binding activity can additionally be improved
by applying ligands with two head groups, inducing a multimeric effect. This
study gives insights into spacer-based differences in integrin-driven cell adhe-
sion processes and remarkably highlights the polyproline-based spacers as
suitable ligand-presenting templates for surface functionalization.
[4]
tial binding motif. Several proteins of the
ECM contain this tripeptidic motif, vitron-
ectin (Vn) being one of the most prominent
[
2a,5]
ones.
The integrin subtype αvβ3, which
primarily binds to Vn, plays a pivotal role
for initial cell adhesion. As cell adhesion
[6]
is crucial in several physiological processes
and important in the development of dis-
eases like thrombosis (blood coagulation),
osteoporosis (insufficient bone matrix
remodeling), and cancer (angiogenesis and
vascularization), this class of proteins has
[2b,7]
attracted much attention.
Starting from the linear RGD sequence,
our group has applied several techniques
to restrict the conformational space such
[8]
as cyclization, incorporation of a d-amino
acid[9] and N-methylation,[10] leading to the
development of the anti-angiogenic drug
c(-RGDf(N-Me)Val-), also known as Cilengit
[10a,10d]
ide.
Cilengitide is currently in clinical
phase II for treatment of several cancers. Additionally, targeting
of integrins by means of cRGD-based compounds has promoted
tremendous advances in the biomaterials field and its use for
biomedical applications has increased dramatically in the last
1
. Introduction
Cell adhesion is a fundamental process for multicellular organ-
isms, whereas integrins are one of the most important protein
families mediating this event.[1] These transmembrane spanning
glycoproteins consist of an α- and β-subunit and mediate cell
adhesion by connecting the cytoskeleton to proteins of the extra-
cellular matrix (ECM). So far 24 different heterodimeric inte-
[7d]
decade. Examples for applications include the use of cRGD pep-
[2]
[11]
tides for the development of integrin αvβ3-targeted radiotracers
[12]
to image metastatic tumors, as coatings for titanium implants
[13]
or organic materials to enhance bone healing, and for surface-
[14]
grins, which can be classified into four subfamilies, have been
modification of liposomes for site selective vascular delivery.
identified.[
2,3]
The members of the RGD recognizing integrin
In all these cases, the successful development of the scaffolds for
Dr. D. Pallarola, Dr. H. Boehm, Prof. J. P. Spatz
Department of New Materials and Biosystems
Max Planck Institute for intelligent Systems
Heisenbergstr. 3, 70569 Stuttgart, Germany
E-mail: spatz@is.mpg.de
Dr. D. Pallarola, Dr. H. Boehm, Prof. J. P. Spatz
Department of Biophysical Chemistry
University of Heidelberg
Dr. H. Boehm
CSF Biomaterials and Cellular Biophysics
Max Planck Institute for Intelligent Systems
Heisenbergstr. 3, 70569, Stuttgart, Germany
Prof. T. R. Sobahi, Prof. H. Kessler
Chemistry Department
Faculty of Science
King Abdulaziz University
6
9120, Heidelberg, Germany
P.O. Box 80203, Jeddah 21589, Saudi Arabia
Dr. A. Bochen, Dr. F. Rechenmacher, Prof. H. Kessler
Institute for Advanced Study and Center for Integrated Protein Science
Department Chemie
Technische Universität München
Lichtenbergstr. 4, 85747, Garching, Germany
E-mail: kessler@tum.de
This is an open access article under the terms of the Creative Commons
Attribution-NonCommercial-NoDerivs License, which permits use
and distribution in any medium, provided the original work is properly
cited, the use is non-commercial and no modifications or adaptations
are made.
DOI: 10.1002/adfm.201302411
Adv. Funct. Mater. 2014, 24, 943–956
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
wileyonlinelibrary.com 943

www.afm-journal.de
www.MaterialsViews.com
integrin adhesion relied on understanding the regulatory interac-
tions between cells and the coating components. Hence, optimi-
zation is of utmost importance for many applications.
Synthetic ligands used for integrin attachment to surfaces
are modular in structure and contain three typical elements: an
integrin-binding head group, a spacer component of variable
length and flexibility, and an attachment point for anchorage
allows the precise positioning of gold nanoparticles (AuNPs) in
a quasi hexagonal pattern with a tunable horizontal interparticle
[19]
distance. Functionalization of the AuNPs with a cyclic adhe-
sive peptide, such as c(-RGDfK-), has allowed a number of inves-
tigations on integrin-mediated cell adhesion under a wide variety
[20]
of specific geometrical arrays. In these studies, it was shown
that an interparticle distance of less than 70 nm is sufficient to
allow for stable cell adhesion, which is characterized by the devel-
(
e.g., a thiol group for binding to gold). The non N-methylated
[8]
[20a]
stem peptide c(-RGDfV-) constitutes a commonly used head
group. Regarding its sequence, it was shown that the 5th posi-
tion (valine) in this sequence can be substituted by any other
amino acid without affecting the activity of the peptide. As
a consequence, many studies used head groups consisting of
c(-RGDfK-), c(-RGDfE-), or a corresponding derivative to the
opment of mature focal adhesion (FA) points.
It is well known that polyproline forms an extended helix of
[21]
type II (PPII) in aqueous media (see e.g., another study and
references cited therein). Within this helix, three proline resi-
dues construct a full turn of the helix and the fourth residue
(i+3) is precisely above the first. Three prolines elongate the helix
by about 9.3 Å. This helical feature of the polyproline sequence
[15]
side chain of lysine or glutamic acid in conjunction with ali-
phatic, or polyethylene glycol (PEG)-based spacers.[
13a,16]
Unfor-
has been widely used as ruler for ligand presentation.
[22]
tunately, the introduction of side chain modifications reduced
the binding affinity of the ligands to integrins. To retain binding
Here, we systematically compare the influence of different
spacer systems on the binding affinity of a c(-RGDfX-)-con-
taining ligand to its primary target, integrin αvβ3. The ligands
were modified with three kinds of spacers: aminohexanoic
acid (Ahx), PEG-based spacers, and polyproline sequences, the
former two being examples of flexible spacers, the latter an
example of a more rigid spacer. In addition, we investigated
the effect of dimerization of the polyproline-based spacers
(Figure 1) on the affinity to integrin αvβ3. All synthesized pep-
tides were tested in vitro in a competitive ELISA assay using
affinity, polyvalent ligands possessing two or more binding
motifs were designed.[
11c,17]
However, those multivalent peptides
are bigger in size and the positive effect of multivalency is par-
tially compensated.[ A distinctive feature of aliphatic and PEG
spacers is their high flexibility. The preferred conformation in
17a]
[18]
PEG is a gauche arrangement and not the fully extended trans.
Hence, it is impossible to precisely control their length by means
of design and only average length can be estimated. Spacer flex-
ibility may prevent optimal exposure of integrin ligands.
To study cell-ECM adhesion interactions, it is necessary to first
reduce the complexity of the research question to a well-defined
model system. Diblock-copolymer micelle nanolithography
[
23]
the natural ligand, Vn, and the soluble integrin αvβ3. These
assays showed that cRGD bearing polyproline-based spacers
displayed significantly higher integrin αvβ3 binding affinity
than those bearing flexible spacers. To address the effect of the
Figure 1. Molecular structure of the peptides studied in this work. 1–5) Ligand peptide comprised of a cRGD headgroup, an alkane (1–2) or PEG (3–5)
type spacer and a thiol anchor for surface attachment. 6–10) Ligand peptide consisting of the cRGD headgroup ligated to a polyproline spacer using
click chemistry. The lysine linker on the opposite end is acetylated at the Nα position for the attachment of monovalent compounds (6–8) or used
as a branching unit for the synthesis of a peptide head-to-head dimer (9–10). Spacers linked to each other through the Nα or Nε of the lysine linker
possess a thiol anchor for surface attachment (gold-SH bond).
9
44 wileyonlinelibrary.com
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
Adv. Funct. Mater. 2014, 24, 943–956

www.afm-journal.de
www.MaterialsViews.com
t
Figure 2. Modification of c(-R(Pbf)GD(O Bu)fE-) (13) for application in click chemistry reactions. a) H , Pd/C, DMA, 12 h; b) 2-azidoethylamine,
2
HATU, DMF, 1 h.
different spacer systems on cell adhesion behavior, rat embryo
fibroblasts (REF52) were plated on surfaces nanostructured
with gold nanoparticles of 8 nm diameter with an interpar-
ticle distance of 68 nm and functionalized with the respec-
tive c(-RGDfX-)-spacer derivatives. Immunohistochemical and
cell dynamic studies revealed that the nature and length of
the ligand-presenting molecule have a profound influence on
cell adhesion behavior. Cells attached to substrates function-
alized with polyproline-containing peptides exhibited higher
spreading rates and FA expression in comparison to those
functionalized with analogous aliphatic or PEG-based peptides.
We believe that the results presented in this study will reveal
useful insights in the field of ligand-oriented drug design and
cell-adhesive surfaces.
2-bromoethylamine hydrochloride (1.0 equiv.) and sodium
azide (3.0 equiv.).
[26]
Ahx and PEG-based spacer systems were synthesized using
the same peptide coupling methodology as described for the
synthesis of the linear RGD peptide (see above). The spacer
was functionalized by trityl protected 3-mercaptopropionic acid
(MPA) as a thiol anchor before being cleaved from the resin
by hexafluorisopropanol (HFIP) (20%/DCM). Each spacer
t
(1.0 equiv.) was reacted with c(-R(Pbf)GD(O Bu)fK-) (1.0 equiv.)
using HATU (1.0 equiv.) and DIEA (4.0 equiv.). Synthesis of the
polyproline-based spacers followed a different Fmoc-based syn-
thesis strategy: The TCP resin was loaded with Fmoc-Lys(Alloc)-
OH, Fmoc was removed, the unprotected Nα was acetylated by
acetic acid anhydride, and the allyloxycarbonyl protecting group
(
Alloc) was removed by a mixture of tetrakis-triphenylphosphin-
palladium(0) (0.25 equiv.) and triphenylsilane (10.0 equiv.) in
anhydrous DCM. For the synthesis of the polyproline sequence
Fmoc-proline-OH (3.0 equiv.), (1-cyano-2-ethoxy-2-oxoethylide-
naminooxy) dimethylamino-morpholino-carbenium hexafluoro-
2
. Chemical Synthesis
The required building blocks—the cRGD peptide and the
spacer unit—were synthesized separately. All peptides were
assembled using solid phase synthesis and Fmoc strategy.
[
27]
phosphate (COMU, 3.0 equiv.), ethyl(hydroxyimino)cyanoac-
[
24]
[28]
etate (Oxyma, 3.0 equiv.) and DIEA (6.0 equiv.) were used.
The linear, side chain-protected sequence of the RGD peptide
was synthesized on tritylchloride polystyrene (TCP) resin as
support, starting with glycine to prevent racemization during
the later cyclization step. The following permanent, orthogonal,
side chain protections were used: 2,2,4,6,7-pentamethyldihyd-
robenzofuran-5-sulfonyl (Pbf) for Arg, tert-butyl for Asp, benzyl
The Fmoc group was removed by standard conditions and, as
a last step, 5-hexynoic acid (3.0 equiv.) was coupled by COMU
(3.0 equiv.) and DIEA (6.0 equiv.) to the polyproline sequence.
To obtain divalent peptides the first polyproline sequence was
synthesized on the unprotected Lys-Nα instead of the acetyla-
tion step. The spacer was cleaved from the solid support by
(
(
1
Bz) for Glu, and benzyloxycarbonyl (Cbz) for Lys. Amino acids
3.0 equiv.) were coupled stepwise with 2-(1H-benzotriazole-
-yl)-1,1,3,3-tetramethyluronium tetrafluoroborate (TBTU, 3.0
HFIP (20%/DCM), ligated to 13 using CuSO (1.0 equiv.) and
4
t
sodium ascorbate (2.0 equiv.) per cyclic peptide in a BuOH/
[
25,29]
H O (1:1–2:1) mixture and purified by RP-HPLC.
2
The
equiv.) and N-hydroxy-benzotriazole (HOBt, 3.0 equiv.) as cou-
pling reagents and N,N-diisopropylamine (DIEA, 6.0 equiv.) as
a base. Cleavage from the resin by retention of the side-chain
protecting groups occurred using a mixture of DCM/acetic
acid/trifluorethanol (7:2:1). Cyclization of the linear peptide was
achieved by 2-(7-aza-1H-benzotriazole-1-yl)-1,1,3,3-tetrameth-
yluronium hexafluorophosphate (HATU, 2.0 equiv.), HOBT
C-terminal carboxylic acid on the lysine was functionalized
by 2-(tritylthio)ethylamine 12 (1.0 equiv.), HATU (1.0 equiv.),
1-hydroxy-7-aza-benzotriazole (HOAt, 1.0 equiv.), and DIEA
(4.0 equiv.), as a last step. Finally, all remaining protecting
groups were removed by trifluoracetic acid/H O/triisopropyl-
2
silane (95:2.5:2.5) treatment and the peptides were purified by
RP-HPLC (Figure 3).
(2.0 equiv.), and DIEA (10 equiv.) using high dilution levels
to favor the intramolecular reactions over intermolecular reac-
tions. Finally, hydrogenation of the Bz or Cbz group resulted in
the partially protected cyclic peptide. The unprotected glutamic
acid of the cyclic peptide was modified by 2-azidoethylamine
3
. Results and Discussion
(4.0 equiv., 11), HATU (1.05 equiv.), and DIEA (5.0 equiv.)
3.1. In Vitro Inhibition of Integrin Binding
resulting in the azido-modified cyclic peptide 13, suitable for
azide-alkyne 1,3-dipolar cycloaddition (click chemistry) reac-
tions (Figure 2).[ 2-azidoethylamine was synthesized from
A comprehensive list of all the monovalent and divalent cRGD
ligands and their reference numbers can be found in Table 1.
25]
Adv. Funct. Mater. 2014, 24, 943–956
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
wileyonlinelibrary.com 945

www.afm-journal.de
www.MaterialsViews.com
Figure 3. Synthesis of a monomeric proline spacer compound and its ligation with 13. a) i: 20% piperidine/NMP (Fmoc dpr.); ii: Ac O, DIEA, NMP; iii:
2
Pd(PPh ) , phenylsilane, anhydrous DCM, 1 h; iv: Fmoc-Pro-OH, COMU, Oxyma, DIEA, NMP, 1 h; (Pro coupling). b) i: repeats of Fmoc dpr (a i) and
3
4
Pro coupling (a iv), 5-hexynoic acid, COMU, DIEA, NMP, 1h, ii 20% HFIP/DCM; c) 11, CuSO , NaAsc., tert.-BuOH/H O, 70 °C, 3 h; d) Trt-cystamine,
4
2
HATU, HOAt, DIEA, DMF, 1 h; e) TFA/TIPS/H O, 1 h.
2
Table 1. Inhibition of integrin binding to vitronectin (αvβ3) by mono-
valent and divalent cRGD pentapeptides using different kinds of spacer
systems
To evaluate possible differences in the integrin-binding affinity
between the ligands containing aliphatic, PEG, monomeric or
dimeric polyproline spacers, all synthesized compounds were
[
23a,23b]
tested in a competitive ELISA.
Immobilized natural ligand
IC50a)αvβ3
nm]
Reference number and peptide description
vitronectin (Vn) and soluble integrin αvβ3 were used. Highly
[
Me
[10a,10d]
active cyclic pentapeptide Cilengitide, c(-RGDf V-)
was
1
2
3
4
5
6
7
8
9
1
c(-RGDfK-)[MPA]
3.4 (± 0.4)
13.6 (± 2.4)
8.4 (± 2.4)
13.6 (± 3.6)
16.5 (± 7.5)
2.4 (± 0.8)
2.5 (± 0.4)
2.1 (± 0.2)
0.52 (± 0.04)
0.17 (± 0.03)
2.6 (± 0.6)
0.54 (± 0.15)
used as an internal control. The unmodified stem compound
c(-RGDfK-)[Ahx-MPA]
[15]
c(-RGDfK-), which has been described in literature,
was
c(-RGDfK-)[Trigas-MPA]
included for further comparison.
c(-RGDfK-)[Hegas-MPA]
The integrin αvβ3 binding affinity of monovalent com-
pounds (1–5) with aliphatic (1: 3.4 nm, 2: 13.6 nm) or PEG
spacers of different length (3–5: 8.4–16.5 nm) was less than the
binding affinity of the unmodified peptide c(-RGDfK-) (2.6 nm)
c(-RGDfK-)[HegasHegas-MPA]
Ac-K-[c(-RGDfE-)[HexPPP]]-cta
Ac-K-[c(-RGDfE-)[HexPPPPPP]]-cta
Ac-K-[c(-RGDfE-)[HexPPPPPPPPP]]-cta
[c(-RGDfE-)[HexPPP]]2K-cta
0 [c(-RGDfE-)[HexPPPPPP]]2K-cta
(
Table 1). For the ligands with aliphatic or PEG spacers the
binding affinity additionally decreased with increasing spacer
length. Remarkably, this was not the case for monovalent
compounds containing polyproline spacers (6–8). The affinity
of the monovalent polyproline containing ligand towards inte-
grin αvβ3 (2.1–2.5 nm) was comparable to that of unmodi-
fied c(-RGDfK-) (2.6 nm). Although the shortest polyproline
sequence we used consists of only three consecutive proline
residues (6), the effect of polyproline as the ligand spacer was
pronounced. In contrast to aliphatic or PEG spacers, a length-
controlled affinity decrease of polyproline containing ligands
was not evidenced when increasing the polyproline spacer
length to six (7) or nine (8) proline residues (Figure 4).
c(-RGDfK-)b)
Cilengitidec)
a)
IC50 values were derived from a competitive ELISA using immobilized Vn and
[23a,23b] b)
soluble integrin αvβ3;
This cyclic pentapeptide was used as precursor for
the design of 1–5;[ c)Cilengitide, c(-RGDfMeV-)
15]
[10d]
was used as an internal refer-
ence compound for the integrin αvβ3 ELISA assay. Ahx: 6-amino-hexanoic acid,
cta: cystamin, Hegas: heptaethylene glycol amino acid (PEG thiol acid), Hex:
4
-(1-(2-aminoethyl)-1H-1,2,3-triazol-4-yl)butanoic acid, MPA: mercaptopropionic
acid, Trigas: triethylene glycol (PEG).
9
46 wileyonlinelibrary.com
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
Adv. Funct. Mater. 2014, 24, 943–956

www.afm-journal.de
www.MaterialsViews.com
unmodified cyclic peptide, and a higher activity was obtained
[
17f ]
only for octamers or even larger compounds.
even describes a step-by-step decrease in binding affinity from
mono- to di- to tetra-valent compounds.
One report
[
33]
And, one study
describes a reduction in the binding affinity with increasing
[
17e]
spacer length.
In this work, we systematically investigated the impact of
three different spacer types on the binding affinity of a cRGD
ligand. We report the direct comparison of Ahx, PEG and poly-
proline spacers and found superior binding affinity of ligands
with spacers containing a polyproline sequence over those with
Ahx and PEG spacers.
3
.2. Cell Adhesion Experiments
3
.2.1. Immunohistochemical Analysis of Cell Spreading
and FA Assembly
Figure 4. Spacer lengths (Å) and types are correlated to the integrin-
binding affinity (IC ). 1–2 ( ), 3–5 ( ), 6–8 ( ), 9–10 ( ᭹). Spacer
REF52 cells were plated on cRGD-nanopatterns to assess the
influence of the different cRGD coatings on cell adhesion
behavior. Our approach to engineer cellular environments is
based on self-organizing spatial positioning of patches of cRGD
attached to glass via a gold nanopattern. The glass substrates
area, which is not covered by gold, is passivated against protein
adsorption and cell interactions by a covalently immobilized
PEG layer. Such substrates offer the highest possible spatial res-
olution with respect to the position of cRGD patches made of a
few single cRGD molecules. On such biointerfaces, the regula-
tion of cellular responses is based on a biologically inert back-
ground that does not initiate any cell activation, which is then
patterned with cRGD in well-defined nanoscopic geometries.
This approach is very powerful, since it enables the testing of
cellular responses to individual cRGD nanopatches and their
spatial ordering which is very important for comparing the
impact of different ligands for integrin activation as reported
here. In detail, the glass coverslips were patterned with AuNPs
of 8 nm diameter arranged in a quasi-hexagonal structure with
5
0
length was calculated for the all-trans configuration of aliphatic ( ) and
PEG ( ) spacers, between the Cα Lys(K) and the thiol; Monomeric pro-
line ( ) spacer length was determined between the Cα Glu(E) and the
thiol; Dimeric proline (᭹) spacer length was determined between the Cα
Glu(E) via Cα Lys(K) to Cα Glu(E).
The limited binding affinity observed for aliphatic and PEG-
based spacer-containing ligands can be ascribed to their high
flexibility, which results in coiling and unwanted shielding of
the pharmacophoric groups. As these spacer types are seldom
found in a fully extended conformation (all-trans conforma-
tion), the spacer prevents maximum interaction with the inte-
grin-binding site. Obviously, the incorporation of only three
consecutive proline residues stiffens the spacer sufficiently to
prevent a coiling-related negative effect on the binding affinity
of the peptide.
We explored the applicability of the polyproline spacer
system for divalent ligands possessing two cRGD binding
motifs (9 and 10). The positive effect of including an extended
polyproline sequence inside the ligand on the binding affinity
towards integrin αvβ3 was confirmed for divalent ligands.
The extended nature of the polyproline-based dimeric con-
struct displayed, at a fixed distance, an additional epitope
able to promote rebinding and therefore increased the rela-
tive potency per ligand.[ Regardless of the spacer length,
dimerization gave compounds with sub-nanomolar activities
[
19]
an average interparticle distance of 68 nm as reported before.
Then, glass area between the AuNPs was passivated with PEG-
[
34]
terminated siloxane. Subsequently, AuNPs were functional-
ized with a cRGD-based thiol ligand as given in Table 1.
In the following, the impact of the three chemically dif-
ferent spacers, the influence of PEG and polyproline spacer
length, as well as the effect of divalent polyproline spacer sys-
tems on the assembly of FAs and actin fibers were examined.
REF52 cells were plated on the individual substrates for 4 h,
then fixed and stained for paxillin, nuclei and actin. Every sub-
strate induced cell adhesion and spreading, indicating suc-
cessful integrin-ligand interactions with all the different com-
pounds (Figure 5). However, distinctive differences of adhesion
based cell responses are evident between the compounds. In a
direct comparison of compounds that differ only with respect to
spacer length, an increase in FA density with the spacer length
is observed (see Figure S1, Supporting Information). The same
observation was made regarding the cell area (see Figure S2,
Supporting Information). On all compound-coated surfaces
cRGD-mediated adhesion induced a dense meshwork of periph-
eral actin filaments with only a few stress fibers appearing.
30]
(
9: 0.52 nm, 10: 0.17 nm), which is a factor of 4–14 increase
to the activities measured for monovalent polyproline peptides
6–8: 2.1–2.5 nm). Notably, these affinities were in the range of
(
Me
[10d]
the binding affinity of Cilengitide c(-RGDf V-),
standard” for targeting integrin αvβ3.
the “gold
Multivalent compounds first appeared in literature quite
some time ago[
pounds using Ahx and PEG-based spacers is known.
30,31]
and the synthesis of multivalent com-
[17a,17b]
However, previously described spacers had several disadvan-
[17d,32]
tages. In some cases the applied spacers were very short.
In another case the addition of tetrameric compounds was
necessary to achieve an activity comparable to that of the
Adv. Funct. Mater. 2014, 24, 943–956
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
wileyonlinelibrary.com 947

www.afm-journal.de
www.MaterialsViews.com
3
.2.2. Dynamic Analysis of Cell Adhesion and Spreading
As a next step, we examined the kinetics of cell adhesion and
spreading on the differently functionalized substrates. Here,
a homemade multiwell array with a PEG passivated and Au-
nanostructured glass base plate (Figure 6) as in the case of
immunohistochemical analysis (Figure 5) was employed. The
different wells were functionalized with the different ligands
and cell adhesion was monitored in parallel in each of these
wells. These studies were conducted with the rat embryo fibro-
blast cell line REF52, which stably expresses yellow fluores-
[
36]
cent protein (YFP)-paxillin, an adhesion associated protein.
Therefore, dynamic monitoring of cell adhesion and FA forma-
tion could be achieved by fluorescent microscopy utilizing the
automated microscopy system Hermes Wiscan.
In Figure 7, fluorescence optical microscopy visualization of
YFP-paxillin REF52 shows cell spreading and FA maturation over
time. Paxillin clusters are shown as bright, mainly elongated spots
at the periphery of spreading cells. We have selected and presented
in Figure 7 micrographs sequences of cell adhesion corresponding
to AuNP-structured surfaces functionalized with compounds 2, 4,
6, and 9. These sequences adequately illustrate the overall influence
of the different kinds of spacers on FA and cell adhesion dynamics.
A quantitative evaluation of the spreading rate was measured
by following the projected cell area at different time points up
to 540 min (Figure 8). Isotropic growth, following a power-law
behavior, was observed for all compounds, similar to previous
[37]
findings. However, striking differences were observed with
respect to maximum projected cell area and the time required
to reach it. As summarized in Table 2, peptides bearing short
hydrophobic spacers—compounds 1 and 2—caused the slowest
cellular spreading rate. Both PEG- and polyproline-containing
(monovalent and divalent) cRGD peptides induced faster cell-
spreading rates than those with short hydrophobic spacers.
Noteworthy, the cellular spreading rate increased with the spacer
length for all compounds. Remarkably, contrary to the surface
immobilized cell assays, soluble monovalent compounds with
alkanethiol and PEG-thiol spacers (1–5) showed a reduced
affinity to integrin with increasing spacer length in the inhibi-
tion assays (Table 1). This reflects the spacer's ability to fold and
thereby shield the active moiety, which must be reduced by the
interchain van der Waals’ interactions in the case of oriented
[38]
surface immobilization in comparison to the soluble one. It
also highlights the role of ligand immobilization for cell adhe-
sion activation. Surfaces functionalized with the hydrophilic
polyproline spacers (6–10) showed faster cell spreading char-
acteristics, which increased with extending spacer length and
dimerization. Lag time for spreading initiation was also influ-
enced by the nature and length of the spacers. Cells plated on
nanopatterns coated with compounds 6–10 (polyproline spacers)
and compound 5 (longest PEG-spacer) showed the initiation
of cell flattening and spreading between 15 and 18 min after
plating. In contrast, compounds 3 and 4 (shorter PEG spacers)
and compounds 1 and 2 (short hydrophobic spacers) induced
cell flattening around 25 and 40 min after plating, respectively.
Figure 5. Fluorescent micrographs of representative REF52 cells on
nanopatterns functionalized with the different monovalent and divalent
cRGD peptides (1–10). Cells were fixed and stained for paxillin (red),
nuclei (blue) and actin (green) after an incubation period of 4 h.
There is a seemingly trend that the longer (i.e., compare 3 vs
5
, 6 vs 8, and 9 vs 10) and more hydrophilic the spacer is (i.e.,
compare 2 vs 3, and 5 vs 8), the more stress fibers structures
were formed inside the cells cytoplasm. Cells did not adhere in
control experiments performed on passivated surfaces lacking
cRGD functionalization. Therefore, cell spreading and FA for-
mation is determined by the presentation of the cRGD motif on
the nanopatterned surface, which have strong affinity to inte-
grin αvβ3.[
3
.2.3. Dynamic Analysis of FA Assembly
To further characterize cell adhesion on the nanopatterns
coated with the different integrin-binding molecules we studied
35]
9
48 wileyonlinelibrary.com
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
Adv. Funct. Mater. 2014, 24, 943–956

www.afm-journal.de
www.MaterialsViews.com
Figure 6. Schematic drawing showing the steps involved in the assembly of the multiwell array employed for cell adhesion dynamics studies. AuNP
nanopatterns, as prepared by diblock-copolymer micelle nanolithography on 26 × 76 mm N°1, are glued to a 16-well chamber. 1) Each well is function-
alized with a different cRGD-based thiol ligand as given in Table 1. 2) YFP-paxillin REF52 cells are plated on each well and visualized with fluorescence
microscopy. The magnified area represents the interaction between the integrin extracellular domains and the cRGD-coated AuNP.
the dynamics of FA development. No significant differences
were revealed in terms of FA size and morphology for the dif-
ferent cRGD-coated surfaces. Therefore, measurements of the
total area of paxillin patches provided a direct quantification of
the density of FAs. Figure 9 shows the development of the total
area of FAs normalized by the projected area of the cell as a
function of time. Similar to the observation on spreading ini-
tiation, FA development was significantly affected by the type
and length of the spacer. As a general rule, functionalization
with shorter spacers led to a more delayed development of FAs.
This was evidenced by the occurrence of paxillin patches in the
cells in Figure 7. Cells on surfaces functionalized with short
spacer compounds (1–3) exhibited well-defined FAs 2.5 h after
seeding. On compound 1, the development of FAs was even
slower and only 50% of cells exhibited robust paxillin patches
only 60% of the cells displayed mature FAs 60–80 min after
seeding. Differences in the total area of mature FAs after a
given amount of time cannot be explained only by a difference
in how quickly spreading initiation commences. After sub-
tracting the lag time for spreading initiation from the values
in Figure 9, the calculated growth rate of FAs on surfaces func-
tionalized with compounds 4–10 was higher than on surfaces
functionalized with compounds containing alkane- and short
PEG-based spacers. This can be interpreted as an increment
of the nucleation rate on substrates with sufficiently exposed
ligands (vide infra). The nucleation of FAs can be described as
the aggregation of two or more molecules of talin connecting
[39]
two αβ-integrin dimers through actin filaments. Subsequent
recruitment of additional components, for example, paxillin
and vinculin, leads to the maturation of these initial clusters
[40]
2.5 h after seeding. In contrast, nanopatterns functionalized
into FAs. As the activity of the integrin epitope promotes the
formation of stable integrin-cRGD complexes, it is also likely
that high affinity interactions between receptors and binding
sites increase the nucleation frequency. Similar observations
with compounds containing longer spacers (4–10) induced FA
development 60–80 min after cells were plated. Compounds 4–
1
0 caused similar effects, with one exception. On compound 4,
Figure 7. Fluorescence visualization of YFP-paxillin REF52 cell adhesion dynamics on gold nanopatterned surfaces functionalized with compound 2
c(-RGDfK-)[Ahx-MPA]), 4 (c(-RGDfK-)[Hegas-MPA]), 6 (Ac-K-[c(-RGDfE-)[HexPPP]]-cta), and 9 ([c(-RGDfE-)[HexPPP]] K-cta).
(
2
Adv. Funct. Mater. 2014, 24, 943–956
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
wileyonlinelibrary.com 949

www.afm-journal.de
www.MaterialsViews.com
Figure 8. Cell spreading dynamics of YFP-paxillin as observed by Figure 7. Data are presented as mean ± standard deviation. The solid lines in each
plot represent the fitting of the time-resolved spreading area data to a one-parameter exp4onential association function.
were reported for 3T3 Swiss fibroblasts plated on thin gold
that is, cRGD thiol in the present case. Several studies con-
ducted on recognition-driven assembly of proteins showed that
the binding affinity of a protein is decreased in high-densely
packed assemblies of the target molecule compared to those
substrates coated with a mixed SAM of cRGDfK-terminated
[
35b]
alkanethiol and tri(ethylene glycol)-terminated alkanethiol.
There, the authors showed that cells adhering to high-affinity
substrates had almost twice as many FAs than cells plated on
surfaces with low-affinity coatings.
[
41]
proteins situated on a surface with lower molecule density.
Similarly, Houseman and Mrksich observed that the activity
of β-1,4-galactosyltransferase was optimum when the reactant
surface molecule (N-acetylglucosamine) constituted 70% of a
Interestingly, the shape of the curves obtained for shorter
(1–3) and longer (4–10) spacers (see Figure 9), showed notice-
[
42]
able differences. Whereas on compounds 4–10 cells displayed
a sustained increase in the total area of FAs followed by a slow
decline towards an asymptotic value, cells plated on surfaces
coated with compounds 1–3 exhibited a nearly constant value
mixed self-assembled monolayer (SAM).
This observation
is attributed to steric hindrance between neighboring binding
sites when the assembly is highly packed. Therefore, we meas-
ured the total amount of chemisorbed thiol species on planar
gold substrates by electrochemically reductive desorption in
(meaning that FA area grew by the same proportion as cell area
[43]
increased). The kinetics of FA assembly is obviously influenced
by the quality of ligand presentation. In contrast, the density and
distribution of paxillin-based plaques at longer time values (>6 h
after seeding) depends on the inherent activity of the pharmaco-
phoric molecule, which in this work remained invariant.
Further analysis of the maximum values of the curves of FA
expression dynamics presented in Figure 9 revealed that cells
adhering to nanopatterns coated with polyproline-containing
compounds induced the highest FA expression (see Figure S3
in the Supporting Information). These results highlight the
ability of polyproline-based spacers, more so than alkane and
PEG spacers, to efficiently present the active moiety to the cell,
thus triggering strong integrin-ligand interactions.
alkaline solution,
and calculated the expected number of
molecules per particle by assuming an available AuNP sur-
2
face of 50 nm , which accounts to approximately 25% of the
total area of a 8 nm-diameter AuNP, while effects of curvature
[
44]
are neglected. The results are summarized in Table 2. The
hydrophobic alkane (1–2) and more hydrophilic PEG spacers
(3–5) showed approximately comparative numbers of mol-
ecules per gold dot, ranging from 67 to 107. While a longer
alkane spacer increased the number of molecules per gold
dot from 67 to 98 (1–2), the number of molecules per dot was
approximately the same for all PEG spacers of different length
(3–5) and in the range of the longer alkane spacer. Contrary,
the number of monomeric polyproline-based peptides (6–8)
decreased with an increase in the number of proline residues
from 54 to 38 molecules per AuNP, respectively. Similar obser-
vations were reported in a recent study on oligoproline-based
3
.2.4. Evaluation of the Ligand Density on AuNP
[
45]
Activation of integrins triggered by cell-ligand interactions is
likely to be affected by the local density of the active ligand,
peptides. Due to the hydrophilic nature of the polyproline
spacer this is attributed to a reduction in the attractive
9
50 wileyonlinelibrary.com
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
Adv. Funct. Mater. 2014, 24, 943–956

www.afm-journal.de
www.MaterialsViews.com
Table 2. Influence of the spacer length and the ligand density on the spreading dynamics of YFP-paxillin REF52 cells plated on cRGD-functionalized
nanopatterns.
Peptide
Spacer lengtha)
Å]
Densityb)
[molecules/50 nm ]
Time constantc)
[s]
2
[
1
2
3
4
5
6
7
8
9
1 1
21
22
33
56
39
49
58
39
49
67 (± 5)
0.21 (± 0.11)
0.32 (± 0.05)
0.44 (± 0.09)
0.53 (± 0.14)
1.04 (± 0.14)
0.50 (± 0.08)
0.81 (± 0.05)
1.18 (± 0.12)
0.79 (± 0.06)
1.09 (± 0.08)
98 (± 14)
92 (± 6)
107 (± 11)
96 (± 10)
54 (± 6)
44 (± 6)
38 (± 5)
18 (± 4)
1
0
15 (± 2)
a)
Spacer length was calculated for the all-trans configuration of aliphatic and PEG spacers between Cα Lys(K) and thiol, and for proline spacers between Cα Glu(E) and
b)
thiol; The surface density of the different thiol-based peptides was estimated by electrochemical reductive desorption conducted on gold planar surfaces. Values are pre-
sented as the amount of molecules per 50 nm (50 nm accounts to ∼25% of the area of a AuNP with a 8 nm diameter), which is approximately equivalent to the available
area on AuNPs attached to PEG-passivated surfaces;
2
2
[
54] c)
Time constant values were obtained by fitting the spreading data for each peptide functionalized substrate to a
one-parameter exponential growth function.
interactions between chains as the spacer length increases. This
was also evidenced by a shift in the desorption potential to less
negative values (see Figure S4a in the Supporting Information)
and is probably caused by a lack of lateral hydrophobic inter-
actions among the polyproline helix, which leads to less com-
pact films. This greatly differs to observations on alkanethiol
monolayers on gold, where increasing chain length leads to
a denser packing of the monolayer.[38] It can be expected that
the extended nature of the polyproline spacers and the reduced
coverage density caused by the longer spacer length lead to a
greater accessibility of individual cRGD moieties by integrins.
These results are in full agreement with the observed cell adhe-
sion behavior on nanopatterns functionalized with monovalent
polyproline peptides of variable length. Longer spacers caused
Figure 9. FA expression dynamics followed by fluorescence visualization of YFP-paxillin. Data are presented as mean ± standard deviation. For com-
parison, FA development is visualized in Figure 7.
Adv. Funct. Mater. 2014, 24, 943–956
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
wileyonlinelibrary.com 951

www.afm-journal.de
www.MaterialsViews.com
a quicker activation of cell adhesion, which can be interpreted
of the binding motif. Because the induction of conformational
[
46]
[49]
as a better accessibility of the ligands by the integrins. QCM
measurements performed on mixed SAMs similarly suggest
ligand density to be important. These data show that soluble
integrin αvβ3 binding is indeed enhanced when the density
of the polyproline-based cRGD peptide is diluted with a non-
changes in the integrin receptors
regulate the exposure
of the binding site, the ligand-binding domain of the acti-
vated integrin heterodimer needs to be located at a defined
minimum distance. Due to the relative shortness of the cyto-
plasmic tails of integrins, the ability to convey conformational
changes between the integrin tail and the ligand-binding head
functionalized Pro -SH spacer (see Figure S5, Supporting
3
[
50]
Information).
group very much depends on the distance between the two.
Similar properties apply for the dimeric polyproline-con-
taining compounds (9–10). The packing density of the mono-
layers decreases with an increasing number of proline residues
With respect to the data presented in Figure 8, this reports
that a successful binding process can only take place if the
spacer length can span the distance between the substrate to
which it is bound and the integrin-binding domain. To quan-
titatively assess the impact of the spacer length for each com-
pound series, we plotted the time constant values for each fitted
curve against the maximum spacer length (Figure 10). Peptides
containing hydrophobic (1–2) and PEG (3–5) spacers were com-
parable in their cell spreading dynamics (hydrophobic spacers:
(see Figure S4b in the Supporting Information). It should be
noted that for the same spacer length (calculated between the
Cα Glu(E) and the thiol) the coverage density of the dimeric
compounds was less than half of that of the monomeric coun-
terparts (i.e., compare 6 vs 9 in Table 2). Therefore, the number
of presented cRGD moieties is also slightly lower in the case
of the dimeric polyproline assembly. This appears reason-
able considering that two polyproline helices shared the same
anchoring point within the dimers, resulting in even greater
space constraints. The higher spreading rates observed for
cells plated on nanopatterns coated with polyproline dimers
can be ascribed to a better accessibility by integrins due to a
less packing density and a more suitable orientation of adjacent
cRGD molecules towards integrin binding considering the on/
off-binding dynamics.
0.011 ± 0.016 Å−1 s ; PEG spacers: 0.018 ± 0.007 Å s ). Pep-
tides containing polyproline spacers, in contrast, speeded up
cell spreading. Compared to each PEG-containing peptide of
equal length, the equivalent polyproline-containing peptides
enhanced cell spreading by a factor of about two. Interestingly,
monomeric and dimeric polyproline compounds presented
−1
−1 −1
−
1
−1
similar slope values (monomers 6–8: 0.036 ± 0.011 Å s ;
dimers 9–10: 0.032 ± 0.014 Å−1 s ), but with higher spreading
rates at equal spacer elongation in the case of the dimeric com-
pounds. These results suggest identical contribution of the
spacer length to the spreading rate, but improved ligand avail-
ability at the nanometric scale, that is, higher integrin-binding
affinity, with polyproline dimers.
−1
In the case of hydrophobic spacers (1–2) the thiolate packing
density increased with spacer length due to enhanced attrac-
tive interactions between neighboring chains. For compound
2
, density coverage reached values two times larger than the
maximum value for compounds of the polyproline series (for
details see Supporting Information, Figure S4c). The moderate
performance of these monolayers for promoting cell adhesion
and spreading can be attributed to the short length and high
flexibility of the spacers. Additionally, the close proximity of the
bulky cRGD molecule and the thiol group is prone to introduce
distortions in the organic layer. This effect was stronger for
compound 1 than for compound 2.
PEG-based monolayers displayed a similar trend to that
observed for polyproline SAMs. The reductive potential was
shifted in a positive direction with increasing PEG chain length
(see Figure S4d, Supporting Information), indicating a decrease
in the attractive interactions between adjacent chains. Although
PEG-based peptides exhibited the highest coverage of all the com-
pounds tested (Table 2), the presence of all PEG chains in a fully
extended helical brush configuration, as is commonly observed
for SAMs of long chain alkanethiols, is highly unlikely.[ Under
well-solvated conditions PEG chains adopt a highly hydrated coil
configuration due to the absence of the necessary driving force to
extend their length upon surface immobilization.[ It is there-
fore reasonable to expect some degree of coiling of molecular
chains on PEG-based SAMs, which ultimately decreases the
effective number of spacer molecules that are able to present the
cRGD binding sequence on a fully extended connector ligand.
47]
48]
Figure 10. Contribution of spacer length to the spreading rate of YFP-
paxillin REF52. Data are presented as mean ± standard deviation. Time
constant (k) and spacer length (L) values were extracted from Table 2.
Slope values (Δk/ΔL) were calculated by a linear fitting for the different
−
1
−1
spacer series: alkane 1–2 ( ): 0.011 ± 0.016 Å s ; polyethylene glycol
−
1
−1
3
0
–5 ( ): 0.018 ± 0.007 Å s ; polyproline monomer 6–8 ( ): 0.036 ±
−1 −1 −1 −1
.011 Å s ; polyproline dimer 9–10 (᭹): 0.032 ± 0.014 Å s . The dif-
3
.2.5. Influence of the Spacer Length on Cell Spreading Rate
ference between the slope obtained for polyproline spacers (monomer
or dimer) and that obtained for polyethylene glycol spacers is significant
with 90% level of confidence. No significant (P<0.1) difference was found
by comparing the slopes of the alkane and polyethylene glycol series.
Integrin binding to the respective ligands depends on inte-
grin activation and is also highly sensitive to the accessibility
9
52 wileyonlinelibrary.com
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
Adv. Funct. Mater. 2014, 24, 943–956

www.afm-journal.de
www.MaterialsViews.com
Basic 10F equipment, with a P-900 pump system, a reversed-phase
YMC-ODS-A C18 column (12 nm pore size, 5 μm particle size, 250 mm ×
4.6 mm), and UV detection (UV-900, 220 and 254 nm). The system was
4
. Conclusion
In this work we have demonstrated the advantages of using a
polyproline sequence (rather than an Ahx or a PEG-containing
spacer) to connect cRGD peptides to artificial substrates used
to study integrin-mediated cell adhesion. In two types of dif-
ferent experimental investigations, isolated receptor ELISA
assays and cell adhesion studies on AuNP-structured surfaces,
the compounds connected by the polyproline spacer resulted in
ligands with higher integrin-binding affinity and improved cell
adhesion properties than ligands using spacers containing Ahx
or PEG. In detail, ELISA assays showed that functionalization
of the ligand using an Ahx spacer-containing peptide drastically
decreased the ligand binding affinity. Similarly, the applica-
tion of a PEG spacer of comparable length influenced ligand
binding, however at a lesser extent than the alkyl derivative. In
addition, increasing the length of the PEG spacer led to less
ligand affinity. In contrast, the use of polyproline sequences
as cRGD-presenting spacer did not alter the ligand binding
affinity towards the targeted integrin αvβ3, independently
of its length. Divalent ligands using the polyproline spacer
achieved 4 to 14-fold higher ligand binding. The results of
ELISA experiments and cell adhesion experiments were com-
parable for polyproline-based peptides. The quality of cell adhe-
sion is the lowest if a short alkyl chain or Ahx spacer is used
and increases with an increasing length of the PEG spacer.
More stable cell adhesion is achieved on surfaces coated with
monovalent ligand containing a polyproline spacer. Cell adhe-
sion becomes even more mature if the proline spacer is made
longer, and even more so when dimeric ligand peptides with
polyproline spacers are used. Cell spreading and FA assembly
dynamics were highly influenced by the type and length of
the spacer. Again, polyproline spacers promoted stronger cell
spreading and FA assembly compared to the other spacer types.
These results emphasize the advantages of using a polypro-
line sequence for the backbone of ligand-presenting molecules
instead of the commonly applied Ahx and PEG spacers. Com-
pared with alkane- and PEG-based spacers, the more extended
characteristic of the polyproline spacers and the low-density
assemblies they yield lead to highly accessible cRGD moie-
ties, thus enhancing cRGD-integrin interactions according to
constructive cell spreading and adhesion maturation. These
findings may stimulate future development of adhesive sur-
faces with a higher affinity and could present the possibility to
control ligand display more precisely and constructively, thus
enabling the study of cell adhesion processes in more defined
surroundings.
run at a flow rate of 1.0 mL/min over 30 min using H O (0.1% TFA) and
2
MeCN (0.1% TFA) as solvents. Semi-preparative HPLC was performed
using a Waters Breeze System, including a 1525 Pump, a UV-Detector
2
487 Dual (220 and 254 nm), and the Driver Software Breeze vers. 3.20.
As column material we used: YMC-ODS-A C18 (12 nm pore size, 5 μm
particle size, 250 mm × 20 mm), YMC-ODS-AQ C18 (12 nm pore size,
5 μm particle size, 250 mm × 20 mm) or YMCbasic (proprietary pore
size, 5 μm particle size, 250 mm × 20 mm). HPLC-ESI-MS analyses
were performed on a Hewlett Packard Series HP 1100 with a Finnigan
LCQ mass spectrometer using a YMC-Hydrosphere C18 column (12 nm
pore size, 3 μm particle size, 125 mm × 2.1 mm) or a YMC-Octyl C8
column (20 nm pore size, 5 μm particle size, 250 mm × 2.1 mm). The
system uses H O (0.1% formic acid) and MeCN (0.1% formic acid) as
2
eluents. Standard peptide coupling techniques were employed. Yields
were not optimized. All tested compounds exhibited ≥ 95% purity, as
determined by RP-HPLC-(MS). Peptide synthesis was carried out using
TCP resin following standard Fmoc-strategy.[ A detailed description of
the synthetic procedures is presented in the Supplementary Information
section.
24]
Integrin Binding Assay (Vn/αvβ3): The inhibiting activity of the
integrin ligands was determined in a solid-phase binding assay using
coated extracellular matrix protein and soluble integrin. Binding of
the integrin was detected by a specific antibody in an enzyme-linked
immune sorbent assay (ELISA). The assay was based on a previously
reported method with several modifications.[
51]
Flat-bottom 96-well
ELISA plates (BRAND, Wertheim, Germany) were coated overnight at
°C with 100 μL/well of 1.0 μg/mL vitronectin (Millipore, Schwalbach/
Ts., Germany) in carbonate-buffer (15 mm Na CO , 35 mm NaHCO ,
4
2
3
3
pH 9.6). Each well was then washed with PBST buffer (137 mm NaCl,
2.7 mm KCl, 10 mm Na HPO , 2 mm KH PO , 0.01% Tween 20, pH 7.4,
2
4
2
4
3
× 200 μL) and blocked for 1 h at room temperature with 150 μL/well of
TSB-buffer (20 mm Tris-HCl, 150 mm NaCl, 1 mm CaCl , 1 mm MgCl ,
2
2
1
mm MnCl , pH 7.5, 1% BSA). After being washed three times
2
with PBST, equal volumes of internal standard (Cilengitide) or test
compounds were mixed with 2.0 μg/mL human integrin αvβ3 (Millipore,
Schwalbach/Ts., Germany). The final dilution in TSB buffer was 1.0 μg/
mL for integrin αvβ3 and ranged between 0.00013 and 10 μm for the
inhibitors. The solutions (100 μL/well) were incubated for 1 h at room
temperature. The plate was washed three times with PBST buffer and
1
00 μL/well of 2.0 μg/mL primary antibody mouse anti-human CD51/61
(BD Biosciences, Heidelberg, Germany) was added to the plate. After
incubation for 1 h at room temperature, the plate was washed three
times with PBST. 100 μL/well of 1.0 μg/mL of secondary peroxidase-
labeled antibody (anti-mouse IgG-POD, Sigma-Aldrich, Taufkirchen,
Germany) was added to the plate and incubated for 1 h at room
temperature. After washing the plate three times with PBST, 50 μL/well of
SeramunBlau fast (Seramun Diagnostic GmbH, Heidesee, Germany) was
added and incubated for 5 min at room temperature. The reaction was
stopped with 50 μL/well of 3 m H SO and absorbance was measured at
2
4
4
50 nm with a plate reader (POLARstar Galaxy, BMG Labtechnologies).
Each compound concentration was tested in duplicate and the resulting
inhibition curves were analyzed using OriginPro 7.5G software. In these
measurements, the inflection point represents the IC50 value. Each plate
contained Cilengitide as internal standard.
5
. Experimental Section
Biofunctionalized Nanopatterns: AuNP quasi-hexagonal patterns
were prepared on glass coverslips by means of diblock-copolymer
micelle nanolithography as previously described.[ Briefly, substrates
were dip-coated with a solution of polystyrene(1056)-block-poly[2-
Chemical Synthesis: All technical solvents were distilled prior to use.
19]
Dry solvents were purchased from Sigma-Aldrich or Fluka. Protected
Fmoc-amino acids and coupling reagents were purchased from Sigma-
Aldrich (Taufkirchen, Germany) Novabiochem (Schwalbach, Germany),
Iris Biotech GmbH (Marktredwitz, Germany), PolyPeptide Laboratories
vinylpyridine(HAuCl )0.25](495) (Polymer Source Inc., Canada) diblock
4
copolymer micelles in o-xylene at a constant pulling rate of 1 mm/s
(Strasbourg, France), and Medalchemy (Alicante, Spain). TCP-resin was
and subsequently subjected to H :Ar 1:10 plasma treatment (350 W,
2
purchased from PepChem (Tübingen, Germany). All other chemicals
and organic solvents were purchased from commercial suppliers at the
highest purity available and used without further purification. Analytical
HPLC was performed using the Amersham Pharmacia Biotech Äkta
0.4 mbar, 90 min). Then, substrates were treated thermally in an oven
at 500 °C for 48 h. This procedure provided nanopatterns consisting
of 8 nm high AuNPs (as measured by atomic force microscopy)
with an interparticle distance between adjacent AuNPs of 68 ± 9 nm
Adv. Funct. Mater. 2014, 24, 943–956
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
wileyonlinelibrary.com 953

www.afm-journal.de
www.MaterialsViews.com
(
determined by scanning electron microscopy). Subsequently, the area
Germany) and were subjected to reductive electrodesorption of thiols.
The charge density of the cathodic peaks was taken as an indication of
between Au nanoparticles was passivated with mPEG-triethoxysilane
[
53]
(2000) to prevent non-specific adhesion according to a procedure
the surface coverage by the different cRGD-thiol derivatives.
detailed description, please refer to the Supporting Information.
For a
[
34]
described elsewhere.
For immunohistochemical experiments, gold
nanopatterns on 20 × 20 mm N°1 glass coverslips (Carl Roth, Germany)
were employed, whereas cell dynamics experiments were performed
on 26 × 76 mm N°1 glass coverslips (Thermo Scientific, Germany).
In the latter case, a 16-well Lab-Tek chamber was glued onto the Supporting Information
nanopatterned surface with a biocompatible adhesive, named Twinsil
Supporting Information is available from the Wiley Online Library or
from the author.
(Picodent, Germany). This configuration allowed high throughput
screening of the entire set of c(-RGDfX-)-based molecules using a single
surface. Each well, in the case of the multiple-well array, or each 20 mm
×
20 mm surface was functionalized with the corresponding integrin-
binding molecule at a concentration of 25 μm in MilliQ water for 2 h
at room temperature. Physisorbed material was removed by exhaustive
rinsing with MilliQ water and PBS. Cell experiments were carried out
immediately after this step.
Acknowledgements
D.P. and A.B. contributed equally to this work. The authors gratefully
acknowledge financial support from the International Graduate School
of Science and Engineering (IGSSE), from the TUM Graduate School
(TUM GS) and the Max Planck Society. Part of the research leading
to these results received funding from the European Union Seventh
Framework Programme (FP7/2007–2013) under grant agreement
n° NMP4-LA-2009–229289 NanoII and n° NMP3-SL-2009–229294
NanoCARD. We gratefully thank for the technical and financial support
from King Abdulaziz University KAU (grant No. HiCi/25–3–1432). The
group is part of the excellence cluster CellNetworks at the University
of Heidelberg. J.P.S. is the Weston Visiting Professor at the Weizmann
Institute of Science.
Cell Culture: REF52 (rat embryo fibroblast) wild type (WT) cells and
REF52 cells expressing yellow fluorescent protein (YFP)-paxillin fusion
[
36]
proteins were a kind gift of Benjamin Geiger (Weizmann Institute of
Science, Rehovot, Israel). REF52 WT cells and YFP-paxillin REF52 cells
were cultured in DMEM medium supplemented with 10% FBS and 1%
L-glutamin (Invitrogen, Germany) at 37 °C and 5% CO . For adhesion
2
experiments, cells in culture were rinsed with PBS at 37 °C and adherent
cells removed from the culture surface by treatment with trypsin-EDTA
0
.25% for 5 min at 37 °C. Cells were plated at a density of 150 cells/
2
mm on the functionalized surfaces in DMEM containing 1% FBS,
% L-glutamin and 100 units/mL penicillin-streptomycin (Invitrogen,
1
Received: July 17, 2013
Revised: August 28, 2013
Published online: October 16, 2013
Germany), followed by incubation at 37 °C and 5% CO2.
Immunofluorescence Staining: After 4 h on the nanopatterned surfaces,
REF52 WT cells were washed with PBS at 37 °C and fixed with 2.5%
paraformaldehyde in PBS for 10 min. Cells were then permeabilized
with 0.1% Triton X-100 in PBS, blocked with 5% goat serum (Invitrogen,
Germany) in PBS for 1 h at room temperature, and incubated with a
1
:100 dilution of rabbit anti-paxillin (Abcam, USA) for 1 h at room
[
[
[
[
1] B. Geiger, J. P. Spatz, A. D. Bershadsky, Nat. Rev. Mol. Cell Biol.
009, 10, 21.
2] a) R. O. Hynes, Cell 1992, 69, 11; b) B. H. Luo, C. V. Carman,
T. A. Springer, Annu. Rev. Immunol. 2007, 25, 619.
temperature. Then, cells were labeled with a 1:100 dilution of anti-rabbit
Alexa 594-conjugated secondary antibody (Invitrogen, Germany) in 5%
goat serum in PBS for 1 h at room temperature. Filamentous actin and
nuclei were labeled with Alexa 488-conjugated phalloidin and DAPI
2
3] M. Barczyk, S. Carracedo, D. Gullberg, Cell Tissue Res. 2010, 339,
(Invitrogen, Germany), respectively. Cells were examined with a 63/1.25
2
69.
Oil Ph3 Antiflex Plan-Neofluar objective (Carl Zeiss, Germany) using an
Axiovert 200 fluorescent microscope (Carl Zeiss, Germany) equipped
with
Hamamatsu Photonics, Germany). Image processing was done using
the Axiovision Image viewer (Carl Zeiss, Germany).
4] a) E. Ruoslahti, M. Pierschbacher, Science 1987, 238, 491;
b) E. Ruoslahti, Annu. Rev. Cell Dev. Biol. 1996, 12, 697;
c) J. D. Humphries, A. Byron, M. J. Humphries, J. Cell Sci. 2006,
a Hamamatsu digital CCD camera (model C10600–10B-H;
1
19, 3901.
Cell Dynamics Experiments: YFP-paxillin expressing REF52 cells were
plated on the multiple-well array and immediately mounted on the
thermostatized stage of the microscope at 37 °C under 5% CO2 and
controlled humidity. Immunofluorescence visualization of cells was
performed with a Hermes WiScan (Idea Bio-Medical, Israel) system
equipped with an Andor digital CCD camera (model iXon 897; Andor
Technology, USA), a fast AutoFocus device[52] and an automated stage.
Cells were examined with a U Plan FL N 60×/0.9 objective (Olympus,
Japan) at different time intervals starting 10 min after plating. Sets of 76
images per well were taken, with an average acquisition time of 0.6 s per
image. Image processing and analysis were performed using the image
analysis platform WiSoft (Idea Bio-Medical, Israel). Briefly, images were
first subjected to a low-pass filtration to smooth out non-uniformities
in intensity. After that, images were subjected to a high-pass filtration
to flatten the image and enhance edges. Finally, the resulting processed
images were used for optimizing parameters (threshold, maximum and
minimum size of the patches, etc.) for the segmentation module, which
defines objects based on their intensity and morphological attributes.
Each time point of the corresponding c(-RGDfX-)-based compound was
based on the evaluation of 50 cells from at least two different multiple-
well arrays.
[5] a) E. Zamir, B. Geiger, J. Cell Sci. 2001, 114, 3577; b) R. O. Hynes,
Science 2009, 326, 1216.
[6] a) S. P. Massia, J. A. Hubbell, J. Cell Biol. 1991, 114, 1089;
b) K. Hodivala-Dilke, Curr. Opin. Cell Biol. 2008, 20, 514.
[7] a) A. Meyer, J. Auernheimer, A. Modlinger, H. Kessler, Curr. Pharma-
ceut. Design 2006, 12, 2723; b) Z. F. Liu, F. Wang, X. Y. Chen, Drug
Dev. Res. 2008, 69, 329; c) D. Cox, M. Brennan, N. Moran, Nat. Rev.
Drug Discovery 2010, 9, 804; d) S. L. Goodman, M. Picard, Trends
Pharmacol. Sci. 2012, 33, 405.
[
8] M. Aumailley, M. Gurrath, G. Müller, J. Calvete, R. Timpl, H. Kessler,
FEBS Lett. 1991, 291, 50.
[
9] R. Haubner, D. Finsinger, H. Kessler, Angew. Chem. Int. Edit. 1997,
3
6, 1375.
[
10] a) M. A. Dechantsreiter, E. Planker, B. Mathä, E. Lohof,
G. Hölzemann, A. Jonczyk, S. L. Goodman, H. Kessler, J. Med.
Chem. 1999, 42, 3033; b) J. Chatterjee, C. Gilon, A. Hoffman,
H. Kessler, Acc. Chem. Res. 2008, 41, 1331; c) J. Chatterjee,
F. Rechenmacher, H. Kessler, Angew. Chem. Int. Ed. 2013, 52, 254;
d) C. Mas-Moruno, F. Rechenmacher, H. Kessler, Anticancer Agents
Med. Chem. 2010, 10, 753.
Electrochemical Experiments: SAMs of the different thiol-based cRGD
peptides were prepared on flamed annealed gold substrates (Arrandees,
[11] a) G. B. Sivolapenko, D. Skarlos, D. Pectasides, E. Stathopoulou,
A. Milonakis, G. Sirmalis, A. Stuttle, N. S. Courtenay-Luck,
9
54 wileyonlinelibrary.com
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
Adv. Funct. Mater. 2014, 24, 943–956

www.afm-journal.de
www.MaterialsViews.com
K. Konstantinides, A. A. Epenetos, Eur. J. Nucl. Med. 1998, 25, 1383;
b) W. B. Cai, D. W. Shin, K. Chen, O. Gheysens, Q. Z. Cao, S. X. Wang,
S. S. Gambhir, X. Y. Chen, Nano Lett. 2006, 6, 669; c) M. Schottelius,
B. Laufer, H. Kessler, H.-J. Wester, Acc. Chem. Res. 2009, 42, 969;
d) S. Maschauer, J. Einsiedel, R. Haubner, C. Hocke, M. Ocker,
H. Huebner, T. Kuwert, P. Gmeiner, O. Prante, Angew. Chem. Int. Ed.
b) Y. A. Fillon, J. P. Anderson, J. Chmielewski, J. Am. Chem. Soc.
2005, 127, 11798; c) G. Sanclimens, L. Crespo, E. Giralt, F. Albericio,
M. Royo, J. Org. Chem. 2005, 70, 6274; d) S. Sato, Y. Kwon,
S. Kamisuki, N. Srivastava, Q. A. Mao, Y. Kawazoe, M. Uesugi,
J. Am. Chem. Soc. 2007, 129, 873; e) M. Kuemin, S. Schweizer,
C. Ochsenfeld, H. Wennemers, J. Am. Chem. Soc. 2009, 131, 15474.
[23] a) A. O. Frank, E. Otto, C. Mas-Moruno, H. B. Schiller, L. Marinelli,
S. Cosconati, A. Bochen, D. Vossmeyer, G. Zahn, R. Stragies,
E. Novellino, H. Kessler, Angew. Chem. Int. Ed. 2010, 49, 9278;
b) F. Rechenmacher, S. Neubauer, J. Polleux, C. Mas-Moruno,
M. De Simone, E. A. Cavalcanti-Adam, J. P. Spatz, R. Faessler,
H. Kessler, Angew. Chem. Int. Ed. 2013, 52, 1572; c) S. Neubauer,
F. Rechenmacher, A. J. Beer, F. Curnis, K. Pohle, C. D´Alessandria,
H.-J. Wester, U. Reuning, A. Corti, M. Schwaiger, H. Kessler, Angew.
Chem. Int. Ed. 2013, DOI: 10.1002/anie.201306376.
2
010, 49, 976; e) R. Haubner, A. J. Beer, H. Wang, X. Chen, Eur. J.
Nucl. Med. Mol. Imaging 2010, 37, S86; f) Y. Zhou, S. Chakraborty,
S. Liu, Theranostics 2011, 1, 58; g) J. Notni, K. Pohle, H.-J. Wester,
Nucl. Med. Biol. 2013, 40, 33.
[
12] a) R. Haubner, W. A. Weber, A. J. Beer, E. Vabuliene, D. Reim,
M. Sarbia, K. F. Becker, M. Goebel, R. Hein, H. J. Wester, H. Kessler,
M. Schwaiger, PLoS Med. 2005, 2, 244; b) A. J. Beer, M. Schwaiger,
in Molecular Imaging: Methods and Protocols, Vol. 680 (Ed: K. Shah),
2
011, 183.
[
13] a)M. Kantlehner, D. Finsinger, J. Meyer, P. Schaffner, A. Jonczyk,
[24] G. B. Fields, R. L. Noble, Int. J. Pept. Protein Res. 1990, 35, 161.
[25] M. Meldal, C. W. Tornoe, Chem. Rev. 2008, 108, 2952.
[26] S. Angelos, Y. W. Yang, K. Patel, J. F. Stoddart, J. I. Zink, Angew.
Chem. Int. Ed. 2008, 47, 2222.
B. Diefenbach, B. Nies, H. Kessler, Angew. Chem. Int. Ed. 1999, 38,
5
60; b) B. Jeschke, J. Meyer, A. Jonczyk, H. Kessler, P. Adamietz,
N. M. Meenen, M. Kantlehner, C. Goepfert, B. Nies, Biomaterials
2
2
002, 23, 3455; c) U. Hersel, C. Dahmen, H. Kessler, Biomaterials
003, 24, 4385; d) S. Rammelt, T. Illert, S. Bierbaum, D. Scharnweber,
[27] a) A. El-Faham, F. Albericio, J. Org. Chem. 2008, 73, 2731;
b) A. El-Faham, R. S. Funosas, R. Prohens, F. Albericio, Chem.-Eur.
J. 2009, 15, 9404.
[28] R. Subiros-Funosas, R. Prohens, R. Barbas, A. El-Faham,
F. Albericio, Chem.-Eur. J. 2009, 15, 9394.
H. Zwipp, W. Schneiders, Biomaterials 2006, 27, 5561.
14] R. Srinivasan, R. E. Marchant, A. Sen Gupta, J. Biomed. Mater. Res.
A 2010, 93A, 1004.
[
[
[
15] R. Haubner, R. Gratias, B. Diefenbach, S. L. Goodman, A. Jonczyk,
H. Kessler, J. Am. Chem. Soc. 1996, 118, 7461.
[29] V. V. Rostovtsev, L. G. Green, V. V. Fokin, K. B. Sharpless, Angew.
Chem. Int. Ed. 2002, 41, 2596.
[30] M. Mammen, S. K. Choi, G. M. Whitesides, Angew. Chem. Int. Ed.
1998, 37, 2755.
16] a) J. Auernheimer, D. Zukowski, C. Dahmen, M. Kantlehner,
A. Enderle, S. L. Goodman, H. Kessler, ChemBioChem 2005, 6, 2034;
b) E. Lieb, M. Hacker, J. Tessmar, L. A. Kunz-Schughart, J. Fiedler,
C. Dahmen, U. Hersel, H. Kessler, M. B. Schulz, A. Göpferich,
Biomaterials 2005, 26, 2333; c) S. Kalinina, H. Gliemann,
M. Lopez-Garcia, A. Petershans, J. Auernheimer, T. Schimmel,
M. Bruns, A. Schambony, H. Kessler, D. Wedlich, Biomaterials 2008,
[31] a) H. Kessler, M. Schudok, A. Haupt, Peptides 1988: Procedings
of the 20th European Peptide Symposium, Tübingen, 1988, (Eds:
G. Jung, E. Bayer), Walter de Gruyter, Berlin, New York 1989, 664;
b) L. L. Kiessling, J. E. Gestwicki, L. E. Strong, Curr. Opin. Chem.
Biol. 2000, 4, 696; c) J. E. Gestwicki, C. W. Cairo, L. E. Strong,
K. A. Oetjen, L. L. Kiessling, J. Am. Chem. Soc. 2002, 124, 14922.
[32] Y. Wu, X. Z. Zhang, Z. M. Xiong, Z. Cheng, D. R. Fisher, S. Liu,
S. S. Gambhir, X. Y. Chen, J. Nucl. Med. 2005, 46, 1707.
[33] C. B. Yim, I. Dijkgraaf, R. Merkx, C. Versluis, A. Eek, G. E. Mulder,
D. T. S. Rijkers, O. C. Boerman, R. M. J. Liskamp, J. Med. Chem.
2010, 53, 3944.
[34] J. Blümmel, N. Perschmann, D. Aydin, J. Drinjakovic, T. Surrey,
M. López-García, H. Kessler, J. P. Spatz, Biomaterials 2007, 28, 4739.
[35] a) B. T. Houseman, M. Mrksich, Biomaterials 2001, 22, 943;
b) M. Kato, M. Mrksich, Biochemistry 2004, 43, 2699.
[36] E. Zamir, B. Z. Katz, S. Aota, K. M. Yamada, B. Geiger, Z. Kam, J.
Cell Sci. 1999, 112, 1655.
2
5
9, 3004; d) K. A. Kilian, M. Mrksich, Angew. Chem. Int. Ed. 2012,
1, 4891.
[
17] a) G. Thumshirn, U. Hersel, S. L. Goodman, H. Kessler, Chem.-
Eur. J. 2003, 9, 2717; b) D. Lössner, H. Kessler, G. Thumshirn,
C. Dahmen, B. Wiltschi, M. Tanaka, W. Knoll, E. K. Sinner,
U. Reuning, Anal. Chem. 2006, 78, 4524; c) L. L. Kiessling,
J. E. Gestwicki, L. E. Strong, Angew. Chem. Int. Ed. 2006, 45, 2348;
d) Z. B. Li, W. B. Cai, Q. Z. Cao, K. Chen, Z. H. Wu, L. N. He,
X. Y. Chen, J. Nucl. Med. 2007, 48, 1162; e) H. Kubas,
M. Schafer, U. Bauder-Wust, M. Eder, D. Oltmanns, U. Haberkorn,
W. Mier, M. Eisenhut, Nucl. Med. Biol. 2010, 37, 885; f) C. Wangler,
S. Maschauer, O. Prante, M. Schafer, R. Schirrmacher, P. Bartenstein,
M. Eisenhut, B. Wangler, Chembiochem 2010, 11, 2168.
[37] F. Chang, C. A. Lemmon, D. Park, L. H. Romer, Mol. Biol. Cell 2007,
18, 253.
[38] C. Vericat, M. E. Vela, G. Benitez, P. Carro, R. C. Salvarezza, Chem.
Soc. Rev. 2010, 39, 1805.
[
18] M. L. Alessi, A. I. Norman, S. E. Knowlton, D. L. Ho, S. C. Greer,
Macromolecules 2005, 38, 9333.
[
[
19] R. Glass, M. Möller, J. P. Spatz, Nanotechnology 2003, 14, 1153.
20] a) M. Arnold, E. A. Cavalcanti-Adam, R. Glass, J. Blümmel, W. Eck,
M. Kantlehner, H. Kessler, J. P. Spatz, ChemPhysChem 2004, 5, 383;
b) M. Arnold, V. C. Hirschfeld-Warneken, T. Lohmüller, P. Heil,
J. Blummel, E. A. Cavalcanti-Adam, M. López-García, P. Walther,
H. Kessler, B. Geiger, J. P. Spatz, Nano Lett. 2008, 8, 2063;
c) M. Arnold, M. Schwieder, J. Blümmel, E. A. Cavalcanti-Adam,
M. López-García, H. Kessler, B. Geiger, J. P. Spatz, Soft Matter 2009,
[39] S. J. Smith, R. McCann, Biochemistry 2007, 46, 10886.
[40] R. Zaidel-Bar, C. Ballestrem, Z. Kam, B. Geiger, J. Cell Sci. 2003, 116,
4605.
[41] a) J. Spinke, M. Liley, H. J. Guder, L. Angermaier, W. Knoll, Langmuir
1993, 9, 1821; b) V. H. Pérez-Luna, M. J. O’Brien, K. A. Opperman,
P. D. Hampton, G. P. López, L. A. Klumb, P. S. Stayton, J. Am.
Chem. Soc. 1999, 121, 6469; c) K. Gorska, K. T. Huang, O. Chaloin,
N. Winssinger, Angew. Chem. Int. Ed. 2009, 48, 7695; d) Y. Sato,
K. Yoshioka, T. Murakami, S. Yoshimoto, O. Niwa, Langmuir 2012,
28, 1846.
5
, 72; d) J. H. Huang, S. V. Grater, F. Corbellinl, S. Rinck, E. Bock,
R. Kemkemer, H. Kessler, J. D. Ding, J. P. Spatz, Nano Lett. 2009,
, 1111; e) I. Platzman, C. A. Muth, C. Lee-Thedieck, D. Pallarola,
R. Atanasova, I. Louban, E. Altrock, J. P. Spatz, RSC Adv. 2013, 3,
3293.
9
[42] B. T. Houseman, M. Mrksich, Angew. Chem. Int. Ed. 1999, 38,
782.
1
[
[
21] M. Moradi, V. Babin, C. Roland, T. A. Darden, C. Sagui, Proc. Natl.
Acad. Sci. U. S. A. 2009, 106, 20746.
22] a) L. Crespo, G. Sanclimens, B. Montaner, R. Pérez-Tomás, M. Royo,
M. Pons, F. Albericio, E. Giralt, J. Am. Chem. Soc. 2002, 124, 8876;
[43] C. A. Widrig, C. Chung, M. D. Porter, J. Electroanal. Chem. 1991,
310, 335.
[44] M. J. Hostetler, J. E. Wingate, C. J. Zhong, J. E. Harris, R. W. Vachet,
M. R. Clark, J. D. Londono, S. J. Green, J. J. Stokes, G. D. Wignall,
Adv. Funct. Mater. 2014, 24, 943–956
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
wileyonlinelibrary.com 955

www.afm-journal.de
www.MaterialsViews.com
G. L. Glish, M. D. Porter, N. D. Evans, R. W. Murray, Langmuir 1998,
[50] a) E. A. Evans, D. A. Calderwood, Science 2007, 316, 1148;
b) I. D. Campbell, M. J. Humphries, Cold Spring Harbor Perspectives
in Biology 2011, 3.
[51] a) C. Mas-Moruno, J. G. Beck, L. Doedens, A. O. Frank, L. Marinelli,
S. Cosconati, E. Novellino, H. Kessler, Angew. Chem. Int. Ed.
2011, 50, 9496; b) J. Chatterjee, O. Ovadia, G. Zahn, L. Marinelli,
A. Hoffman, C. Gilon, H. Kessler, J. Med. Chem. 2007, 50, 5878.
[52] Y. Liron, Y. Paran, N. G. Zatorsky, B. Geiger, Z. Kam, J. Microsc.
2006, 221, 145.
14, 17.
[
[
45] J. Juhaniewicz, S. Sek, Bioelectrochemistry 2012, 87, 21.
46] a) J. C. Love, L. A. Estroff, J. K. Kriebel, R. G. Nuzzo,
G. M. Whitesides, Chem. Rev. 2005, 105, 1103; b) D. Samanta,
A. Sarkar, Chem. Soc. Rev. 2011, 40, 2567.
47] M. Cerruti, S. Fissolo, C. Carraro, C. Ricciardi, A. Majumdar,
R. Maboudian, Langmuir 2008, 24, 10646.
[
[
[
48] P. Kingshott, H. Thissen, H. J. Griesser, Biomaterials 2002, 23,
2
043.
[53] M. E. Vela, H. Martin, C. Vericat, G. Andreasen, A. H. Creus,
R. C. Salvarezza, J. Phys. Chem. B 2000, 104, 11878.
[54] S. Upadhyayula, T. Quinata, S. Bishop, S. Gupta, N. R. Johnson,
B. Bahmani, K. Bozhilov, J. Stubbs, P. Jreij, P. Nallagatla, V. I. Vullev,
Langmuir 2012, 28, 5059.
49] a) J. Zhu, J. Zhu, T. A. Springer, J. Cell Biol. 2013, 201, 1053;
b) M. A. Müller, J. Opfer, L. Brunie, L. A. Volkhardt, E. K. Sinner,
D. Boettiger, A. Bochen, H. Kessler, K. E. Gottschalk, U. Reuning, J.
Mol. Biol. 2013, 425, 2988.
9
56 wileyonlinelibrary.com
© 2013 The Author. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
Adv. Funct. Mater. 2014, 24, 943–956