Sonochemically-promoted preparation of silica-anchored cyclodextrin derivatives for efficient copper catalysis

Article abstract of DOI:10.3390/molecules24132490

Silica-supported metallic species have emerged as valuable green-chemistry catalysts because their high efficiency enables a wide range of applications, even at industrial scales. As a consequence, the preparation of these systems needs to be finely contr

Full text of DOI:10.3390/molecules24132490

molecules
Article
Sonochemically-Promoted Preparation of
Silica-Anchored Cyclodextrin Derivatives for Efficient
Copper Catalysis
Katia Martina 1 , Federica Calsolaro
1
, Alessio Zuliani 2 , Gloria Berlier 3
,
3
,4
1
2,5
Fernando Chávez-Rivas
, Maria Jesus Moran , Rafael Luque
1
,
and Giancarlo Cravotto *
1
Dipartimento di Scienza e Tecnologia del Farmaco, Università di Torino, Via Pietro Giuria 9, 10125 Turin, Italy
Departamento de Quimica Organica, Universidad de Cordoba, Edificio Marie-Curie (C-3), Ctra Nnal IV-A,
Km 396 Cordoba, Spain
Dipartimento di Chimica, Università di Torino, Via Pietro Giuria 7, 10125 Turin, Italy
Instituto Politécnico Nacional, ESFM, Departamento de Física, UPALM, Zacatenco,
Ciudad de México 07738, Mexico
2
3
4
5
Peoples Friendship University of Russia (RUDN University), 6 Miklukho-Maklaya str.,
1
17198 Moscow, Russia
*
Correspondence: giancarlo.cravotto@unito.it; Tel.: +39-011-670-7183
ꢀ
ꢁꢂꢀꢃꢄꢅꢆꢇ
Academic Editor: Gregory Chatel
Received: 8 June 2019; Accepted: 2 July 2019; Published: 7 July 2019
ꢀ
ꢁꢂꢃꢄꢅꢆ
Abstract: Silica-supported metallic species have emerged as valuable green-chemistry catalysts
because their high efficiency enables a wide range of applications, even at industrial scales.
As a consequence, the preparation of these systems needs to be finely controlled in order to achieve
the desired activity. The present work presents a detailed investigation of an ultrasound-promoted
synthetic protocol for the grafting of
has emerged as a fast technique for promoting efficient derivatization of a silica surface with organic
moieties at low temperature. Three different -CD silica-grafted derivatives have been obtained,
and the ability of -CD to direct and bind Cu when CD is bonded to silica has been studied. A detailed
characterization has been performed using TGA, phenolphthalein titration, FT-IR, diffuse reflectance
DR), DR UV-Vis, as well as the inductively-coupled plasma (ICP) of the -CD silica-grafted systems
β-cyclodextrin (β-CD) onto silica. Truly, ultrasound irradiation
β
β
(
β
and the relative Cu-supported catalysts. Spectroscopic characterization monitored the different
steps of the reaction, highlighting qualitative differences in the properties of amino-derivatized
precursors and final products. In order to ensure that the Cu-
robust, its applicability in Cu(II)-catalyzed alkyne azide reactions in the absence of a reducing agent
has been explored. The presence of -CD and an amino spacer has been shown to be crucial for the
reactivity of Cu(II), when supported.
β-CD silica catalyst is efficient and
β
Keywords: sonochemistry; copper-catalysis; β-cyclodextrin; silica; green chemistry; organic-inorganic
hybrid materials; infrared spectroscopy; diffuse reflectance; UV-visible
1
. Introduction
The design of novel organic-inorganic hybrid systems has achieved considerable success in several
fields, including catalysis, photochemistry, biochemistry, and optoelectronics [
studies have enriched the literature on this type of compound, and especially so in recent years [
For example, a hybrid inorganic-organic, TiS , and ammonium-cation-based superlattice has recently
1
]. Numerous innovative
2–5].
2
been described as a promising flexible thermoelectric thin film [
6]. Moreover, an innovative system,
consisting of a core of BaTiO , covered by PMMA, has been demonstrated to have tailorable dielectric
3
Molecules 2019, 24, 2490; doi:10.3390/molecules24132490
www.mdpi.com/journal/molecules

Molecules 2019, 24, 2490
2 of 18
properties [7]. The key feature of this type of system is that its characteristics arise not only from the
individual contributions of the phases, but also from the properties of the inner interface, which can
also be predominant. The unique active behavior of these hybrid systems is therefore not observed
when the single components are used alone [8].
Organic-inorganic hybrid systems can be divided into two classes according to the nature of
the organic-inorganic interface [
bonded together via weak interactions, such as van der Waals forces, hydrogen bonding, and ionic
bonds. Class II compounds are made up of stronger covalent or iono–covalent interactions [ ].
9]. Class I materials possess organic and inorganic components
9
Some organic-inorganic hybrid systems of both classes have emerged as a winning combination in the
general field of catalysis due to their enhanced heterogeneous properties. In fact, the immobilization
and stabilization of organic active sites over inorganic solids has strongly improved the recovery and
recyclability characteristics [1,10]. However, class II compounds have attracted much more interest
from the field of catalysis due to the higher stability of their hybrid systems. Indeed, class II materials
can be used under harsher reaction conditions, whereas class I systems are more sensitive and may
be irreversibly damaged. For example, mesoporous silica, such as SBA-15 and MCM-41, has been
functionalized with numerous organic ligands for several catalytic applications [10
of Class II hybrid components has led to the growth of materials in which catalytically-active
coordination-metal complexes are covalently anchored to inorganic substrates [14 18]. Due to the
–13]. The evolution
–
impractical nature of infinitely recycling the metals, research is being directed toward the utilization
of more abundant and inexpensive metals, such as iron, cobalt, copper, and nickel, in the place of
precious metals [19
years [25 29]. In fact, copper has undergone thorough investigations in its role as a homogeneous
catalyst, and remarkable results have been achieved in many reactions, including oxidations, additions,
C-C bond cleavage, and Michael addition reactions [30 34]. Therefore, the development of stable Cu
–24]. Specifically, copper catalysis has received a great deal of attention in recent
–
–
catalysts that can be used in heterogeneous conditions has recently attracted considerable interest. For
example, copper nanoparticles that are supported over silica have been studied as efficient catalysts for
the hydrogenation of alkynes [35]. Furthermore, Cu that is supported over manganese oxide octahedral
molecular sieves has been demonstrated to be an efficient catalyst for the synthesis of imidazoles [36].
The purpose of Cu organic-inorganic hybrid systems resides in the possibility of synthesizing
heterogeneous catalysts with the lowest possible metal dimensions in order to increase active surface
area. The ambitious major objective in this field is therefore that of producing atomic-scale particles.
This can be achieved via the selection of stable ligands for Cu that can be strongly anchored
over the various solid supports.
β-cyclodextrin (
β-CD, Figure 1) has been demonstrated to be
an attractive macromolecule for this purpose.
β-CD is a cyclic oligosaccharide composed of seven
linked D-glucopyranose units and that can be represented as a toroid structure with narrow and wide
openings corresponding to the primary and secondary hydroxyl groups, respectively [37]. This peculiar
structure means that
Several studies have proposed ingenious strategies for supporting Cu/
Moradi et al. recently stabilized Cu(II)/ -CD complexes over fibrous nanosilica and successfully
employed the material as a catalyst in the synthesis of oxazolidinones [41]. Xia and co-workers
prepared a magnetically-recoverable catalyst made of Cu(II)/ -CD complexes anchored over ferric
β-CD can easily encapsulate copper and numerous other compounds [38
–40].
β-CD complexes. For example,
β
β
oxide and covered by silica [42]. Shafiee et al. reported the preparation of functionalized PEGylated
mesoporous silica nanoparticle-graphene oxide as a catalyst for the synthesis of imidazoles [43].
Figure 1. General structure of β-cyclodextrin (β-CD).

Molecules 2019, 24, 2490
3 of 18
Ultrasound (US) has seen widespread use in the promotion of organic syntheses [44
heterogeneous phase reactions [46
,
45] and
,
47]. In addition, sonochemical techniques have been claimed to have
outstanding methodologies for sustainable and green synthesis [48]. Significant effort has been devoted
to organic synthesis with supported catalysts and reagents on the surfaces of inexpensive and recyclable
mineral supports, such as clay, silica, and alumina [49]. However, only a limited number of publications
have made reference to US-promoted silica derivatization. The focus is mainly on Class I derivatives
that possess organic and inorganic components. Sonication has been efficiently employed to give
silica-based nanocomposites. For example, guanidine acetic acid has been immobilized on the surface
of modified Fe O @SiO [50], and carbon nanotubes have been derivatized with tetraethoxysilane
3
4
2
using an ultrasonic sol-gel process [51]. Only a few examples have studied the preparation of Class II
derivatives, and an alkoxysilane derivate of thiacalix[4]arene has been efficiently covalently grafted
onto silica [52].
Herein, we describe a detailed investigation into the influence of US irradiation on the reaction
rate of silica derivatization to obtain CD-grafted silica. A number of routes have been explored and
compared with the aim of obtaining this class of peculiar organic-inorganic hybrid materials using a
highly-reproducible, efficient synthetic protocol. Commonly-employed silica-grafting procedures entail
long reaction times at high temperatures, and the capability of US to shorten reaction times and operate
at lower temperatures has been demonstrated. By supporting Cu(II) on the CD-grafted silica, we were
able to produce a new copper catalyst for click azido-alkyne cycloadditions. Remarkably, the click
1,3-dipolar cycloaddition was optimized without the addition of a reducing agent because of the
presence of CD. Due to the utilization of an abundant metal in Earth’s crust and the exploitation of
sonication, the so-produced material could be pointed out as a novel green and sustainable hybrid
organic-inorganic catalyst [53].
2
. Results and Discussion
2
.1. Synthesis of Copper Supported on Si-NH-CD and Si-DETA-CD
On the basis of our experience with covalently-functionalized silica [54,55], the modification of
silica surfaces via the grafting of organic compounds can lead to improve catalytic activity and may
increase sorption capacity. With the aim of obtaining different silica-support-grafted -CDs for Cu(II)
species using a short and reliable synthetic protocol, two different routes were compared. Specifically,
-CD was anchored to silica via a diethylentriamino spacer that can contribute to Cu binding strength,
and amino CD was directly grafted onto the silica surface (Scheme 1). Precipitated silica SIPERNAT 320
β
β
(
Evonik) was used as an inorganic support, with a moderate absorption capacity and BET specific surface
2
area (SSA) of 164 m /g. The sample was characterized by medium particle size, in the range of tenths to
hundredths of micrometers, formed by the agglomeration of nanosized (20–50 nm) primary particles.
3
Interparticle porosity resulted in relatively large pore volume (1.2 cm /g). Preliminarily, silica was
converted to silica chloride (Si-Cl) in the presence of thionyl chloride, as has already been described
in the literature [56
,57], and the resulting chloride ions were titrated with a silver nitrate solution in
I
I
the presence of a potassium chromate solution, used as an indicator. 6 amino-6 -deoxy-
β-CD was
then reacted to obtain the Si-NH-CD derivatives. In the second route, which gives the Si-DETA-CD
I
derivative, 6 -tosyl-
β
-CD was anchored to silica via a diethylentriamino spacer. Chlorinate silica was
I
then reacted with diethylenetriamine (DETA), and a nucleophilic substitution with 6 -tosyl-
β-CD was
performed (Scheme 1).

Molecules 2019, 24, 2490
4 of 18
H
N
OH
OH
SOCl2
reflux, 16 h
OH
Cl
H2N
NH2
OH
H
N
SiO2
SiO2
SiO2
N
H
NH2
Solvent, time
See Table 1
Si-Cl
Si-DETA
6I-Amino β−CD
6I-Tosyl β−CD
Solvent, time
See Table 1
Solvent, time
See Table 1
OH
OH VII
OH
H
SiO2
OH VII
SiO2
N
N
N
H
N
H
H
β
β
HO
VI
OH
HO
VI
OH VII
VII
Si-NH-CD
Scheme 1. Synthetic schemes for the preparation of Si-NH-CD and Si-DETA-CD.
Si-DETA-CD
In order to optimize the reaction conditions, both schemes were performed under different reaction
conditions, as depicted in Table 1. Thermogravimetric analyses (TGA) and IR spectra were carried out
to measure the loading and to confirm the identity of the synthesized silica derivatives. TGA allowed
the grafting efficacy of every single step to be quantified by assuming that water is the only compound
◦
removed from the starting silica by surface dehydroxylation. The curves were all normalized to 150 C
to circumvent any possible solvent influence on yield calculations. When DETA was reacted with
silica chloride, a number of solvents were compared under conventional conditions, and a suspension
◦
of Si-Cl in toluene, chloroform, and DMF was treated with the triamine derivative at 60 C for 12 h.
As represented in Figure 2, the TGA analyses of Si-DETA showed a higher degree of derivatization
◦
when toluene was used as the solvent. The first derivative peak temperature (315 C) indicates the
point of the greatest rate of change on the weight loss curve, and the profile was consistent in all three
samples. The synthetic process was also performed under sonication in order to reduce the reaction
time and improve functionalization. US irradiation is considered to be a nonconventional means to
achieve efficient heating, dispersion, the deagglomeration of solids, and improvements in mass transfer.
It offers a facile, versatile synthetic tool for the preparation of nano-/micro-structured materials that
are often unavailable via conventional methods. Several different frequencies (40–80–120 kHz) were
used and compared when the reaction was repeated under sonication. For the sake of comparison, the
reaction was sonicated for 2 and 4 h, and the results obtained in toluene were compared to reactions
performed neat in diethylenetriamine as the solvent. As depicted in Table 1, the same degree of
◦
substitution that was measured by TGA after 2 h of sonication was achieved after 12 h at 60 C,
while after 4 h of US irradiation, the degree of substitution was maintained without improvement.
Figure 3 shows the TGA profiles of Si-DETA batches obtained at a range of different frequencies,
either in toluene or neat in 2 h. An increase in weight loss was observed when the reactions were
sonicated at 80 kHz. 40 and 120 kHz failed to give the maximum degree of substitution under both
sets of reaction conditions.

Molecules 2019, 24, 2490
5 of 18
Table 1. Synthesis of grafted silica.
Loading
Loading
(µmol/g)
Entry
Product
Reaction Condition
Time
(
w/w %)
14 (a)
1.37 × 10
0.96 × 10
1.49 × 10
0.87 × 10
1.35 × 10
1.12 × 10
0.69 × 10
1.26 × 10
0.79 × 10
0.97 × 10
1.12 × 10
0.97 × 10
0.77 × 10
1.26 × 10
0.88 × 10
3 (c)
1
2
3
4
5
6
7
8
9
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA
Si-DETA-CD
Si-Cl, DETA, DCM, reflux
12 h
12 h
12 h
2 h
2 h
2 h
2 h
2 h
2 h
4 h
4 h
4 h
4 h
4 h
4 h
24 h
4 h
12 h
12 h
2 h
2 h
4 h
4 h
◦
(a)
3 (c)
3 (c)
3 (c)
3 (c)
3 (c)
3 (c)
3 (c)
3 (c)
3 (c)
3 (c)
3 (c)
3 (c)
3 (c)
3 (c)
Si-Cl, DETA, DMF, 60 C
10
15
9
14
11.5
7.1
◦
(a)
Si-Cl, DETA, toluene, 60 C
(
a)
Si-Cl, DETA, toluene, US, 40 kHz
Si-Cl, DETA, toluene, US, 80 kHz
Si-Cl, DETA, toluene, US, 120 kHz
Si-Cl, DETA, neat, US, 40 kHz
Si-Cl, DETA, neat, US, 80 kHz
Si-Cl, DETA, neat, US, 120 kHz
Si-Cl, DETA, toluene, US, 40 kHz
Si-Cl, DETA, toluene, US, 80 kHz
Si-Cl, DETA, toluene, US, 120 kHz
Si-Cl, DETA, neat, US, 40 kHz
Si-Cl, DETA, neat, US, 80 kHz
Si-Cl, DETA, neat, US, 120 kHz
(
a)
(
a)
(
a)
(
a)
13
8.2
10
(
a)
(
a)
10
11
12
13
14
15
16
17
18
19
20
21
22
23
14.3 (
a)
a)
(
10.9
(
a)
(
8
a)
13.5
(
a)
9
◦
(b)
(d)
Si-DETA, 6-tosyl β-CD, DMF, 70 C
1.3
11
3.3 (a)–3.4 (b)
30
(c,d)
Si-DETA-CD Si-DETA, 6-tosyl β-CD, DMF, US, 80 kHz
◦
(a)
(b)
35 (c)
Si-NH-CD
Si-NH-CD
Si-NH-CD
Si-NH-CD
Si-NH-CD
Si-NH-CD
Si-Cl, 6-amino β-CD, DMF, 60 C
4.02 –0.99
◦
(a)
(b)
(c)
(c)
(c)
(c)
(d)
Si-Cl, 6-amino β-CD, H O, 60 C
2.6 –0.81
20
30
60
30
60
2
3.81 ( –0.68
a)
(b)
(b)
Si-Cl, 6-amino β-CD, DMF, US, 80 kHz,
(
a)
Si-Cl, 6-amino β-CD, H O, US, 80 kHz,
7.12 –0.60
3.5 ( –0.67
6.8 ( –0.68
2
a)
(b)
(b)
Si-Cl, 6-amino β-CD, DMF, US, 80 kHz,
a)
Si-Cl, 6-amino β-CD, H O, US, 80 kHz,
2
1
Preparation of Si-DETA: Si-Cl (0.00 g), solvent (0.500 mL), and diethylenetriamine (0.500 mL). Preparation of
I
Si-DETA-CD: Si-DETA (0.100 g), DMF (1.7 mL), and 6 -tosyl-
solvent (2 mL), and 6-amino -CD (0.163 g). (a) The w/w % grafting was measured on the basis of TGA; (b) the w/w
grafting was based on phenolphthalein (Php) titration; (c) mmol/g values were measured on the basis of TGA
considering the organic moiety anchored to the silica surface; (d) mmol/g of β-CD based on PhP titration.
β-CD (0.100 g). Preparation of Si-NHCD: Si-Cl (0.100 g),
β
%
Figure 2. TGA profiles of starting silica and Si-DETA substrates (Table 1, Entries 1–3). The reaction
◦
mixture was heated at 60 C and conventionally stirred for 12 h. Three different solvents were tested.
Solid line, starting silica; dashed line, Si-DETA prepared in DMF, Table 1, Entry 2; dotted line, Si-DETA
prepared in DCM, Table 1, Entry 1; dashed-dotted line, Si-DETA prepared in toluene, Table 1, Entry 3.
I
When
β
-CD was grafted onto Si-DETA via the nucleophilic replacement of 6 -tosyl
β-CD, the
◦
reaction was performed conventionally in DMF at 70 C for 24 h (Entry 16, Table 1). Looking at TGA
(
Figure 3), we can assume that DETA was acting as the leaving group as the organic moiety on the silica
surface was reduced in weight after the reaction if compared to the starting material. The interaction
between -CD and phenolphthalein (Php) was used to achieve the dual aims of measuring the amount
β

Molecules 2019, 24, 2490
6 of 18
of
inclusion capacity of the grafted
via titration with Php in the buffer solution (pH = 10.5) of 0.008 mM. The amount of grafted
β
-CD that maintains its inclusive properties when grafted onto the silica and of investigating the
-CD. In combination with TGA, the amount of -CD was measured
-CD was
β
β
β
measured on the basis of UV adsorbance, via interpolation from the standard curve. The change in
Php absorbance was recorded on a UV spectrophotometer at 553 nm. When the grafting of CD was
performed under conventional heating, by UV adsorbance of the Php solution, we could detect the
presence of solid supported β-CD and measure a w/w % of grafting of 1.3 mg/100 mg Entry 16, Table 1).
◦
◦
The same sample analyzed by TGA showed a decrease in total weight loss in the range 150 C–800 C
if compared to the starting Si-DETA derivative (see Figure 4). Based on this fact, we assumed the
instability of the precursor in the reaction condition, as furthermore confirmed by IR analysis described
below. Under sonication at 80 kHz, the grafting percentage increased to 3.3% w/w, and PhP titration
confirmed the derivatization data (Entry 17, Table 1). Unfortunately, we observed that the preparation
I
of Si-DETA-CD was not reproducible, and so, we proceeded with the direct grafting of 6 amino
to Si-Cl (Scheme 1).
β-CD
Figure 3. TGA profiles of silica and Si-DETA obtained using US irradiation at different frequencies
40–80–120 kHz), in neat conditions (Table 1, Entries 7–9, blue lines) and in toluene (Table 1, Entries 4–6,
(
red lines). Solid line, starting silica; blue, dashed line, Si-DETA, neat, US 40 kHz, Table 1, Entry 7; blue,
dashed-dotted line, Si-DETA, neat conditions, 120 kHz, Table 1, Entry 9; red, dashed line, Si-DETA,
toluene, 40 kHz, Table 1, Entry 4; red, dashed-dotted line, Si-DETA, toluene, 120 kHz, Table 1, Entry 6;
blue, dotted line, Si-DETA, neat conditions, 80 kHz, Table 1, Entry 8; red, dotted line, Si-DETA, toluene,
8
0 kHz, Table 1, Entry 5.
I
I
◦
β-CD was reacted with Si-Cl for 12 h at 60 C in
As described in Table 1, when 6 -amino-6 -deoxy-
DMF, a w/w % degree of derivatization of 4% was detected by TGA, while PhP titration detected only
.99% of -CD, providing an inconclusive answer to the preservations of its properties (Entries 18–19,
0
β
Table 1). A higher percent of grafting was observed in water. When the reaction was repeated under
sonication, the reaction reached the same degree of derivatization in 2 h; after 4 h, any improvement
was observed (Entries 20–23, Table 1 Figure 3).
Copper(II) forms a complex with CD in alkaline solution, and the complexes with
have already been isolated and characterized [58]. The efficacy of -CD to direct and bind Cu when
CD is bonded to silica has been already studied, and its catalytic activity as a Lewis acid has been
demonstrated [59]. As the literature has focused mainly on the non-covalent bonding of -CD onto the
silica surface [60 61], we have aimed to explore the efficacy of -CD that is covalently grafted onto
α- and β-CD
β
β
,
β
silica to chelate Cu(II) and to exploit this system as a catalyst for alkyne-azide cycloaddition (CuAAC)
in the absence of a reducing agent.
Si-DETA CD and Si NH CD (Entries 17 and 22, Table 1) were both loaded with Cu(II), and the
reaction was performed in a NaOH water solution to obtain a blue-colored catalyst.

Molecules 2019, 24, 2490
7 of 18
Figure 4. TGA profile of starting silica, Si-DETA (green line), Si-NHCD (red lines), and Si-DETA-CD
blue lines) prepared conventionally or under US irradiation. Solid line, starting silica; red, dotted line,
Si-NHCD US irradiation 80 kHz in DMF for 2 h, Table 1, Entry 20; blue, dashed line, Si-DETA-CD
(
◦
conventional heating in DMF at 70 C for 24 h, Table 1, Entry 16; red, dashed line, Si-NHCD US
irradiation 80 kHz in H O for 2 h, Table 1, Entry 21; green, dashed line, Si-DETA; blue, dotted line,
2
Si-DETA-CD US irradiation 80 kHz in DMF for 4 h, Table 1, Entry 17.
2
.2. Characterization of Copper Supported on Si-NH-CD and Si-DETA-CD
2
The BET surface area of the functionalized materials was found to be around 110 m /g.
The micrometer-sized particles, formed by nanometer-sized primary particles, were preserved after
sonication, as observed by scanning electron microscopy (SEM; not reported). Si-DETA, Si-DETA-CD,
and Si-NH-CD (Entries 5, 17, and 21, Table 1) were characterized by IR to prove the identity of the grafted
silica. The same was done for Si-DETA-CD-Cu and Si-NH-CD-Cu. As shown in Figure 5, the presence
of the diethylentriamino spacer on Si-DETA can be observed in Spectrum c. This was characterized by
−
1
a broad absorption band centered on 3000 cm , which can be ascribed to hydrogen-bonded Si-OH and
N–H groups [62]. The expected NH bands can be only seen as a modulation of the intense absorption,
υ
−
1
between 3400 and 3200 cm . The corresponding weak
δ
NH mode was vibrating at a similar frequency
2
−1
−1
as the physisorbed water (around 1600 cm ), while the band at 1510 cm can be ascribed to the
δ
NH
vibrations of the secondary amines. Important changes can be observed in the spectrum (Curve d) after
I
the reaction with 6 -tosyl-
β
-CD (and subsequent Cu inclusion). Namely, the high frequency region was
−
1
−1
υCH/υCH bands at 2930 cm
2
dominated by an intense band centered at 3360 cm
shoulder at 2860 cm ). The low frequency region shows the typical bending mode of physisorbed
(υ
OH), with clear
−
1
(
−1
−1
water
δ
H O centered at 1605 cm (shoulder at 1662 cm ) and a complex group of bands between
2
−
1
1500 and 1250 cm
(δCH and δOH). These features can be safely ascribed to the presence of β-CD,
−
1
even if the assignment of the shoulder at 1662 cm to physisorbed water alone is not straightforward.
Similar results were obtained with the sample prepared with direct Si-NH-CD (Curve e). The main
difference was in the relative intensity of the bands assigned to
spectra of -CD and Cu-CD (not reported) led us to propose that this vibrational mode is sensitive to
the presence of the Cu(II) ions included in the cavity and at the rim of the CD cavity. These results thus
confirmed the presence of -CD on the silica in the various preparations. However, the changes in the
δH O modes. A comparison of the
2
β
β
high frequency region passing from Si-DETA to Si-DETA-CD (Curves c and d) suggested a decrease in
the amount of the diethylentriamino spacer, confirming the instability of Si-DETA when submitted to
I
reaction with 6 -tosyl-
β-CD. The hydroxyl group of CD may act as a nucleophile, and DETA cannot be
efficiently and reproducibly washed from the silica surface because of the strong interactions with
surface silanol/silanolate groups [63].

Molecules 2019, 24, 2490
8 of 18
δH O
νOH
νCH
2
δOH
δCH
3
360
δNH
nd
2
1
e)
d)
c)
νNH
b)
a)
δNH2
0
4
000
3500
3000
1750
1500
1250
-
1
Wavenumbers (cm )
Figure 5. Infrared spectra of: (
Si-NH-CD. All samples were outgassed at 80 C before measurements.
a) Si-diAm; (b) Si-diAm-CD-Cu; (c) Si-DETA; (d) Si-DETA-CD-Cu; (e)
◦
The presence of Cu on the catalysts was monitored by diffuse reflectance UV-Vis-NIR spectroscopy.
For example (see Figure 6), we report the spectrum of Si-NH-CD-Cu (blue curve) compared to the spectra
of the reference materials (
UV (200–400 nm), corresponding to O
corresponding to the ligand-field d-d transitions of Cu(II) ions; and (iii) NIR (800–2500 nm), where the
overtone and combination modes of infrared modes can be observed. The NIR region analysis allows
us to further confirm the presence of the CDs that are linked to the silica support and to confirm the
involvement of OH groups in the coordination of the Cu ions. Indeed, all the hybrid-material spectra
β-CD, SiO , and Si-NH-CD). The spectra can be divided into three regions: (i)
2
2−
→
Cu(II) charge transfer (CT) transitions; (ii) visible (400–800 nm),
showed signals in this region that were a mixture of the vibrational modes of SiO (Si-OH overtone
2
υ0-2 OH,
υ
+
δ
H2O
/υ
+
δ
OH
combination modes of physisorbed water and of Si-OH groups) and those
of CD ( 0
υ
-2 OH,
υ
+
δH2O,
υ0-2 CH,
υ
OH
+ υCO). On the other hand, the UV-Vis region of Si-NH-CD-Cu
clearly showed the typical fingerprint of hexacoordinated Cu(II) ions, with a CT component at 260 nm
and an intense and broad d-d band at 700 nm [64]. These results were in agreement with the structures
proposed in [65], which involved hexacoordinated Cu(II) ions in the cavity and at the rim of the CD cavity,
−
coordinated by H O molecules, OH/O CD groups, and/or extra ligands.
2
100
80
60
40
20
Cu(II)
d-d
CT
400
800
1200
1600
2000
2400
Wavelenght (nm)
Figure 6. Diffuse reflectance DR UV-Vis-NIR spectra of: SiO (grey);
β-CD (black); Si-NH-CD (pink);
2
Si-NH-Cu-CD (blue); and Si-diAm-Cu-CD (green).

Molecules 2019, 24, 2490
9 of 18
ICP analyses of Si-NH-CD-Cu and Si-DETA-CD-Cu quantified the Cu content on the silica: at
1
0.1 mg/g and 7.2 mg/g of Cu, respectively.
2
.3. Test of the Catalytic Activity of Copper Supported on Si-NH-CD and Si-DETA-CD
Cu(II)- -CD has been proven to be a reliable, water-soluble, green catalyst for 1,2,3-triazole
β
synthesis without the addition of a reducing agent [40]. Both catalysts were tested in a model CuAAC
reaction (Scheme 2).
Scheme 2. Model reaction for the copper alkyne-azide cycloaddition (CuAAC) test of Si-NH-CD-Cu
and Si-DETA-CD-Cu.
As depicted in Table 2, the click Cu-catalyzed cyclization of benzyl azide and phenylacetylene
was repeated under a number of reaction conditions, and different copper sources were compared.
◦
The reaction was performed at 85 C for 1 h. Silica-supported Si-NHCD-Cu and Si-DETA-CD-Cu
showed differing catalytic activities. In fact, only the second acted as an efficient catalyst for CuAAC
(
Entries 5–6, Table 2). As already observed in the Php titrations, it showed a higher inclusion capability
when CD was bound to the silica with a spacer; furthermore, the triamino spacer can stabilize
Cu(II) species. Si-DETA-CD-Cu showed high efficiency even when used in very small amounts.
However, a reduction of activity was observed when the catalyst amount was decreased to 0.5 mol%
(
Entries 6–8 Table 2). Cu(II) salts Cu(OAc) and CuSO were tested, for the sake of comparison, and the
2 4
reaction was compared to a click reaction that was catalyzed by a previously-prepared Cu(II)-
β-CD
complex, and a reaction using a physical mixture of CuSO and -CD. Only the Cu(II)- -CD complex
β
β
4
gave satisfactory results, and a 55% yield was recovered. In order to understand the influence of silica
and the amino spacer on reaction outcome, Si-Cu and Si-DETA-Cu were tested to confirm that the
complex between the copper ions and β-CD played a key role in the performance of the reaction,
in which β-CD acted as a ligand for copper and the reducing agent.
Table 2. Panel test of the CuAAC reaction.
Yield (%) (a)
Entry
Catalyst, Cu mol%
Cu(OAc) , 5 mol%
1
2
3
4
5
6
7
8
9
14
0
0
55
5
>99
>99
>99
80
>99
65
4
2
CuSO , 5 mol%
4
β-CD-CuSO , 5 mol% (physical mixture)
4
β-CD-Cu, 5 mol% (complex)
Si-NHCD-Cu, 4 mol%, (17 mg)
Si-DETA-CD-Cu, 4 mol% (24 mg)
Si-DETA-CD-Cu, 2 mol% (12 mg)
Si-DETA-CD-Cu, 1 mol% (6 mg)
Si-DETA-CD-Cu, 0.5 mol% (3 mg)
Si-DiAm-CD, 4 mol% (11 mg)
Si-DiAm-CD, 2 mol% (5.5 mg)
Silica-Cu (12 mg)
1
1
1
1
0
1
2
3
a
Si-DETA-Cu (12 mg)
0
◦
Reaction conditions: benzyl azide (0.0676 mmol, 1 eq), phenylacetylene (1 eq), H
or MW 85 C 20 min. (a) Determined by GC-MS.
2
O:tBuOH (1:1; 500
µ
L), 85 C, 1 h,
◦

Molecules 2019, 24, 2490
10 of 18
2
.4. Synthesis, Characterization, and Catalytic Activity of Copper Supported on Si-diAm-CD
In order to obtain a stable silica-supported -CD derivative with a polyamino spacer, Si-diAm-CD
β
was synthesized on the basis of our previous experience (see Scheme 3).
Scheme 3. Schematic representation of the Si-diAm-CD synthesis.
Silica was derivatized with 3-(2-aminoethylamino)propyltrimethoxysilane (AEPS) to obtain Si-diAm.
As described in Table 3, we can confirm that sonication reduced the reaction time to 2 h, whereas the
◦
same degree of substitution was achieved after 36 h at 80 C under conventional heating and magnetic
stirring. No differences in activation was observed between the use of 40 and 80 kHz, and both were very
◦
efficient. In order to obtain the efficient grafting of
β-CD, 6-O-tosyl
β
-CD was reacted at 60 C for 60 h,
and 4.7% w/w derivatization was observed by TGA, while 2.8% was measured by Php titration. Sonication
at 80 kHz in a US bath reactor was insufficient to obtain a satisfactory grafting percent, because of the low
◦
reaction temperature (45–50 C). An increase in grafting percentage was observed when the reaction was
prolonged to six days. The synergic effect of combined MW and sonication was also exploited. Enhancing
the silica dispersion, increasing the active surface, and allowing a selective MW irradiation, the combined
system permitted obtaining high efficacy of grafting in a short time, 4 h, and a 6.1 w/w% derivatization
was afforded. As depicted in Figure 7, the first derivative TGA profile of Si-diAm indicated that the
◦
degradation peak was approximately at 314 ; when CD was grafted, two degradation steps were visible,
◦
◦
and the peaks were at 298 C and at 413 C.
Table 3. Synthesis of Si-diAm-CD.
Loading
Loading
(µmol/g)
Entry
Product
Reaction Condition
Time
(
w/w %)
◦
6.5 (a)
13.6
(c)
(c)
(c)
(c)
(c)
1
2
3
4
5
6
7
8
9
Si-diAm
Si-diAm
Si-diAm
Si-diAm
Si-diAm
Si-diAm-CD
Si-diAm-CD
Si-diAm-CD
Si-diAm-CD
Silica, AEPS, toluene, 80 C
6 h
36 h
2 h
2 h
4 h
60 h
6 days
4 h
290
610
640
540
600
42
54
15
54
◦
(a)
a)
Silica, AEPS, toluene, 80 C
(
Silica, AEPS, toluene, US, 40 kHz
Silica, AEPS, toluene, US, 80 kHz
Silica, AEPS, toluene, US, 80 kHz
Si-diAm, 6 -tosyl-β-CD, DMF, 60 C
Si-diAm, 6 -tosyl-β-CD, DMF, 60 C
14
12
13
(
(
a)
a)
I
◦
4.7 (a)–2.15
6.1 –2.8
1.7 –1.18
6.1 –2.09
(b)
(c)
I
◦
(a)
(b)
(c)
(c)
(c)
I
(a)
(b)
(b)
Si-diAm, 6 -tosyl-β-CD, DMF, US, 80 kHz
Si-diAm, 6 -tosyl-β-CD, DMF, MW/US, 100 C
I
◦
(a)
4 h
(
%
a) Measured by TGA; the weight loss was calculated on the basis of the starting material (see Figure 6); (b) the w/w
grafting was based on PhP titration; (c) mmol/g of organic moiety grafted on the silica surface.

Molecules 2019, 24, 2490
11 of 18
Figure 7. TGA profile of Si-DiAm-CD. (Solid line) Starting silica; (dashed line) Si-DiAm, obtained in
US at 80 kHz, 2 h, toluene, Table 3, Entry 4; (dotted line) Si-DiAm-CD, MW-US combined irradiation at
◦
1
00 C, 4 h, DMF, Table 3, Entry 9.
Si-diAm-CD was loaded with Cu (II) in basic conditions, and the catalysts, Si-diAm and
Si-diAm-CD, were characterized by IR and DR UV-Vis-NIR.
The IR spectra of Si-diAm and Si-diAm-CD are reported in Figure 2. Si-diAm (Curve a) showed
− −1 −1
very clear υNH (3362 and 3296 cm ), υCH (2932, 2870, and 2806 cm ), and δNH bands (ca. 1600 cm ),
2
1
which were preserved after reaction to graft CD (Si-diAm-CD, Curve b). This proved Si-diAm’s
increased stability during the reaction with CD, as compared to Si-DETA derivatization in which
the bands were partially displaced (Curves c and d). An analysis of the low-frequency region of the
spectra showed the fingerprints of β-CD (δH O, δCH, and δOH). Diffuse reflectance UV-Vis-NIR
2
spectroscopy showed the presence of Cu after the reaction between CuSO and Si-diAm-CD, and the
4
typical fingerprint of hexacoordinated Cu(II) ions (d-d band at 650 nm and CT at 260 nm) can be
observed (Figure 5). ICP analysis showed a loading of 15.5 mg/g of copper.
When catalytic activity was tested in a model reaction (CuAAC of benzyl azide and phenyl
acetylene), it was possible to evaluate the high catalytic activity of Si-DETA-CD-Cu. A slightly higher
amount of catalyst was employed in order to obtain full conversion, and the reaction was successful in
the presence of 4 mol% of catalyst. Alkylic and arylic azido derivatives, as well as alkynes, were tested
to prove not only the efficacy, but also the versatility of the system (See Table 4). Full conversion was
observed, and the product was isolated without purification.

Molecules 2019, 24, 2490
12 of 18
Table 4. Synthetic results of conventional Cu-supported catalyst.
Entry
Alkyne
Azide
Product
Yield (%)
N
N
N
9
9 (a)
9
9
5 (a)
2 (a)
8
9 (a)
Reaction conditions: azide (0.0676 mmol, 1 eq), terminal alkyne (1 eq), H
catalyst (4 mol %), MW heating at 85 C, 1 h. (a) Yields determined by GC-MS.
2
O (250
µL), tBuOH (250
µL), 11 mg of
◦
3
. Materials and Methods
3
.1. Materials
All commercially-available reagents and solvents were purchased from Sigma-Aldrich
Milan, Italy) and used without further purification. SIPERNAT 320 amorphous silica was
(
I
I
supplied by Evonik Degussa (Essen, Germany). The synthesis of 6 -amino-6 -deoxy-
β-CD and
I
6
-O-p-Toluenesulfonyl-β-CD was performed following the published synthetic procedure [66]. β-CD
was provided by Wacker Chemie (München, Germany). US irradiation at 40–80–120 kHz was performed
in highly efficient bath reactors supplied by Weber Ultrasonics GmbH (Karlsbad-Ittersbach, Germany).
The transducers’ efficiency was monitored by measurements with a cavitometer. Owing to the size
reduction of cavitation bubbles moving from 40, to 80, to 120 kHz, a progressive decrease of the
measured cavitation intensity was observed.
The reactions were carried out in a combined microwave (MW)/US system [45] designed in
our laboratory using a probe equipped with a horn made in Pyrex inserted in an MW cavity
(RotoSynth, Milestone, Bergamo) (Figure 8).
Thermogravimetric analyses were performed using a thermogravimetric analyzer TGA 4000
◦
−1
(
PerkinElmer, MA, USA) at 10 C min operating with alumina crucibles that contained 10 20 mg
−
of sample. The analyses were performed under an argon atmosphere at a starting temperature of
◦ ◦
0 C and an end temperature of 800 C. Total mass loss was attributed to the functional groups that
5
were covalently attached to the sidewalls. UV-Vis absorption spectra were measured on a dual-beam
spectrophotometer (Agilent Technologies Cary 60, G6860AA, Santa Clara, CA, USA) equipped with a
1
-cm path length quartz cuvette. Elemental analyses were performed on an EA 1108 (Fison Instruments).
Reactions were carried out in a professional MW reactor (Monowave 400/200, Anton Paar GmbH,
Graz, AT) using reaction vial G10. Reactions were monitored by TLC on Merck 60 F254 (0.25 mm)
plates (Milan, Italy), which were visualized by UV inspection. GC-MS analyses were performed in a

Molecules 2019, 24, 2490
13 of 18
GC Agilent 6890 (Agilent Technologies, Santa Clara, CA, USA) that was fitted with a mass detector
Agilent Network 5973, using a 30-m capillary column, i.d. of 0.25 mm, and a film thickness of 0.25
µ
◦
◦
m.
◦
GC conditions were: injection split 1:10, injector temperature 250 C, detector temperature 280 C.
◦
The gas carrier was helium (1.2 mL/min), and temperature program was from 50 C (5 min) to 100 C
(
◦ ◦ ◦ ◦ ◦
1 min) at 10 C/min, to 230 C (1 min) at 20 C/min, and to 300 C (5 min) at 20 C/min. HRMS was
determined using a MALDI-TOF mass spectra (Bruker Ultraflex TOF mass spectrometer, Milan, Italy).
The cations were determined with a Perkin Elmer Optima 7000 (Perkin Elmer, Norwalk, Connecticut,
USA) inductively-coupled plasma-optical emission spectrometer (ICP-OES).
Figure 8. Combined MW/US device.
3
.2. Catalyst Preparation
3
.2.1. Preparation of Chlorinate Silica
Ten-point-five milliliter of SOCl were added dropwise to 1 g of silica SIPERNAT 320. The mixture
2
was left stirring under reflux, 16 h. The suspension was filtered, and the powder was washed with
chloroform and dried under a vacuum [56].
Si-Cl Titration
The amount of chloride present in the sample was determined via argentometric titration.
The Mohr method was followed. The sample solution was titrated against a solution of silver nitrate of
known concentration. Chloride ions reacted with silver(I) ions to give insoluble silver chloride (1):
+
−
Ag (aq) + Cl → AgCl (s)
(1)
One gram of Si-Cl was dispersed in 100 mL of a NaHCO solution (0.005 M). The solution was
3
stirred for 1 h at room temperature. Potassium chromate was used as an indicator, giving red silver
chromate after all the chloride ions had reacted:
+
2−
2
Ag (aq) + CrO4 (aq) → Ag CrO (s)
(2)
2
4
Three hundred ninety eight microliters of K CrO 0.25 M were added, and the solution was titrated
2
4
−
1
with AgNO 0.1 M (2) to obtain the amount of chlorosilyl groups on the silica surface (~0.9 mmol g ).
3

Molecules 2019, 24, 2490
14 of 18
3
.2.2. Preparation of Si-DETA
Diethylenetriamine (0.500 mL) was dissolved in 0.500 mL of solvent (see Table 1, Entries 1–3),
◦
and Si-Cl was added (0.100 g). The suspension was heated under stirring in an oil bath (60 C for
12 h). When the reaction was performed in a US bath reactor (40, 80, or 120 kHz, power 200 W),
the suspension was sonicated for 2–4 h in toluene or in diethylenetriamine (see Table 1, Entries 4–15).
The modified silica was then filtered, washed with water, methanol, and chloroform, and dried under
a vacuum at room temperature for 12 h.
3
.2.3. Preparation of Si-DETA-CD
6
-monotosyl-CD (0.100 g, 0.077 mmol) was dissolved in DMF (1.7 mL), and Si-DETA (0.100 g)
◦
was added (Table 1, Entry 16). The suspension was heated to 70 C under magnetic stirring for 24 h.
When the reaction was performed under sonication, the suspension reacted in 4 h (power 200 W,
frequency 80 kHz) (Table 1, Entry 17). Silica was filtered, washed with water, methanol, and chloroform,
and dried under vacuum at room temperature for 12 h.
3
.2.4. Preparation of Si-NH-CD
6I-amino-6 -deoxy-
I
β-CD (0.163 g, 0.14 mmol) was dissolved in DMF (2 mL) or water, and then,
chlorinate silica (0.100 g) and pyridine (0.332 mL) were added (Table 1, Entries 18–23). The suspension
◦
was either conventionally stirred at 60 C for 12 h or was sonicated in a US bath reactor at 80 kHz
(
power 200 W) for 2–4 h. Modified silica was filtered, washed with water, methanol, and chloroform,
and dried under a vacuum at room temperature for 12 h.
3
.2.5. Preparation of Si-DiAm
-(2-Aminoethylamino)propyltrimethoxysilane (0.040 mL) was dissolved in toluene (1 mL),
3
and silica SIPERNAT 320 (0.100 g) was added. The suspension was either heated under stirring in an
◦
oil bath (80 C for 36 h) or the reaction was performed in a US bath reactor (power 200 W, comparing
40 and 80 kHz as frequencies), as depicted in Table 2 (Entries 1–5). Silica was filtered, washed with
toluene and chloroform, and dried under a vacuum at room temperature for 12 h.
3
.2.6. Preparation of Si-DiAm-CD
6I-O-p-Toluenesulfonyl-
β
-CD (0.100 g, 0.077 mmol) was dissolved in DMF (1.5 mL), and Si-DiAm
◦
(
(
0.100 g) was added. The suspension was either heated to 60 C and stirred for 60 h or sonicated
4 h, power 200 W, frequency 80 kHz) (Entries 6–9 Table 3). The same procedure was repeated under
MW and US combined irradiation: 1 g of Ts-CD was dissolved in 15 mL of DMF, and 1 g of Si-DiAm
◦
was added. The suspension was heated at 100 C for 4 h (average MW power 20 W, average US
power 35 W). After cooling to room temperature, the modified silica was filtered, washed with water,
methanol, and chloroform, and dried under a vacuum at room temperature for 12 h.
3
.2.7. Cyclodextrin-Supported Silica and Copper Complexation
For CD-supported silica (0.100 g), either Si-NH-CD, Si-DETA-CD, or Si-diAm-CD were dispersed
in 0.675 mL of NaOH 0.5 M. The suspension was stirred for 1 min by sonication, and 0.719 mL of
CuSO 0.08 M were added dropwise. The mixture was sonicated for 10 s in an US bath reactor and
4
was then filtered and washed thoroughly with water and methanol and, finally, dried under a vacuum
at room temperature for 12 h.
3
.3. Click Chemistry Reaction
Azide (0.0676 mmol, 1 eq) and terminal alkyne (1 eq) were dissolved in 0.500 µL of H O: tBuOH
2
(
1:1). Solid-supported catalyst Si-NHCD-Cu, Si-DETA-CD-Cu, or Si-diAm-CD-Cu was added as
◦
◦
described in Table 4. The reaction was heated up at 85 C, for 1 h or under MW irradiation (85 C) for

Molecules 2019, 24, 2490
15 of 18
2
0 min. The resulting mixture was filtered and washed with methanol and chloroform. The solvent was
1
removed under vacuum to afford the triazole. All products were confirmed by H NMR and GC-MS.
3
.4. Physico-Chemical Characterization
The specific surface area (SSA) of the samples was measured by N adsorption isotherms
2
at liquid nitrogen temperature using an ASAP 2020 physisorption analyzer (Micromeritics).
0
The SSA was calculated by the Brunauer–Emmett–Teller (BET) method in the p/p 0.05–0.3 interval.
Before measurements, the samples were outgassed at room temperature overnight.
Infrared spectra were recorded on a BRUKER FTIR-66 spectrophotometer with a resolution of
−1
2
cm , using a DTGS detector. Measurements were carried out using a home-made cell allowing in situ
thermal treatment and room temperature measurement. Thin self-supporting pellets for transmission
2
measurements (around 10 mg/cm ) were prepared with a hydraulic press. Before the measurements,
◦
the samples were outgassed at 80 C for 2 h in the same cell used for the measurements.
β-CD and
Cu-CD were measured after dilution in KBr, without thermal treatment (spectra not reported).
UV-Vis-NIR spectra were recorded in the 2500–200-nm range at 1-nm resolution on a Cary 5000
UV-Vis-NIR spectrophotometer (Agilent) equipped with a diffuse reflectance attachment with an
integrating sphere coated by BaSO . Prior to each measurement, a baseline spectrum was collected by
4
using Teflon as a reference. Spectra are reported as relative reflectance (R%), defined as:
R% = Rsample/Rreference × 100
(3)
4
. Conclusions
In conclusion, the ability of sonication to speed up the synthetic procedures for silica grafting
was demonstrated. New -CD grafted silicas were synthesized and fully characterized. The influence
of US at different frequencies (40–80 and 120 KHz) was studied and compared to conventional
conditions. MW combined with US was also employed in grafting -CD to previously derivatized
silica. The influence that -CD had on directing and activating Cu(II) on the silica surface for
CuAAC reactions, in absence of a reducing agent, was studied and confirmed. Low cost, green, fast,
and efficient procedures can be exploited to obtain Cu- -CD-grafted silica with polyamino spacers
β
β
β
β
under sonication. The catalyst showed excellent performance in CuAAC reactions without the addition
of a reduction agent.
Author Contributions: Conceptualization, K.M. and G.C; validation, K.M. and F.C.; investigation F.C. M.J.M. and A.Z.;
data curation, G.B and F.C.-R.; writing, original draft preparation, K.M. writing, review and editing, G.C. and R.L.
Funding: This project received funding from the European Union’s Horizon 2020 research and innovation program
under the Marie Skłodowska-Curie Grant Agreement No. 721290. This publication reflects only the author’s
view, exempting the Community from any liability. Project website: http://cosmic-etn.eu/. The publication was
prepared with support of RUDN University Program 5-100.
Acknowledgments: The authors acknowledge the University of Turin for the financial support (ricerca locale
2
018), the contribution of Compagnia di San Paolo supplied under the Multi-year Convention (2016–2018) between
the University of Turin and Compagnia di San Paolo, and Agnese Giacomino (University of Turin) for ICP analysis.
Conflicts of Interest: The authors declare no conflict of interest.
References
1
.
Gomez-Romero, P. Hybrid organic-inorganic materials—In search of synergic activity. Adv. Mater. 2001, 13, 163–174.
CrossRef]
[
2
.
Heo, J.H.; Im, S.H.; Noh, J.H.; Mandal, T.N.; Lim, C.S.; Chang, J.A.; Lee, Y.H.; Kim, H.J.; Sarkar, A.;
Nazeeruddin, M.K.; et al. Efficient inorganic-organic hybrid heterojunction solar cells containing perovskite
compound and polymeric hole conductors. Nat. Photonics 2013, 7, 487–492. [CrossRef]
3
.
Parola, S.; Julian-Lopez, B.; Carlos, L.D.; Sanchez, C. Optical properties of hybrid organic-inorganic materials
and their applications. Adv. Funct. Mater. 2016, 26, 6506–6544. [CrossRef]

Molecules 2019, 24, 2490
16 of 18
4
.
Taleghani, S.; Mirzaei, M.; Eshtiagh-Hosseini, H.; Frontera, A. Tuning the topology of hybrid inorganic-organic
materials based on the study of flexible ligands and negative charge of polyoxometalates: A crystal engineering
perspective. Coord. Chem. Rev. 2016, 309, 84–106. [CrossRef]
5.
6.
7.
Cui, J.D.; Jia, S.R. Organic-inorganic hybrid nanoflowers: A novel host platform for immobilizing biomolecules.
Coord. Chem. Rev. 2017, 352, 249–263. [CrossRef]
Wan, C.L.; Tian, R.M.; Kondou, M.; Yang, R.G.; Zong, P.G.; Koumoto, K. Ultrahigh thermoelectric power
factor in flexible hybrid inorganic-organic superlattice. Nat. Commun. 2017, 8. [CrossRef] [PubMed]
You, N.; Zhang, C.; Liang, Y.; Zhang, Q.; Fu, P.; Liu, M.; Zhao, Q.; Cui, Z.; Pang, X. Facile fabrication
of size-tunable core/shell ferroelectric/polymeric nanoparticles with tailorable dielectric properties via
organocatalyzed atom transfer radical polymerization driven by visible light. Sci. Rep. 2019, 9, 1869.
[CrossRef] [PubMed]
8
9
1
1
1
.
Sanchez, C.; Soler-Illia, G.; Ribot, F.; Lalot, T.; Mayer, C.R.; Cabuil, V. Designed hybrid organic-inorganic
nanocomposites from functional nanobuilding blocks. Chem. Mater. 2001, 13, 3061–3083. [CrossRef]
Sanchez, C.; Julian, B.; Belleville, P.; Popall, M. Applications of hybrid organic-inorganic nanocomposites.
J. Mater. Chem. 2005, 15, 3559–3592. [CrossRef]
.
0. Ziarani, G.M.; Lashgari, N.; Badiei, A. Sulfonic acid-functionalized mesoporous silica (SBA-Pr-SO H) as
3
solid acid catalyst in organic reactions. J. Mol. Catalys. Chem. 2015, 397, 166–191. [CrossRef]
1. Ziarani, G.M.; Badiei, A.; Mousavi, S.; Lashgari, N.; Shahbazi, A. Application of amino-functionalized SBA-15 type
mesoporous silica in one-pot synthesis of spirooxindoles. Chin. J. Catalys. 2012, 33, 1832–1839. [CrossRef]
2. Bhanja, P.; Modak, A.; Chatterjee, S.; Bhaumik, A. Bifunctionalized mesoporous SBA-15: A new heterogeneous
catalyst for the facile synthesis of 5-hydroxymethylfurfural. Acs Sustain. Chem. Eng. 2017, 5, 2763–2773.
[CrossRef]
1
1
1
1
3. Bied, C.; Gauthier, D.; Moreau, J.J.E.; Man, M.W.C. Preparation and characterization of new templated hybrid
materials containing a chiral diamine ligand. J. Sol-Gel Sci. Technol. 2001, 20, 313–320. [CrossRef]
4. Du, J.Z.; Chen, Y.M. Organic-inorganic hybrid nanoparticles with a complex hollow structure. Angew. Chem.
Int. Ed. 2004, 43, 5084–5087. [CrossRef] [PubMed]
5. Allain, C.; Favette, S.; Chamoreau, L.M.; Vaissermann, J.; Ruhlmann, L.; Hasenknopf, B. Hybrid
organic-inorganic porphyrin-polyoxometalate complexes. Eur. J. Inorg. Chem. 2008, 3433–3441. [CrossRef]
6. Zhang, J.; Jiang, P.P.; Shen, Y.R.; Zhang, W.J.; Bian, G. Covalent anchoring of Mo(VI) Schiff base complex into
SBA-15 as a novel heterogeneous catalyst for enhanced alkene epoxidation. J. Porous Mater. 2016, 23, 431–440.
[CrossRef]
1
1
7. Zare, M.; Moradi-Shoeili, Z.; Ashouri, F.; Bagherzadeh, M. Heterogeneous SBA-15-supported
oxoperoxomolybdenum(VI) complex for enhanced olefin epoxidation. Catal. Commun. 2017, 88, 9–12. [CrossRef]
8. Bhar, S.; Ananthakrishnan, R. Ru(II)-metal complex immobilized mesoporous SBA-15 hybrid for visible
light induced photooxidation of chlorophenolic compounds in aqueous medium. Photochem. Photobiol. Sci.
2
017, 16, 1290–1300. [CrossRef]
1
2
9. Reck, B.K.; Graedel, T.E. Challenges in metal recycling. Science 2012, 337, 690. [CrossRef]
0. Song, B.Q.; Wang, X.L.; Sun, C.Y.; Zhang, Y.T.; Wu, X.S.; Yang, L.; Shao, K.Z.; Zhao, L.; Su, Z.M. An
organic-inorganic hybrid photocatalyst based on sandwich-type tetra-Co-substituted phosphotungstates
with high visible light photocatalytic activity. Dalton Trans. 2015, 44, 13818–13822. [CrossRef]
1. Wei, X.L.; Lu, X.H.; Ma, X.T.; Peng, C.; Jiang, H.Z.; Zhou, D.; Xia, Q.H. Synthesis and catalytic activity
of organic-inorganic hybrid catalysts coordinated with cobalt(II) ions for aerobic epoxidation of styrene.
Catal. Commun. 2015, 61, 48–52. [CrossRef]
2
2
2
2. Barbe, J.M.; Canard, G.; Brandes, S.; Guilard, R. Organic-inorganic hybrid sol-gel materials incorporating
functionalized cobalt(III) corroles for the selective detection of CO. Angew. Chem. Int. Ed. 2005, 44, 3103–3106.
[CrossRef] [PubMed]
3. Al-Rehili, S.; Fhayli, K.; Hammami, M.A.; Moosa, B.; Patil, S.; Zhang, D.L.; Alharbi, O.; Hedhili, M.N.;
Mohwald, H.; Khashab, N.M. Anisotropic self-assembly of organic-inorganic hybrid microtoroids. J. Am.
Chem. Soc. 2017, 139, 10232–10238. [CrossRef] [PubMed]
2
4. Parmeggiani, C.; Cardona, F. Transition metal based catalysts in the aerobic oxidation of alcohols. Green Chem.
2
012, 14, 547–564. [CrossRef]
2
5. Hojoh, K.; Ohmiya, H.; Sawamura, M. Synthesisofalpha-quaternaryformimidesandaldehydesthroughumpolung
asymmetric copper catalysis with isocyanides. J. Am. Chem. Soc. 2017, 139, 2184–2187. [CrossRef] [PubMed]

Molecules 2019, 24, 2490
17 of 18
2
6. Zhang, K.; Lu, L.Q.; Yao, S.; Chen, J.R.; Shi, D.Q.; Xiao, W.J. Enantioconvergent copper catalysis: In situ
generation of the chiral phosphorus ylide and its wittig reactions. J. Am. Chem. Soc. 2017, 139, 12847–12854.
CrossRef] [PubMed]
7. Hickman, A.J.; Sanford, M.S. High-valent organometallic copper and palladium in catalysis. Nature
012, 484, 177–185. [CrossRef] [PubMed]
8. Chen, Z.F.; Meyer, T.J. Copper(II) Catalysis of water oxidation. Angew. Chem. Int. Ed. 2013, 52, 700–703.
CrossRef] [PubMed]
9. Wang, D.H.; Zhu, N.; Chen, P.H.; Lin, Z.Y.; Liu, G.S. Enantioselective decarboxylative cyanation employing
cooperative photoredox catalysis and copper catalysis. J. Am. Chem. Soc. 2017, 139, 15632–15635. [CrossRef]
0. Saunthwal, R.K.; Patel, M.; Kumar, S.; Verma, A.K. Cu(II)-catalyzed tandem synthesis of 2-imino 1,3
benzothiazines from 2-aminoaryl acrylates via thioamidation and concomitant chemoselective thia-Michael
addition. Tetrahedron Lett. 2015, 56, 677–681. [CrossRef]
[
2
2
2
3
2
[
3
3
3
3
3
3
1. Zhang, G.F.; Han, X.W.; Luan, Y.X.; Wang, Y.; Wen, X.; Xu, L.; Ding, C.R.; Gao, J.R. Copper-catalyzed aerobic alcohol
oxidation under air in neat water by using a water-soluble ligand. Rsc Adv. 2013, 3, 19255–19258. [CrossRef]
2. Maity, R.; Naskar, S.; Das, I. Copper(II)-catalyzed reactions of alpha-keto thioesters with azides via C–C and C–S
bond cleavages: Synthesis of N-acylureas and amides. J. Org. Chem. 2018, 83, 2114–2124. [CrossRef] [PubMed]
3. Jiang, N.; Ragauskas, A.J. Cu(II)-catalyzed selective aerobic oxidation of alcohols under mild conditions.
J. Org. Chem. 2006, 71, 7087–7090. [CrossRef] [PubMed]
4. Kitanosono, T.; Xu, P.Y.; Kobayashi, S. Heterogeneous versus homogeneous copper(II) catalysis in enantioselective
conjugate-addition reactions of boron in water. Chem. Asian J. 2014, 9, 179–188. [CrossRef] [PubMed]
5. Fedorov, A.; Liu, H.J.; Lo, H.K.; Coperet, C. Silica-supported cu nanoparticle catalysts for alkyne semihydrogenation:
Effect of ligands on rates and selectivity. J. Am. Chem. Soc. 2016, 138, 16502–16507. [CrossRef]
6. Meng, X.; Zhang, J.Q.; Chen, B.H.; Jing, Z.Q.; Zhao, P.Q. Copper supported on H+-modified manganese
oxide octahedral molecular sieves (Cu/H-OMS-2) as a heterogeneous biomimetic catalyst for the synthesis of
imidazo 1,2-a -N-heterocycles. Catal. Sci. Technol. 2016, 6, 890–896. [CrossRef]
3
3
3
7. Zou, Y.D.; Wang, X.X.; Ai, Y.J.; Liu, Y.H.; Ji, Y.F.; Wang, H.Q.; Hayat, T.; Alsaedi, A.; Hu, W.P.; Wang, X.K.
beta-Cyclodextrin modified graphitic carbon nitride for the removal of pollutants from aqueous solution:
Experimental and theoretical calculation study. J. Mater. Chem. A 2016, 4, 14170–14179. [CrossRef]
8. Kaboudin, B.; Abedi, Y.; Yokomatsu, T. Cu-II-beta-cyclodextrin complex as a nanocatalyst for the homo-
and cross-coupling of arylboronic acids under ligand- and base-free conditions in air: Chemoselective
cross-coupling of arylboronic acids in water. Eur. J. Org. Chem. 2011, 6656–6662. [CrossRef]
9. Gupta, D.; Mishra, A.; Kundu, S. Cu (II)-beta-CD as water-loving catalyst for one-pot synthesis of triazoles
and biofuels intermediate at room temperature without any other additive. Chemistryselect 2017, 2, 2997–3008.
[CrossRef]
4
4
4
0. Kaboudin, B.; Abedi, Y.; Yokomatsu, T. One-pot synthesis of 1,2,3-triazoles from boronic acids in water using
Cu(II)-beta-cyclodextrin complex as a nanocatalyst. Org. Biomol. Chem. 2012, 10, 4543–4548. [CrossRef]
1. Ye, R.P.; Lin, L.; Liu, C.Q.; Chen, C.C.; Yao, Y.G. One-pot synthesis of cyclodextrin-doped Cu-SiO catalysts for
2
efficient hydrogenation of dimethyl oxalate to ethylene glycol. Chemcatchem 2017, 9, 4587–4597. [CrossRef]
2. Duan, Z.B.; Ding, X.C.; Wang, Y.; Zhu, L.J.; Xia, D.H. A new strategy for fuel desulfurization by molecular
inclusion with copper(II)-beta-cyclodextrin@SiO @Fe O for removing thiophenic sulfides. Energy Fuels
2
3
4
2
018, 32, 11421–11431. [CrossRef]
4
3. Bahadorikhalili, S.; Ma'mani, L.; Mahdavi, H.; Shafiee, A. Copper supported β-cyclodextrin functionalized
PEGylated mesoporous silica nanoparticle -graphene oxide hybrid: An efficient and recyclable nano-catalyst
for straightforward synthesis of 2-arylbenzimidazoles and 1,2,3-triazoles. Microporous Mesoporous Mater.
2
018, 262, 207–216. [CrossRef]
4
4
4
4
4. Saurabh, P.; Balbir, K.; Anupama, P.; Harish, K. Applications of ultrasound in organic synthesis—A green
approach. Curr. Org. Chem. 2013, 17, 1790–1828.
5. Cravotto, G.; Cintas, P. Power ultrasound in organic synthesis: Moving cavitational chemistry from academia
to innovative and large-scale applications. Chem. Soc. Rev. 2006, 35, 180–196. [CrossRef] [PubMed]
6. Wu, Z.; Borretto, E.; Medlock, J.; Bonrath, W.; Cravotto, G. Effects of ultrasound and microwaves on selective
reduction: Catalyst preparation and reactions. ChemCatChem 2014, 6, 2762–2783. [CrossRef]
7. Luche, J.-L. Effect of ultrasound on heterogeneous systems. Ultrason. Sonochem. 1994, 1, S111–S118. [CrossRef]

Molecules 2019, 24, 2490
18 of 18
4
4
5
8. Wu, Z.; Tagliapietra, S.; Giraudo, A.; Martina, K.; Cravotto, G. Harnessing cavitational effects for green
process intensification. Ultrason. Sonochem. 2019, 52, 530–546. [CrossRef]
9. Varma, R.S. “Greener” chemical syntheses using mechanochemical mixing or microwave and ultrasound
irradiation. Green Chem. Lett. Rev. 2007, 1, 37–45. [CrossRef]
0. Shaabani, A.; Sepahvand, H.; Hooshmand, S.E.; Borjian Boroujeni, M. Design, preparation and
characterization of Cu/GA/Fe O @SiO nanoparticles as a catalyst for the synthesis of benzodiazepines and
3
4
2
imidazoles. Appl. Organomet. Chem. 2016, 30, 414–421. [CrossRef]
5
5
5
5
5
1. Hsu, Y.-W.; Wu, C.-C.; Wu, S.-M.; Su, C.-C. Synthesis and properties of carbon nanotube-grafted silica
nanoarchitecture-reinforced poly(Lactic Acid). Materials (Basel) 2017, 10, 829. [CrossRef] [PubMed]
2. Gorbachuk, V.V.; Ziatdinova, R.V.; Evtugyn, V.G.; Stoikov, I.I. Stabilization of silica nanoparticles dispersions
by surface modification with silicon derivative of thiacalix[4]arene. J. Nanopart. Res. 2015, 17, 117. [CrossRef]
3. Unterlass, M.M. Green synthesis of inorganic–organic hybrid materials: State of the art and future perspectives.
Eur. J. Inorg. Chem. 2016, 2016, 1135–1156. [CrossRef]
4. Martina, K.; Baricco, F.; Berlier, G.; Caporaso, M.; Cravotto, G. Efficient green protocols for preparation of
highly functionalized β-cyclodextrin-grafted silica. Acs Sustain. Chem. Eng. 2014, 2, 2595–2603. [CrossRef]
5. Martina, K.; Baricco, F.; Caporaso, M.; Berlier, G.; Cravotto, G. Cyclodextrin-grafted silica-supported
Pd nanoparticles: An efficient and versatile catalyst for ligand-free C
ChemCatChem 2016, 8, 1176–1184. [CrossRef]
−C coupling and hydrogenation.
5
6. Khalafi-Nezhad, A.; Panahi, F. Immobilized palladium nanoparticles on a silica-starch substrate (PNP-SSS):
As an efficient heterogeneous catalyst for Heck and copper-free Sonogashira reactions in water. Green Chem.
2
011, 13, 2408–2415. [CrossRef]
5
5
5
7. Mohanazadeh, F.; Amini, H. Silica chloride mediated alkylation of electron-rich aromatics by benzyl or
tert-butyl chloride. Bull. Korean Chem. Soc. 2010, 31, 3038–3040. [CrossRef]
8. Bagabas, A.A.; Frasconi, M.; Iehl, J.; Hauser, B.; Farha, O.K.; Hupp, J.T.; Hartlieb, K.J.; Botros, Y.Y.; Stoddart, J.F.
γ-Cyclodextrin cuprate sandwich-type complexes. Inorg. Chem. 2013, 52, 2854–2861. [CrossRef]
9. Sadeghzadeh, S.M.; Zhiani, R.; Moradi, M. KCC-1 Supported Cu(II)-
catalyst for the synthesis of 3-Aryl-2-oxazolidinones from carbon dioxide, epoxide, anilines. ChemistrySelect
018, 3, 3516–3522. [CrossRef]
β-cyclodextrin complex as a reusable
2
6
6
0. Fedorova, A.A.; Morozov, I.V.; Kotovshchikov, Y.N.; Romanovsky, B.V.; Sirotin, S.V.; Knyazeva, E.E.;
Lermontov, A.S.; Shaporev, A.S. Preparation and characterization of copper- and iron-containing mesoporous
silica using β-cyclodextrin as a structure-directing agent. Mendeleev Commun. 2011, 21, 171–172. [CrossRef]
1. Liu, J.; He, P.; Wang, L.; Liu, H.; Cao, Y.; Li, H. An efficient and stable Cu/SiO catalyst for the syntheses
2
of ethylene glycol and methanol via chemoselective hydrogenation of ethylene carbonate. Chin. J. Catal.
2
018, 39, 1283–1293. [CrossRef]
6
6
6
2. Musso, G.E.; Bottinelli, E.; Celi, L.; Magnacca, G.; Berlier, G. Influence of surface functionalization on the
hydrophilic character of mesoporous silica nanoparticles. PCCP 2015, 17, 13882–13894. [CrossRef]
3. Zhu, M.; Lerum, M.Z.; Chen, W. How to prepare reproducible, homogeneous, and hydrolytically stable
aminosilane-derived layers on silica. Langmuir 2012, 28, 416–423. [CrossRef] [PubMed]
4. Negri, C.; Signorile, M.; Porcaro, N.G.; Borfecchia, E.; Berlier, G.; Janssens, T.V.W.; Bordiga, S. Dynamic
CuII/CuI speciation in Cu-CHA catalysts by in situ Diffuse Reflectance UV–vis-NIR spectroscopy. Appl. Catal.
A: Gen. 2019, 578, 1–9. [CrossRef]
6
5. Velasco, M.I.; Krapacher, C.R.; de Rossi, R.H.; Rossi, L.I. Structure characterization of the non-crystalline complexes of
copper salts with native cyclodextrins. Dalton Trans. 2016, 45, 10696–10707. [CrossRef] [PubMed]
6. Trotta, F.; Martina, K.; Robaldo, B.; Barge, A.; Cravotto, G. Recent advances in the synthesis of cyclodextrin
derivatives under microwaves and power ultrasound. J. Incl. Phenom. Macrocycl. Chem. 2007, 57, 3–7. [CrossRef]
6
Sample Availability: Samples of the compounds Si-diAm-CD Si-DETA-CD, Si-NH-CD and relative Cu supported
catalyst are available from the authors.
©
2019 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access
article distributed under the terms and conditions of the Creative Commons Attribution
CC BY) license (http://creativecommons.org/licenses/by/4.0/).
(