Selective coordination of N3− and tuning of luminescence in garnet (Y1−x,Lax)3(Al,Si)5(O,N)12: Ce3+ phosphors

Add time:07/22/2019    Source:sciencedirect.com

Spectrum deficiency in red component of YAG: Ce3+ phosphor is hopeful to be made up by small amount of Si4+-N3− replacing Al3+-O2− for high quality lighting, while the important indicators of emission efficiency and thermal quenching properties dramatically decrease in this approach. Thus micro-structural tuning by cation substitution usually is an effective way to improve the luminescence properties. This study focuses on the structural variations and tuning luminescence induced by La3+ incorporating into Y3(Al,Si)5(O,N)12: Ce3+ phosphors. The results show that the emission efficiency and thermal quenching properties are remarkably enhanced, while the spectrum shows blue-shift to some extent. The mechanism of property variation is clarified, which is ascribed to selective coordination of N3−. This effect is important and possible to be extended to other N3− contained garnet phosphors, becoming an important rule for materials design. The obtained phosphors are promising to develop into practicable phosphors for high color rendition w-LEDs.

We also recommend Trading Suppliers and Manufacturers of (2S,3S)-FMoc-Abu(3-N3)-OH (cas 131669-42-6). Pls Click Website Link as below: cas 131669-42-6 suppliers

Prev:Enantioselective synthesis of (+)-(2S,3s)-3-ethynyltyrosine
Next:Epoxidation of alkenes bearing a carboxylic acid group by iron complexes of the tetradentate ligand N,N′-dimethyl-N,N′-bis(2-pyridylmethyl)-1,2-diaminoethane and its derivatives)