Comparison of chemical vapor deposition of TiN using tetrakis-diethylamino-titanium and tetrakis-dimethylamino-titanium

Add time:07/28/2019    Source:sciencedirect.com

The attributes and limitations of chemically vapor-deposited titanium nitride films from the reaction of tetrakis-diethylamino-titanium with ammmonia and tetrakis-dimethylamino-titanium wiht ammonia are discussed. Deposited films were characterized by growth rate, resistivity, surface morphology and step coverage over contact structures. Films deposited without ammonia flow were unstable in the atmosphere and Auger analysis showed a higher relative carbon content. It was found that the deposition pressure had a stronger effect than did the deposition temperature on the bulk resistivity and surface roughness. A higher pressure has a tendency to reduce the resistivity. Films appear smooth at low deposition temperatures and low pressures. Films become rough at high deposition temperatures and high pressures. The deposition process and resulting TiN layers are successfully integrated in a chemically vapor-deposited W plus fill applciation.

We also recommend Trading Suppliers and Manufacturers of TETRAKIS(DIMETHYLAMINO)TIN (cas 1066-77-9). Pls Click Website Link as below: cas 1066-77-9 suppliers

Prev:Atomic layer deposition of TiO2 from tetrakis(dimethylamino)titanium and H2O
Next:Improvement of the electrical and interfacial propertie of TiN/ZrO2 by a modulated atomic layer deposition process with controlled O3 dosing)