Structure of a thin barrier film deposited from tetrakis-(dimethylamino)-titanium onto a Si(100)-2×1 substrate

Add time:07/31/2019    Source:sciencedirect.com

The formation and structure of a thin film deposited using tetrakis-(dimethylamino)-titanium [Ti(N(CH3)2)4, TDMAT] as a precursor onto a Si(100)-2×1 substrate at ultrahigh vacuum (UHV) conditions was investigated by a combination of surface analytical techniques. The effects of surface temperature and pressure of the precursor molecules on the deposition rate are correlated with the monolayer chemistry of the precursor. The titanium carbonitride (TiCxNy) thin films produced by thermal deposition of TDMAT onto Si(100)-2×1 at 593 K are continuous and smooth with a root-mean-square (RMS) roughness of <2 nm, having a thickness with a lower limit of 4.7±0.4 nm, and a stoichiometry of approximately x=y=1. In addition, it was determined that the lower limit of the sputtering rate for TiCxNy was ∼0.016 nm s−1 under the conditions used here. These films hold great promise as barrier materials in next-generation microelectronic devices.

We also recommend Trading Suppliers and Manufacturers of TETRAKIS(DIMETHYLAMINO)TIN (cas 1066-77-9). Pls Click Website Link as below: cas 1066-77-9 suppliers

Prev:Sulfur-Modulated Tin Sites Enable Highly Selective Electrochemical Reduction of CO2 to Formate
Next:Numerical studies on PACVD processes used for TiN multifunctional films using metal organic precursors)