Tribological studies of monolithic CHROMIUM DIBORIDE (cas 12007-16-8) against cemented tungsten carbide (WC–Co) under dry condition

Add time:07/26/2019    Source:sciencedirect.com

Friction and wear behaviour of the hot pressed monolithic CHROMIUM DIBORIDE (cas 12007-16-8) (CrB2) of 94% theoretical density were studied at different loads (3, 5 and 10 N) and frequencies (10 and 15 Hz) under dry reciprocative sliding condition against cemented tungsten carbide (WC–Co) ball. Coefficient of friction and wear rate were calculated. While the value of coefficient of friction (COF) is decreased from 0.50 to 0.36 with increasing load from 3 N to 10 N; it is observed to be nearly independent with respect to sliding frequency. The measured wear volume is in the range of 0.67×10−3–2.24 ×10−3 mm3 for the investigated regime. The lowest specific wear rate of 4.63× 10−7 mm3/N m was observed at 10 N load and 15 Hz frequency. Abrasive and tribo-oxidative wear with delamination were the active mechanisms manifested in both flat and counter body materials.

We also recommend Trading Suppliers and Manufacturers of CHROMIUM DIBORIDE (cas 12007-16-8). Pls Click Website Link as below: cas 12007-16-8 suppliers

Prev:Pressureless sintering of CHROMIUM DIBORIDE (cas 12007-16-8) using spark plasma sintering facility
Next:Effect of substrate and film thickness on the growth, structure, mechanical and optical properties of CHROMIUM DIBORIDE (cas 12007-16-8) thin films)