Investigation on synthesis, pressureless sintering and hot pressing of CHROMIUM DIBORIDE (cas 12007-16-8)

Add time:07/28/2019    Source:sciencedirect.com

Experimental investigations were carried out on synthesis of chromium diboride through boron carbide reduction of Cr2O3. The products obtained were characterized by X-ray diffraction and the process optimized to prepare single-phase CrB2 powder. Densification of CrB2 was investigated by pressureless sintering and hot pressing. A maximum of 93% ρth was obtained by pressureless sintering at 1850 °C after a prolonged duration of 360 min. However, near theoretical density was achieved by hot pressing at 1600 °C and 35 MPa pressure for 2 h. The hardness and fracture toughness of fully dense CrB2 was measured as 22 GPa and 3.5 MPa m1/2, respectively. The mode of fracture in pressureless sintered samples is intergranular whereas that in hot pressed is transgranular.

We also recommend Trading Suppliers and Manufacturers of CHROMIUM DIBORIDE (cas 12007-16-8). Pls Click Website Link as below: cas 12007-16-8 suppliers

Prev:Effect of substrate and film thickness on the growth, structure, mechanical and optical properties of CHROMIUM DIBORIDE (cas 12007-16-8) thin films
Next:NMR studies of single crystal CHROMIUM DIBORIDE (cas 12007-16-8))