Preparation and morphology of magnesium borate (cas 12007-62-4) fibers via electrospinning
-
Add time:07/26/2019 Source:sciencedirect.com
magnesium borate (cas 12007-62-4) fibers were prepared by electrospinning technique (and following calcination) from sol–gel precursors, using polyvinyl-pyrrolidone (PVP) as processing aid. Phase-pure fibers of about 6 μm in diameter were obtained by high temperature calcination of the inorganic–organic composite mats. The samples thus prepared were characterized by means of SEM, XRD and FT-IR, respectively. The concentration of the initial solution influenced only the fiber diameter in the green samples, while the final dimension after ceramization was related to the formation of new porous fibers in a preferential direction. This phenomenon resulted from some orientation already present in the green mats, and from the softening and densification of the fibers after decomposition of the PVP. An incomplete crystallization of the samples was observed after heat treatment at 800 °C, with a residual glassy phase due to the Mg modification of the B2O3 network. Fully crystalline fibers were obtained from the mats calcined at 1000 °C.
We also recommend Trading Suppliers and Manufacturers of magnesium borate (cas 12007-62-4). Pls Click Website Link as below: cas 12007-62-4 suppliers
Prev:Physical, structural and optical studies on magnesium borate (cas 12007-62-4) glasses doped with dysprosium ion
Next:Thermoluminescence glow curve deconvolution and trapping parameters determination of dysprosium doped magnesium borate (cas 12007-62-4) glass) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Optical and erbium ion concentration correlation in lithium magnesium borate (cas 12007-62-4) glass08/01/2019
- Experimental determination of solubilities of magnesium borate (cas 12007-62-4)s: Solubility constants of boracite [Mg3B7O13Cl(cr)] and aksaite [MgB6O7(OH)6·2H2O(cr)]07/31/2019
- Synthesis of magnesium borate (cas 12007-62-4)s using sodium borate and magnesium sulfate07/30/2019
- Realization of dysprosium doped lithium magnesium borate (cas 12007-62-4) glass based TLD subjected to 1–100 Gy photon beam irradiations07/29/2019
- Microstructure and properties of functional magnesium titanate ceramic joint brazed by bismuth-borate glass07/28/2019
- Thermoluminescence glow curve deconvolution and trapping parameters determination of dysprosium doped magnesium borate (cas 12007-62-4) glass07/27/2019
- Physical, structural and optical studies on magnesium borate (cas 12007-62-4) glasses doped with dysprosium ion07/25/2019
- Effect of heat treatment conditions on magnesium borate (cas 12007-62-4) fibers prepared via electrospinning07/24/2019
-
Health and Chemical more >